Microstructure and Properties of SIMP Steel Joint by Three Step Heating Transient Liquid Phase Diffusion Welding with Different Process Parameters
摘 要
采用BNi2和Fe78Si9B13非晶合金箔作为中间层,对SIMP钢管进行三温工艺瞬时液相(TLP)扩散焊接,研究了不同等温凝固工艺参数(温度1 230,1 240℃;时间180,240 s;压力8,9 MPa)下接头的显微组织和力学性能。结果表明:等温凝固温度的升高或时间的延长均可以促进降熔元素的扩散,减少焊缝组织中脆硬相的生成,从而提高接头的抗拉强度、降低焊缝的显微硬度;较佳的等温凝固工艺参数为温度1 240℃、时间240 s、压力9 MPa,采用该参数焊接后接头组织为均匀马氏体,焊缝组织与两侧母材组织的差异很小,抗拉强度最高,为794 MPa,拉伸断裂方式为韧性断裂。
Abstract
With BNi2 and Fe78Si9B13 amorphous alloy foils as intermediate layer, SIMP steel tubes were joined by three step heating transient liquid phase (TLP) diffusion welding. Microstructure and mechanical properties of the joint welded with different isothermal solidification process parameters (temperature of 1 230, 1 240℃; time of 180, 240 s; pressure of 8, 9 MPa) were studied. The results show that increasing isothermal solidification temperature or time was beneficial to the diffusion of melting elements and reducing formation of brittle hard phases in the weld microstructure, thereby improving the tensile strength of the joint and reducing the microhardness of the weld. The relatively optimal isothermal solidification parameters were listed as follows:temperature of 1 240℃, time of 240 s, and pressure of 9 MPa. After welding with these parameters, the microstructure of the joint was composed of uniform martensite, and the difference between the weld microstructure and the base metal microstructure was small; the tensile strength of the joint reached the largest value of 794 MPa, and the tensile fracture mode was ductile fracture.
中图分类号 TG456.9 DOI 10.11973/jxgccl201908003
所属栏目 试验研究
基金项目 河南理工大学金属学科项目(660642/036));河南理工大学与中国科学院金属所合作项目(H16-037)
收稿日期 2018/7/15
修改稿日期 2019/6/20
网络出版日期
作者单位点击查看
备注郝丽丽(1994-),女,河北邢台人,硕士研究生
引用该论文: HAO Lili,CHEN Sijie,DING Guangzhu,LI Bao,LI Shihui,ZHAO Pifeng. Microstructure and Properties of SIMP Steel Joint by Three Step Heating Transient Liquid Phase Diffusion Welding with Different Process Parameters[J]. Materials for mechancial engineering, 2019, 43(8): 12~17
郝丽丽,陈思杰,丁光柱,李报,李世会,赵丕峰. 不同工艺参数下SIMP钢三温工艺瞬时液相扩散焊接头的组织与性能[J]. 机械工程材料, 2019, 43(8): 12~17
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】吴增强, 白银, 马龙腾, 等. 650℃马氏体耐热钢研究及其进展[J]. 钢铁, 2015, 50(5):1-6.
【2】杨柯, 严伟, 王志光, 等. 核用新型耐高温、抗辐照、耐液态金属腐蚀结构材料:SIMP钢的研究进展[J]. 金属学报, 2016, 52(10):1207-1221.
【3】王磊, 俞建荣, 董晓慧, 等. 瞬时液相扩散焊技术的研究进展[J]. 机械制造与自动化, 2015, 44(4):7-9.
【4】王非森, 陈思杰, 高增, 等. 瞬时液相扩散连接在镍及镍基合金焊接中的应用[J]. 电焊机, 2009, 39(9):38-42.
【5】ASSADI H, SHIRZADI A A, WALLACH E R. Transient liquid phase diffusion bonding under a temperature gradient:Modelling of the interface morphology[J]. Acta Materialia, 2001, 49(1):31-39.
【6】SHIRZADI A A, WALLACH E R. Analytical modelling of transient liquid phase (TLP) diffusion bonding when a temperature gradient is imposed[J]. Acta Materialia, 1999, 47(13):3551-3560.
【7】王磊, 俞建荣, 董晓慧, 等. 20钢与0Cr18Ni9异种金属材料的瞬时液相扩散焊研究[J]. 热加工工艺, 2015, 44(3):45-47.
【8】KUNDU S, GHOSH M, LAIK A, et al. Diffusion bonding of commercially pure titanium to 304 stainless steel using copper interlayer[J]. Materials Science and Engineering:A, 2005, 407(1/2):154-160.
【9】陈思杰, 高增. TP304H/12Cr2MoWVTiB异种钢管的双温瞬时液相扩散焊工艺[J]. 机械工程材料, 2009, 33(8):28-31.
【10】陈思杰, 王学刚, 李辛庚, 等. 地质钻杆的瞬时液相扩散连接双温工艺[J]. 机械工程材料, 2008, 32(5):52-54.
【11】陈思杰, 徐琴, 王振江, 等. 102/T91异种钢瞬时液相扩散连接双温工艺接头的组织与性能[J]. 机械工程材料, 2008, 32(6):70-73.
【2】杨柯, 严伟, 王志光, 等. 核用新型耐高温、抗辐照、耐液态金属腐蚀结构材料:SIMP钢的研究进展[J]. 金属学报, 2016, 52(10):1207-1221.
【3】王磊, 俞建荣, 董晓慧, 等. 瞬时液相扩散焊技术的研究进展[J]. 机械制造与自动化, 2015, 44(4):7-9.
【4】王非森, 陈思杰, 高增, 等. 瞬时液相扩散连接在镍及镍基合金焊接中的应用[J]. 电焊机, 2009, 39(9):38-42.
【5】ASSADI H, SHIRZADI A A, WALLACH E R. Transient liquid phase diffusion bonding under a temperature gradient:Modelling of the interface morphology[J]. Acta Materialia, 2001, 49(1):31-39.
【6】SHIRZADI A A, WALLACH E R. Analytical modelling of transient liquid phase (TLP) diffusion bonding when a temperature gradient is imposed[J]. Acta Materialia, 1999, 47(13):3551-3560.
【7】王磊, 俞建荣, 董晓慧, 等. 20钢与0Cr18Ni9异种金属材料的瞬时液相扩散焊研究[J]. 热加工工艺, 2015, 44(3):45-47.
【8】KUNDU S, GHOSH M, LAIK A, et al. Diffusion bonding of commercially pure titanium to 304 stainless steel using copper interlayer[J]. Materials Science and Engineering:A, 2005, 407(1/2):154-160.
【9】陈思杰, 高增. TP304H/12Cr2MoWVTiB异种钢管的双温瞬时液相扩散焊工艺[J]. 机械工程材料, 2009, 33(8):28-31.
【10】陈思杰, 王学刚, 李辛庚, 等. 地质钻杆的瞬时液相扩散连接双温工艺[J]. 机械工程材料, 2008, 32(5):52-54.
【11】陈思杰, 徐琴, 王振江, 等. 102/T91异种钢瞬时液相扩散连接双温工艺接头的组织与性能[J]. 机械工程材料, 2008, 32(6):70-73.
相关信息