工业用镍材在熔融烧碱中的均匀腐蚀行为
General Corrosion Behavior of Industrial Nickel in Molten Caustic Soda
摘 要
采用失重法研究了浸泡时间和微量合金元素Fe、Mg、Ti对氯碱工业用镍材在熔融烧碱（NaOH）中均匀腐蚀（全面腐蚀）速率的影响。结果表明：随着浸泡时间的延长，含不同量合金元素的镍材在熔融烧碱中的腐蚀速率均呈现先增大后降低，然后逐渐趋于稳定的趋势；在熔融烧碱中，Fe对镍材的耐蚀性有不利影响，而Mg、Ti对镍材的耐蚀性无明显影响。
镍
熔融烧碱
均匀腐蚀
chloro-alkali industry
nickel
molten caustic soda
general corrosion
Abstract
Effects of immersion time and trace alloying elements Fe, Mg and Ti on the general corrosion behavior of industrial nickel in molten caustic soda were evaluated by weight-loss method. The results show that with the increase of immersion time, corrosion rates of all nickel materials with different concentrations of alloying elements in molten caustic soda increased first and then decreased, and then gradually became stable. In molten caustic soda, Fe had an adverse effect on the corrosion resistance of nickel, while Mg and Ti had no significant effect on the corrosion resistance of nickel.
中图分类号 TQ138.1+3 TG172.8 DOI 10.11973/fsyfh-202002004
所属栏目 试验研究
基金项目 重庆市科技创新领军人才支持计划（CSTCKJCXLJRC01）；重庆市重点产业共性关键技术创新专项（cstc2015zdcy-ztzx50002）
收稿日期 2018/2/28
修改稿日期
网络出版日期
作者单位点击查看
引用该论文: LIU Yinglong,HE Wenhai,LIU Haiding,CHANG Liang,XU Yongfu,LIU Min,WANG Dongzhe. General Corrosion Behavior of Industrial Nickel in Molten Caustic Soda[J]. Corrosion & Protection, 2020, 41(2): 19
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】苏亚莉, 张建英. 镍在氯碱工业中的应用[J]. 氯碱工业, 1995, 31(9):8-12.
【2】尹晓燕. 工业纯镍在烧碱溶液中的腐蚀行为研究[D]. 大连: 大连理工大学, 2006.
【3】ABD EL-HALEEM S M, ABD EL-WANEES S. Chloride induced pitting corrosion of nickel in alkaline solutions and its inhibition by organic amines[J]. Materials Chemistry and Physics, 2011, 128(3): 418-426.
【4】白金海, 刘长厚, 张述伟. 低浓度固碱生产中镍的腐蚀研究[J]. 腐蚀与防护, 1995, 16(5): 221-223.
【5】马斌. 进口与国产降膜管在固碱工艺中使用寿命比较[J]. 氯碱工业, 2014, 50(12): 26, 29.
【6】张磊. 工业纯镍N6焊接接头组织与腐蚀性能的研究[D]. 天津:河北工业大学,2015.
【7】KOMATH M. Hot corrosion of nickel in anhydrous sodium hydroxide[J]. Materials Chemistry and Physics, 1996, 45(2): 171-175.
【8】陈步荣. 工业纯镍在热浓烧碱溶液中的腐蚀[J]. 氯碱工业, 2003, 39(8): 41-42, 45.
【9】郭宁, 秦紫瑞. 金属镍腐蚀与磨蚀行为的研究[J]. 石油机械, 1996, 24(8): 23-27.
【2】尹晓燕. 工业纯镍在烧碱溶液中的腐蚀行为研究[D]. 大连: 大连理工大学, 2006.
【3】ABD EL-HALEEM S M, ABD EL-WANEES S. Chloride induced pitting corrosion of nickel in alkaline solutions and its inhibition by organic amines[J]. Materials Chemistry and Physics, 2011, 128(3): 418-426.
【4】白金海, 刘长厚, 张述伟. 低浓度固碱生产中镍的腐蚀研究[J]. 腐蚀与防护, 1995, 16(5): 221-223.
【5】马斌. 进口与国产降膜管在固碱工艺中使用寿命比较[J]. 氯碱工业, 2014, 50(12): 26, 29.
【6】张磊. 工业纯镍N6焊接接头组织与腐蚀性能的研究[D]. 天津:河北工业大学,2015.
【7】KOMATH M. Hot corrosion of nickel in anhydrous sodium hydroxide[J]. Materials Chemistry and Physics, 1996, 45(2): 171-175.
【8】陈步荣. 工业纯镍在热浓烧碱溶液中的腐蚀[J]. 氯碱工业, 2003, 39(8): 41-42, 45.
【9】郭宁, 秦紫瑞. 金属镍腐蚀与磨蚀行为的研究[J]. 石油机械, 1996, 24(8): 23-27.
相关信息