20Cr2Ni4钢制打击罩硬度异常分析
Hardness Abnormality Analysis of Striking Covers Made of 20Cr2Ni4 Steel
摘 要
某批20Cr2Ni4钢制打击罩硬度出现异常，导致机加工刀具寿命严重降低。通过宏观分析、化学成分分析、硬度分析和金相检验等方法对打击罩异常件和正常件进行了对比分析。结果表明：该钢热加工后产生了硬度较高的粒状贝氏体，后续正火+高温回火热处理可以使粒状贝氏体分解从而降低产品硬度；异常件为未经热处理的产品，其奥氏体晶粒粗大，硬度偏高，从而导致刀具损坏严重。建议产品分类摆放，加强现场管理和监控力度。
打击罩
奥氏体
热处理
粒状贝氏体
20Cr2Ni4 steel
striking cover
austenite
heat treatment
granular bainite
Abstract
The hardness abnormality of striking covers made of 20Cr2Ni4 steel led to serious decrease of machining tool life. The abnormal and normal workpieces were compared and analyzed by macroscopic analysis, chemical composition analysis, hardness analysis and metallographic examination. The results show that granular bainite with high hardness was produced in 20Cr2Ni4 steel after hot working. The subsequent normalizing and high tempering heat treatment can decompose granular bainite and reduce the hardness of products. The abnormal workpieces were products without heat treatment, whose coarse austenite grain and high hardness resulted in serious tool damage. It is suggested classifying the products and strengthening the on-site management and monitoring.
中图分类号 TG115.2 DOI 10.11973/lhjy-wl201912007
所属栏目 质量控制与失效分析
基金项目
收稿日期 2018/10/12
修改稿日期
网络出版日期
作者单位点击查看
备注赵杰(1995-),男,工程师,主要从事金属材料热处理和理化检验工作,zhaojie01@longchengforging.com.cn
引用该论文: ZHAO Jie,LI Yan,ZHENG Juntao. Hardness Abnormality Analysis of Striking Covers Made of 20Cr2Ni4 Steel[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2019, 55(12): 850～852
赵杰,李艳,郑俊涛. 20Cr2Ni4钢制打击罩硬度异常分析[J]. 理化检验－物理分册, 2019, 55(12): 850～852
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】蔡玉冬. 齿轮壳安装定位柱断裂失效分析[J]. 理化检验(物理分册),2017,53(1):58-61.
【2】王燕慧,陈卓玥,王丽萍,等. 2Cr13不锈钢止血钳断裂原因分析[J]. 理化检验(物理分册),2016,52(1):74-76.
【3】徐小红. 汽车右后拖曳臂轴断裂原因分析[J]. 理化检验(物理分册),2018,54(1):55-59.
【4】乔斌. 粒状贝氏体的形成[J].淮海工学院学报(自然科学版),1998,7(2):13-16.
【5】冉旭,陈莉,邬占田,等. 20CrMnTi钢粒状贝氏体的消除[J]. 吉林工学院学报,1999,20(2):15-20.
【6】姚培友,王晓华. 20Cr2Ni4钢正火新工艺的研究[J]. 热处理技术与装备,2009,30(5):54-55.
【7】桂晓露,刘蓉,高古辉,等. Cr元素对贝氏体钢连续转变规律的影响[J]. 材料热处理学报,2016,37(10):154-158.
【8】陈雪慧,杨才福,张倩,等. 粒状贝氏体对10CrNiMoV球扁钢力学性能的影响[J]. 上海金属,2010,32(3):34-37.
【2】王燕慧,陈卓玥,王丽萍,等. 2Cr13不锈钢止血钳断裂原因分析[J]. 理化检验(物理分册),2016,52(1):74-76.
【3】徐小红. 汽车右后拖曳臂轴断裂原因分析[J]. 理化检验(物理分册),2018,54(1):55-59.
【4】乔斌. 粒状贝氏体的形成[J].淮海工学院学报(自然科学版),1998,7(2):13-16.
【5】冉旭,陈莉,邬占田,等. 20CrMnTi钢粒状贝氏体的消除[J]. 吉林工学院学报,1999,20(2):15-20.
【6】姚培友,王晓华. 20Cr2Ni4钢正火新工艺的研究[J]. 热处理技术与装备,2009,30(5):54-55.
【7】桂晓露,刘蓉,高古辉,等. Cr元素对贝氏体钢连续转变规律的影响[J]. 材料热处理学报,2016,37(10):154-158.
【8】陈雪慧,杨才福,张倩,等. 粒状贝氏体对10CrNiMoV球扁钢力学性能的影响[J]. 上海金属,2010,32(3):34-37.
相关信息