Effect of Mixed Resin Powders on 6063 Aluminum Alloy Corrosion in Valve Cooling System at Converter Station
摘 要
通过浸泡腐蚀试验及电化学试验研究了混合树脂粉末对阀冷系统6063铝合金腐蚀行为的影响。结果表明:随着浸泡时间的延长,阴阳树脂分解产物与溶出物含量增多,溶液酸化,表现为溶液电导率上升,pH下降;混合树脂粉末、电流均会加速6063铝合金的腐蚀;电化学测试表明混合树脂粉末使6063铝合金的自腐蚀电位负移,自腐蚀电流密度增大;随着浸泡时间的延长,电化学阻抗谱中容抗弧半径减小,极化电阻减小,即混合树脂粉末溶液中铝合金的耐腐蚀性能降低,腐蚀加快。因此,在实际应用中应该考虑阀冷系统中混合树脂粉末对6063铝合金的腐蚀问题,并采取相应的防护措施。
Abstract
The effects of mixed resin powders on the corrosion behavior of 6063 aluminum alloy were investigated by immersion corrosion test and electrochemical test. The results showed that with the prolongation of immersion time, the concentrations of decomposition products and soluble substances of anion resin and cation resin increased, and the solution acidified, which resulted in the increase of conductivity and the decrease of pH value for the solution. The current and the mixed resin powders could accelerate the corrosion of 6063 aluminum alloy. The electrochemical tests showed that in the mixed resin powder solution, the free corrosion potential of 6063 aluminum alloy decreased and the free corrosion current density increased. With the prolongation of immersion time, both the radius of tolerance arc in the EIS spectrum and the polarization resistance decreased, which means that the corrosion resistance of aluminum alloy was reduced and the corrosion was accelerated. Therefore, in the practical application of the valve cooling system, the corrosion of the mixed resin powders to 6063 aluminum alloy should be considered and the corresponding protective measures should be taken.
中图分类号 TG172 DOI 10.11973/fsyfh-202002008
所属栏目 试验研究
基金项目 国网浙江省电力有限公司科研项目(5211DS160023)
收稿日期 2018/6/21
修改稿日期
网络出版日期
作者单位点击查看
联系人作者朱志平(zzp8389@163.com)
引用该论文: SONG Xiaoning,CHENG Yijie,YANG Lei,ZHU Zhiping. Effect of Mixed Resin Powders on 6063 Aluminum Alloy Corrosion in Valve Cooling System at Converter Station[J]. Corrosion & Protection, 2020, 41(2): 39
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】舒印彪. 我国特高压输电的发展与实施[J]. 中国电力, 2005, 38(11):1-8.
【2】赵杰. 高压直流输电的前沿技术[J]. 中国电力, 2005, 38(10):1-6.
【3】李道豫, 邱志远, 李学武, 等. 铝在高压直流输电系统中高电压高温下的腐蚀行为研究[J]. 化工进展, 2016, 35(b11):92-98.
【4】刘凯. ±500 kV换流站阀冷系统水质监督与结垢分析[J]. 湖南电力, 2015(4):41-43.
【5】高压直流输电换流阀冷却水运行管理导则:DL/T 1716-2017[S]. 北京:中国电力出版社,2017.
【6】臧兴平, 胡永恒, 吴红艳. 大功率电力电子器件纯水冷却系统树脂泄漏问题的分析与处理[J]. 电工技术, 2015(5):64-65.
【7】龚云峰, 吴春华, 丁桓如. 凝结水处理用树脂溶出物问题研究[J]. 离子交换与吸附, 2000, 16(5):461-466.
【8】荆玲玲, 朱志平, 熊书华,等. 凝结水精处理阳树脂硫酸根溶出特性研究[J]. 离子交换与吸附, 2011, 27(5):435-443.
【9】尉院春, 周柏青. 大孔阴树脂水中受热降解动力学研究[J]. 热力发电, 2014, 43(1):61-65.
【10】王少龙, 吴春华, 丁桓如,等. 001×7阳树脂溶(浸)出有机磺化物氧化分解特性研究[J]. 中国电力, 2016, 49(1):49-52.
【11】周瑜. 电厂阳树脂氧化分解产生硫酸根的特性研究[D]. 长沙:长沙理工大学, 2012.
【12】刘伟伟. 空冷机组凝结水精处理系统阴树脂及滤元耐温性能[J]. 中国电力, 2012, 45(3):58-61.
【13】范云鸽, 肖国林. 耐高温强碱阴离子交换树脂研究进展[J]. 离子交换与吸附, 2005, 21(4):376-384.
【14】孟宇, 张俐, 史然峰,等. 15CrMo钢在含有SO42-的模拟汽轮机初凝水中的腐蚀特性[J]. 腐蚀与防护, 2014, 35(12):1208-1211.
【15】SU X, YIN Z, CHENG Y F. Corrosion of 16Mn line pipe steel in a simulated soil solution and the implication on its long-term corrosion behavior[J]. Journal of Materials Engineering and Performance, 2013, 22(2):498-504.
【16】邓丹萍, 杜楠, 王帅星,等. SO42-对X80管线钢在酸性红壤模拟溶液中腐蚀行为的影响[J]. 腐蚀与防护, 2017, 38(5):327-330.
【17】ELIYAN F F, MAHDI E, ALFANTAZI A. Electrochemical evaluation of the corrosion behavior of API-X100 piepline steel in aerated bicarbonated solution[J]. Corrosion Science, 2012, 58:181-191.
【18】生海, 董超芳, 肖葵,等. pH值对2024-T351铝合金在NaCl溶液中电化学行为的影响[J]. 腐蚀与防护, 2013, 34(2):107-110.
【19】CHEN X, TIAN W, LI S, et al. Effect of temperature on corrosion behavior of 3003 aluminum alloy in ethylene glycol-water solution[J]. 中国航空学报(英文版), 2016, 29(4):1142-1150.
【2】赵杰. 高压直流输电的前沿技术[J]. 中国电力, 2005, 38(10):1-6.
【3】李道豫, 邱志远, 李学武, 等. 铝在高压直流输电系统中高电压高温下的腐蚀行为研究[J]. 化工进展, 2016, 35(b11):92-98.
【4】刘凯. ±500 kV换流站阀冷系统水质监督与结垢分析[J]. 湖南电力, 2015(4):41-43.
【5】高压直流输电换流阀冷却水运行管理导则:DL/T 1716-2017[S]. 北京:中国电力出版社,2017.
【6】臧兴平, 胡永恒, 吴红艳. 大功率电力电子器件纯水冷却系统树脂泄漏问题的分析与处理[J]. 电工技术, 2015(5):64-65.
【7】龚云峰, 吴春华, 丁桓如. 凝结水处理用树脂溶出物问题研究[J]. 离子交换与吸附, 2000, 16(5):461-466.
【8】荆玲玲, 朱志平, 熊书华,等. 凝结水精处理阳树脂硫酸根溶出特性研究[J]. 离子交换与吸附, 2011, 27(5):435-443.
【9】尉院春, 周柏青. 大孔阴树脂水中受热降解动力学研究[J]. 热力发电, 2014, 43(1):61-65.
【10】王少龙, 吴春华, 丁桓如,等. 001×7阳树脂溶(浸)出有机磺化物氧化分解特性研究[J]. 中国电力, 2016, 49(1):49-52.
【11】周瑜. 电厂阳树脂氧化分解产生硫酸根的特性研究[D]. 长沙:长沙理工大学, 2012.
【12】刘伟伟. 空冷机组凝结水精处理系统阴树脂及滤元耐温性能[J]. 中国电力, 2012, 45(3):58-61.
【13】范云鸽, 肖国林. 耐高温强碱阴离子交换树脂研究进展[J]. 离子交换与吸附, 2005, 21(4):376-384.
【14】孟宇, 张俐, 史然峰,等. 15CrMo钢在含有SO42-的模拟汽轮机初凝水中的腐蚀特性[J]. 腐蚀与防护, 2014, 35(12):1208-1211.
【15】SU X, YIN Z, CHENG Y F. Corrosion of 16Mn line pipe steel in a simulated soil solution and the implication on its long-term corrosion behavior[J]. Journal of Materials Engineering and Performance, 2013, 22(2):498-504.
【16】邓丹萍, 杜楠, 王帅星,等. SO42-对X80管线钢在酸性红壤模拟溶液中腐蚀行为的影响[J]. 腐蚀与防护, 2017, 38(5):327-330.
【17】ELIYAN F F, MAHDI E, ALFANTAZI A. Electrochemical evaluation of the corrosion behavior of API-X100 piepline steel in aerated bicarbonated solution[J]. Corrosion Science, 2012, 58:181-191.
【18】生海, 董超芳, 肖葵,等. pH值对2024-T351铝合金在NaCl溶液中电化学行为的影响[J]. 腐蚀与防护, 2013, 34(2):107-110.
【19】CHEN X, TIAN W, LI S, et al. Effect of temperature on corrosion behavior of 3003 aluminum alloy in ethylene glycol-water solution[J]. 中国航空学报(英文版), 2016, 29(4):1142-1150.
相关信息