X52输气管道腐蚀失效分析
Corrosion Failure Analysis of X52 Gas Pipeline
摘 要
某油气田X52螺旋焊管外壁发生局部腐蚀，通过送检管段理化性能测试、土壤环境分析、硫酸盐还原菌（SRB）腐蚀试验等系统研究了该管道腐蚀失效的原因。结果表明：该X52螺旋焊管的化学成分和组织均符合技术规范的要求；管体周围土壤含水量较高且含有大量的硫酸盐和硫酸盐还原菌，管道底部防腐蚀层剥落区发生硫酸盐还原菌的厌氧腐蚀，导致管体局部产生无定向分布的严重蚀坑。
硫酸盐还原菌
硫化氢
失效分析
microbial corrosion
sulfate reducing bacteria
hydrogen sulfide
failure analysis
Abstract
Localized corrosion occurred on the outer walls of X52 spiral welded pipeline in a certain oil and gas field. The failure reasons for corrosion of the pipeline were studied by testing the physical and chemical properties of the test pipe section, soil environment analysis, sulfate reducing bacteria (SRB) corrosion testing. The results show that the chemical composition and microstructure of X52 spiral welded pipe conformed to the requirements in technical specifications. The soil around the pipe body had a high moisture content and contained a large amount of sulfate and sulfate reducing bacteria. Anaerobic corrosion of sulfate reducing bacteria happened in the peeling area of the anticorrosive layer at the bottom of the pipe, resulting in severe corrosion pits distributing on localized pipe body without direction.
中图分类号 TG172 DOI 10.11973/fsyfh-202004015
所属栏目 失效分析
基金项目 国家自然科学基金青年科学基金（51702258）；华中科技大学材料成型与模具技术国家重点实验室开放课题研究基金（P2017-005）；陕西省教育厅专项科研计划项目（17JK0598）
收稿日期 2019/6/10
修改稿日期
网络出版日期
作者单位点击查看
引用该论文: ZHANG Ke,ZHU Lixia,HE Zhi,LI Kai,LIU Chang. Corrosion Failure Analysis of X52 Gas Pipeline[J]. Corrosion & Protection, 2020, 41(4): 73
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】高鹏,高振宇,杜东,等. 2017年中国油气管道行业发展及展望[J]. 中国石油经济,2018,26(3):21-27.
【2】张学元,王凤平,杜元龙,等. 油气工业中细菌的腐蚀和预防[J]. 石油与天然气化工,1999,28(1):52-56.
【3】XIAO R J,XIAO G Q,HUANG B,et al. Corrosion failure cause analysis and evaluation of corrosion inhibitors of Ma Huining oil pipeline[J]. Engeering Failure Analysis,2016,68:113.
【4】牛涛,杨建炜,王林,等. 硫酸盐还原菌作用下X60管线钢的腐蚀穿孔机制[J]. 腐蚀与防护,2014,35(10):1060-1064.
【5】罗金恒,王曰燕,赵新伟,等. 在役油气管道土壤腐蚀研究现状[J]. 石油工程建设,2004,30(6):1-6.
【6】蒋波,弓爱君,李晓刚,等. 硫酸盐还原菌在8个土壤试验站中的分布规律研究[J]. 化学与生物工程,2008,25(4):54-56.
【7】ENNING D,GARREIFS J. Corrosion of iron by sulfate-reducing bacteria:new views of an old problem[J]. Applied & Environmental Microbiology,2014,80(4):1226-1236.
【8】张小里,刘海洪,陈开勋,等. 硫酸盐还原菌生长规律的研究[J]. 西北大学学报(自然科学版),1999,29(5):1-6.
【9】管方,翟晓凡,段继周,等. 阴极极化对硫酸盐还原菌腐蚀影响的研究进展[J]. 中国腐蚀与防护学报,2018,38(1):1-9.
【10】VON WIZOGEN KUHR C A,VAN VIUGT L S,DE GRAFI-TEERING,et al. Electrobiochemich process manscrobe gonden water[J]. Corrosion,1984,18(6):147.
【11】朱绒霞,那静彦,郭生武,等. 硫酸盐还原菌的腐蚀机理[J]. 空军工程大学学报(自然科学版),2000,1(3):11-12.
【12】王丹,谢飞,吴明,等. 硫酸盐还原菌对X80钢应力腐蚀开裂行为的影响[J]. 材料热处理学报,2016,37(5):198-203.
【13】卢旭东,田力,吕法阳. 某海上油田生产水系统管线的腐蚀原因[J]. 腐蚀与防护,2019,40(3):224-229.
【14】KING R A. Study on mechanism of microbiology corrosion[J]. Nature,1971,233(5):491-492.
【2】张学元,王凤平,杜元龙,等. 油气工业中细菌的腐蚀和预防[J]. 石油与天然气化工,1999,28(1):52-56.
【3】XIAO R J,XIAO G Q,HUANG B,et al. Corrosion failure cause analysis and evaluation of corrosion inhibitors of Ma Huining oil pipeline[J]. Engeering Failure Analysis,2016,68:113.
【4】牛涛,杨建炜,王林,等. 硫酸盐还原菌作用下X60管线钢的腐蚀穿孔机制[J]. 腐蚀与防护,2014,35(10):1060-1064.
【5】罗金恒,王曰燕,赵新伟,等. 在役油气管道土壤腐蚀研究现状[J]. 石油工程建设,2004,30(6):1-6.
【6】蒋波,弓爱君,李晓刚,等. 硫酸盐还原菌在8个土壤试验站中的分布规律研究[J]. 化学与生物工程,2008,25(4):54-56.
【7】ENNING D,GARREIFS J. Corrosion of iron by sulfate-reducing bacteria:new views of an old problem[J]. Applied & Environmental Microbiology,2014,80(4):1226-1236.
【8】张小里,刘海洪,陈开勋,等. 硫酸盐还原菌生长规律的研究[J]. 西北大学学报(自然科学版),1999,29(5):1-6.
【9】管方,翟晓凡,段继周,等. 阴极极化对硫酸盐还原菌腐蚀影响的研究进展[J]. 中国腐蚀与防护学报,2018,38(1):1-9.
【10】VON WIZOGEN KUHR C A,VAN VIUGT L S,DE GRAFI-TEERING,et al. Electrobiochemich process manscrobe gonden water[J]. Corrosion,1984,18(6):147.
【11】朱绒霞,那静彦,郭生武,等. 硫酸盐还原菌的腐蚀机理[J]. 空军工程大学学报(自然科学版),2000,1(3):11-12.
【12】王丹,谢飞,吴明,等. 硫酸盐还原菌对X80钢应力腐蚀开裂行为的影响[J]. 材料热处理学报,2016,37(5):198-203.
【13】卢旭东,田力,吕法阳. 某海上油田生产水系统管线的腐蚀原因[J]. 腐蚀与防护,2019,40(3):224-229.
【14】KING R A. Study on mechanism of microbiology corrosion[J]. Nature,1971,233(5):491-492.
相关信息