粘接试验方法测定激光熔覆层与基体结合强度
Adhesive Test Method for Measuring Interfacial Bonding Strength between Laser Cladding and Matrix
摘 要
关于激光熔覆层与基体结合强度的检测还没有相关标准，为给激光熔覆层与基体结合强度检测标准的建立提供参考，采用粘接试验的方法，将激光熔覆层视为复材，对304不锈钢棒材和20钢棒材激光熔覆钴基合金STL粉末后的熔覆层与基体结合强度进行了检测。结果表明：该方法的试样制备和试验操作简单易行，对试验设备的要求不高，测定的激光熔覆层与基体结合强度数值的相对标准偏差在5%以内。
激光熔覆层
结合强度
粘接试验
steel bar
laser cladding
bonding strength
adhesive test
Abstract
There is no relevant standard for testing the bonding strength between laser cladding layer and matrix. In order to provide a reference for establishing the testing standard for the bonding strength between laser cladding layer and matrix, the bonding strength of laser cladding layer on 304 stainless steel bar and 20 steel bar after laser cladding of cobalt-based alloy STL powder was tested by using adhesive test method. The results show that the sample preparation and test operation were simple and feasible, and the requirement for test equipment was not high. The relative standard deviation of the measured bonding strength between laser cladding layer and matrix was less than 5%.
中图分类号 TG495 DOI 10.11973/lhjy-wl201911001
所属栏目 试验与研究
基金项目
收稿日期 2018/12/3
修改稿日期
网络出版日期
作者单位点击查看
备注王文明(1975-),男,高级工程师,博士,主要从事金属材料表面硬化方面的工作,dearwmwang@163.com
引用该论文: WANG Wenming,SHEN Jianbiao,CHEN Yan,ZHANG Cheng,CHEN Chuanhui. Adhesive Test Method for Measuring Interfacial Bonding Strength between Laser Cladding and Matrix[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2019, 55(11): 745～747
王文明,沈剑标,陈彦,张程,陈川辉. 粘接试验方法测定激光熔覆层与基体结合强度[J]. 理化检验－物理分册, 2019, 55(11): 745～747
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】许明三,李剑峰,李驊登,等. 激光熔覆粉料和工艺参数对45钢基体与熔覆层结合强度的影响研究[J]. 机械工程学报,2017,53(9):209-216.
【2】PEI Y T, OCELÍ K V, DE HOSSON J T M. Interfacial adhesion of laser clad functionally graded materials[J]. Materials Science and Engineering:A,2003,342(1/2):192-200.
【3】WANG Q Y, XI Y C, LIU X Y, et al. Microstructure and mechanical properties of interface between laser cladded hastelloy coating and steel substrate[J]. Transactions of Nonferrous Metals Society of China,2017,27(3):733-740.
【4】宋亚南,徐滨士,王海斗,等. 喷涂层结合强度测量方法的研究现状[J]. 工程与试验,2011,51(4):1-8.
【5】苏修梁,张欣宇. 表面涂层与基体间的界面结合强度及其测定[J]. 电镀与环保,2004,24(2):6-11.
【6】孔德军,张永康,鲁金忠. 基于XRD的薄膜界面结合强度试验研究[J]. 中国表面工程,2007,20(1):38-41.
【7】孙畅,李龙,周德敬. 层状复合材料界面结合强度非传统评价方法[J]. 材料导报,2017,31(11):59-67.
【8】于斌斌,袁军堂,孙淮阳,等. 新型界面结合强度检测技术理论及实验研究[J]. 材料科学与工艺,2011,19(5):72-78.
【9】李龙,张心金,刘会云,等. 金属层状复合材料结合性能的评价方法[J]. 武汉科技大学学报(自然科学版),2013,36(3):195-201.
【10】程序. 高结合性能涂层结合强度的实验研究及有限元分析[D]. 南京:南京航空航大大学,2011.
【11】ZHANG H, LI D Y. Determination of interfacial bonding strength using a cantilever bending method with in situ monitoring acoustic emission[J]. Surface and Coatings Technology,2002,155(2/3):190-194.
【12】聂继红,唐家祥,王爱华. 应用扫描电镜拉伸台测定激光熔覆层结合强度[J]. 分析测试技术与仪器,1997,3(3):156-161.
【13】KATIPELLI L R, AGARWAL A, DAHOTRE N B. Interfacial strength of laser surface engineered TiC coating on 6061 Al using four-point bend test[J]. Materials Science and Engineering:A,2000,289(1/2):34-40.
【14】刘衍聪,刘本良,战祥华,等. 激光熔覆层结合强度测试方法研究及装置设计[J]. 应用激光,2016,36(6):641-648.
【15】石世宏,贾帅,周亮,等. 激光熔覆层与基体结合强度的评定方法:ZL201510547682.2[P]. 2015-08-31.
【16】李荣锋. 我国金属材料物理性能现场检测技术现状与展望[J]. 理化检验(物理分册),2015,51(12):835-838.
【2】PEI Y T, OCELÍ K V, DE HOSSON J T M. Interfacial adhesion of laser clad functionally graded materials[J]. Materials Science and Engineering:A,2003,342(1/2):192-200.
【3】WANG Q Y, XI Y C, LIU X Y, et al. Microstructure and mechanical properties of interface between laser cladded hastelloy coating and steel substrate[J]. Transactions of Nonferrous Metals Society of China,2017,27(3):733-740.
【4】宋亚南,徐滨士,王海斗,等. 喷涂层结合强度测量方法的研究现状[J]. 工程与试验,2011,51(4):1-8.
【5】苏修梁,张欣宇. 表面涂层与基体间的界面结合强度及其测定[J]. 电镀与环保,2004,24(2):6-11.
【6】孔德军,张永康,鲁金忠. 基于XRD的薄膜界面结合强度试验研究[J]. 中国表面工程,2007,20(1):38-41.
【7】孙畅,李龙,周德敬. 层状复合材料界面结合强度非传统评价方法[J]. 材料导报,2017,31(11):59-67.
【8】于斌斌,袁军堂,孙淮阳,等. 新型界面结合强度检测技术理论及实验研究[J]. 材料科学与工艺,2011,19(5):72-78.
【9】李龙,张心金,刘会云,等. 金属层状复合材料结合性能的评价方法[J]. 武汉科技大学学报(自然科学版),2013,36(3):195-201.
【10】程序. 高结合性能涂层结合强度的实验研究及有限元分析[D]. 南京:南京航空航大大学,2011.
【11】ZHANG H, LI D Y. Determination of interfacial bonding strength using a cantilever bending method with in situ monitoring acoustic emission[J]. Surface and Coatings Technology,2002,155(2/3):190-194.
【12】聂继红,唐家祥,王爱华. 应用扫描电镜拉伸台测定激光熔覆层结合强度[J]. 分析测试技术与仪器,1997,3(3):156-161.
【13】KATIPELLI L R, AGARWAL A, DAHOTRE N B. Interfacial strength of laser surface engineered TiC coating on 6061 Al using four-point bend test[J]. Materials Science and Engineering:A,2000,289(1/2):34-40.
【14】刘衍聪,刘本良,战祥华,等. 激光熔覆层结合强度测试方法研究及装置设计[J]. 应用激光,2016,36(6):641-648.
【15】石世宏,贾帅,周亮,等. 激光熔覆层与基体结合强度的评定方法:ZL201510547682.2[P]. 2015-08-31.
【16】李荣锋. 我国金属材料物理性能现场检测技术现状与展望[J]. 理化检验(物理分册),2015,51(12):835-838.
相关信息