不同热处理状态下GCr15钢的晶粒度显示方法
Display Method of Grain Size of GCr15 Steel in Different Heat Treatment States
摘 要
在实际生产中，采用传统的浸蚀方法无法直接检验出交货状态材料的实际晶粒度。为此通过试验得到了不同热处理状态GCr15钢晶粒度显示所需的最佳浸蚀条件，证明了可以通过优化的浸蚀方法显示出原奥氏体晶界，从而确定退火、热轧状态GCr15钢的实际晶粒度。
奥氏体
晶粒度
浸蚀
GCr15 steel
austenite
grain size
erosion
Abstract
In actual production, the actual grain size of materials in delivery state can not be directly inspected by traditional erosion methods. For the reason, the optimum erosion conditions for GCr15 steel in different heat treatment states were obtained through experiments. It is proved that the original austenite grain boundary can be displayed by optimum erosion method, thus the actual grain size of GCr15 steel in annealing and hot rolling states can be determined.
中图分类号 TG115.21 DOI 10.11973/lhjy-wl201908003
所属栏目 专题报道(金属晶粒度测定方法)
基金项目
收稿日期 2019/1/10
修改稿日期
网络出版日期
作者单位点击查看
备注俞亚杰(1982-),女,工程师,主要从事金属材料物理测试工作,yyj515102@163.com
引用该论文: YU Yajie,SHI Jingsong. Display Method of Grain Size of GCr15 Steel in Different Heat Treatment States[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2019, 55(8): 530～532
俞亚杰,史景松. 不同热处理状态下GCr15钢的晶粒度显示方法[J]. 理化检验－物理分册, 2019, 55(8): 530～532
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】钟云龙,刘国权,刘胜新,等. 新型油井管钢33Mn2V的奥氏体晶粒长大规律[J]. 金属学报,2003,39(7):699-703.
【2】刘建涛,张义文,陶宇,等. FGH96合金锻造盘坯热处理过程中的晶粒长大行为[J]. 金属热处理,2006,31(6):40-44.
【3】刘建涛,刘国权,胡本芙,等. FGH96合金晶粒长大规律的研究[J]. 材料热处理学报,2004,25(6):25-29.
【4】赵辉,鹿守理,窦晓峰,等. 低碳钢轧后冷却过程中的晶粒长大模型[J]. 钢铁,1999,34(2):51-53.
【5】岳重祥,张立文,廖舒纶,等. GCrl5钢奥氏体晶粒长大规律研究[J]. 材料热处理学报,2008,29(1):94-97.
【2】刘建涛,张义文,陶宇,等. FGH96合金锻造盘坯热处理过程中的晶粒长大行为[J]. 金属热处理,2006,31(6):40-44.
【3】刘建涛,刘国权,胡本芙,等. FGH96合金晶粒长大规律的研究[J]. 材料热处理学报,2004,25(6):25-29.
【4】赵辉,鹿守理,窦晓峰,等. 低碳钢轧后冷却过程中的晶粒长大模型[J]. 钢铁,1999,34(2):51-53.
【5】岳重祥,张立文,廖舒纶,等. GCrl5钢奥氏体晶粒长大规律研究[J]. 材料热处理学报,2008,29(1):94-97.
相关信息