乙二醇对阀冷系统6063铝合金的腐蚀影响
Effect of Ethylene Glycol on Corrosion Behavior of 6063 Aluminum Alloy in Valve Cooling System
摘 要
通过浸泡腐蚀试验及电化学测试研究了乙二醇对换流站阀冷系统6063铝合金的腐蚀影响。结果表明：不论通电与否，乙二醇均加速6063铝合金的腐蚀，乙二醇含量越大，腐蚀越严重，且通入10 mA直流电流后，腐蚀速率更大；同时，乙二醇被氧化生成乙醇酸、乙二酸等腐蚀性物质，加快6063铝合金腐蚀。因此，阀冷系统在实际应用中，应重视乙二醇对6063铝合金的腐蚀问题，并采取相应对策。
6063铝合金
乙二醇
电流
腐蚀
valve cooling system
6063 aluminum alloy
ethylene glycol
current
corrosion
Abstract
Effect of ethylene glycol on the corrosion behavior of 6063 aluminum alloy in valve cooling system of converter station was investigated by immersion corrosion test and electrochemical test. The results show that ethylene glycol accelerated the corrosion of 6063 aluminum alloy whether or not it was electrified, and the corrosion of 6063 aluminum alloy was aggravated with the increase of ethylene glycol content. In addition, the corrosion rate was much higher when 10 mA DC current was entered. Furthermore, ethylene glycol was oxidized to glycolic acid, ethane diacid and other corrosive substances, accelerating the corrosion of 6063 aluminum alloy. Therefore, in practical application, the corrosion of 6063 aluminum alloy by ethylene glycol should be considered and the corresponding countermeasures should be taken.
中图分类号 TG174.4 DOI 10.11973/fsyfh-202004002
所属栏目 试验研究
基金项目 国网浙江省电力有限公司科研项目（5211DS160023）
收稿日期 2018/9/11
修改稿日期
网络出版日期
作者单位点击查看
联系人作者朱志平(zzp8389@163.com)
引用该论文: YU Zhiyong,SONG Xiaoning,CHENG Yijie,FENG Likui,HONG Canfei,YANG Lei,ZHU Zhiping. Effect of Ethylene Glycol on Corrosion Behavior of 6063 Aluminum Alloy in Valve Cooling System[J]. Corrosion & Protection, 2020, 41(4): 7
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】舒印彪. 我国特高压输电的发展与实施[J]. 中国电力,2005,38(11):1-8.
【2】赵杰. 高压直流输电的前沿技术[J]. 中国电力,2005,38(10):1-6.
【3】电力行业电厂化学标准化技术委员会. 高压直流输电换流阀冷却水运行管理导则:DL/T 1716-2017[S]. 北京:中国电力出版社,2017.
【4】齐晶. 乙二醇生产工艺及市场分析[D]. 大庆:东北石油大学,2016.
【5】李国兴,姜子秋,关艳玲,等. 换流站换流阀内冷却水水质要求与控制[J]. 黑龙江电力,2013,35(6):542-545.
【6】范金龙,龚敏,侯肖,等. 3A21铝合金在乙二醇水溶液中的腐蚀行为[J]. 腐蚀与防护,2014,35(11):1116-1121.
【7】王远游,郝志杰,林睿. 天广直流工程换流阀冷却系统腐蚀与沉积[J]. 高电压技术,2006,32(9):80-83.
【8】李振宇,丁德,曹顺安. 二氧化碳对换流阀铝合金散热器冲刷腐蚀影响分析[J]. 清洗世界,2016,32(10):28-32.
【9】赵文亮. 高压直流输电换流阀晶闸管铝散热器腐蚀问题研究[J]. 清洗世界,2015,31(12):1-3.
【10】金星,饶楚仪,高立新,等. 铝合金在乙二醇-水模拟冷却液中的腐蚀行为[J]. 材料保护,2011,44(9):15-17.
【11】威廉斯,弗莱明. 有机化学中的光谱分析[M]. 北京:北京大学出版社,2001.
【12】WANG D P,ZHANG D Q,LEE K Y,et al. Performance of AA5052 alloy anode in alkaline ethylene glycol electrolyte with dicarboxylic acids additives for aluminium-air batteries[J]. Journal of Power Sources,2015,297:464-471.
【13】王娜娜,王锋涛,常亮,等. 锅炉补给水中典型有机物分解规律及其对低压缸叶片腐蚀特性研究[J]. 中国腐蚀与防护学报,2017,37(6):597-694.
【14】ORLIKOWSKI J,RYL J,JARZYNKA M,et al. Instantaneous impadance monitoring of aluminum alloy 7075 corrosion in borate bufffer with admixed chloride ions[J]. Corrosion 2015,71(7):828-838.
【15】李丽,苏霄. 1050A铝合金模拟海洋大气环境腐蚀行为的中性盐雾试验[J]. 腐蚀与防护,2014,35(4):367-370.
【16】ZHANG D Q,ZHOU L X,RAO C Y,et al. Effect of pH and glycolic acid on corrosion of AA6061 alloy in ethylene glycol-water solution[J]. Materials & Corrosion,2014,65(1):31-37.
【17】杨绮琴,方北龙,童叶翔. 应用电化学[M]. 2版. 广州:中山大学出版社,2005.
【18】POURBAIX M,FRANKLIN J A. Atlas of electrochemical equilibria in aqueous solutions[J]. Atlas of Electrochemical Equilibria in Aqueous Solutions,1966,1(4):471-471.
【19】曹楚南. 腐蚀电化学原理[M]. 3版. 北京:化学工业出版社,2008.
【20】孟宇,张俐,史然峰,等. 15CrMo钢在含有SO42-的模拟汽轮机初凝水中的腐蚀特性[J]. 腐蚀与防护,2014,35(12):1208-1211.
【21】房本岭,杜翠薇,丁德,等. 典型接地材料在陕北黄土高原土壤模拟液中的短期腐蚀行为[J]. 材料保护,2018,51(4):43-46.
【22】熊立斌,孟若愚. 碳钢管储运腐蚀因子分析[J]. 石油和化工设备,2017,20(5):131-133.
【2】赵杰. 高压直流输电的前沿技术[J]. 中国电力,2005,38(10):1-6.
【3】电力行业电厂化学标准化技术委员会. 高压直流输电换流阀冷却水运行管理导则:DL/T 1716-2017[S]. 北京:中国电力出版社,2017.
【4】齐晶. 乙二醇生产工艺及市场分析[D]. 大庆:东北石油大学,2016.
【5】李国兴,姜子秋,关艳玲,等. 换流站换流阀内冷却水水质要求与控制[J]. 黑龙江电力,2013,35(6):542-545.
【6】范金龙,龚敏,侯肖,等. 3A21铝合金在乙二醇水溶液中的腐蚀行为[J]. 腐蚀与防护,2014,35(11):1116-1121.
【7】王远游,郝志杰,林睿. 天广直流工程换流阀冷却系统腐蚀与沉积[J]. 高电压技术,2006,32(9):80-83.
【8】李振宇,丁德,曹顺安. 二氧化碳对换流阀铝合金散热器冲刷腐蚀影响分析[J]. 清洗世界,2016,32(10):28-32.
【9】赵文亮. 高压直流输电换流阀晶闸管铝散热器腐蚀问题研究[J]. 清洗世界,2015,31(12):1-3.
【10】金星,饶楚仪,高立新,等. 铝合金在乙二醇-水模拟冷却液中的腐蚀行为[J]. 材料保护,2011,44(9):15-17.
【11】威廉斯,弗莱明. 有机化学中的光谱分析[M]. 北京:北京大学出版社,2001.
【12】WANG D P,ZHANG D Q,LEE K Y,et al. Performance of AA5052 alloy anode in alkaline ethylene glycol electrolyte with dicarboxylic acids additives for aluminium-air batteries[J]. Journal of Power Sources,2015,297:464-471.
【13】王娜娜,王锋涛,常亮,等. 锅炉补给水中典型有机物分解规律及其对低压缸叶片腐蚀特性研究[J]. 中国腐蚀与防护学报,2017,37(6):597-694.
【14】ORLIKOWSKI J,RYL J,JARZYNKA M,et al. Instantaneous impadance monitoring of aluminum alloy 7075 corrosion in borate bufffer with admixed chloride ions[J]. Corrosion 2015,71(7):828-838.
【15】李丽,苏霄. 1050A铝合金模拟海洋大气环境腐蚀行为的中性盐雾试验[J]. 腐蚀与防护,2014,35(4):367-370.
【16】ZHANG D Q,ZHOU L X,RAO C Y,et al. Effect of pH and glycolic acid on corrosion of AA6061 alloy in ethylene glycol-water solution[J]. Materials & Corrosion,2014,65(1):31-37.
【17】杨绮琴,方北龙,童叶翔. 应用电化学[M]. 2版. 广州:中山大学出版社,2005.
【18】POURBAIX M,FRANKLIN J A. Atlas of electrochemical equilibria in aqueous solutions[J]. Atlas of Electrochemical Equilibria in Aqueous Solutions,1966,1(4):471-471.
【19】曹楚南. 腐蚀电化学原理[M]. 3版. 北京:化学工业出版社,2008.
【20】孟宇,张俐,史然峰,等. 15CrMo钢在含有SO42-的模拟汽轮机初凝水中的腐蚀特性[J]. 腐蚀与防护,2014,35(12):1208-1211.
【21】房本岭,杜翠薇,丁德,等. 典型接地材料在陕北黄土高原土壤模拟液中的短期腐蚀行为[J]. 材料保护,2018,51(4):43-46.
【22】熊立斌,孟若愚. 碳钢管储运腐蚀因子分析[J]. 石油和化工设备,2017,20(5):131-133.
相关信息