Leakage Reason of 0Cr18Ni9 Stainless Steel Natural Gas Pipeline
摘 要
某海上天然气输送管线采用0Cr18Ni9无缝钢管,管线在安装结束后,在水压试验时发现有泄漏现象。利用直读光谱仪、拉伸试验机、光学显微镜、扫描电子显微镜等分析手段,对泄漏失效的天然气管线进行了分析。结果表明:泄漏管线材料的冶金质量符合技术要求,但管线内表面泄漏部位存在翘皮,在翘皮和基体之间产生了缝隙腐蚀,蚀坑穿透管壁导致管线泄漏。
Abstract
0Cr18Ni9 seamless steel pipe was used in an offshore natural gas transmission pipeline. After the installation of the pipeline, a leakage was found during the water pressure test. The leaked natural gas pipeline was analyzed by direct reading spectrometer, tensile testing machine, optical metallurgical microscopy, scanning electron microscopy and other analysis methods. The results show that the metallurgical quality of the leaked pipeline met the technical requirements, but there was a warped skin on the inner surface of the pipeline, and crevice corrosion occurred between the warped skin and the substrate, resulting in the pipeline perforation and leakage.
中图分类号 TG174 DOI 10.11973/fsyfh-202005015
所属栏目 失效分析
基金项目
收稿日期 2019/9/17
修改稿日期
网络出版日期
作者单位点击查看
引用该论文: LIU Xiaogui. Leakage Reason of 0Cr18Ni9 Stainless Steel Natural Gas Pipeline[J]. Corrosion & Protection, 2020, 41(5): 73
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】高磊,王保成. 温度对SUS304与SUS430不锈钢耐腐蚀性及其钝化膜半导体性能的影响[J]. 太原理工大学学报,2015,46(3):268-273.
【2】解群,翟祥华,葛红花. 氯离子和硫离子对不锈钢侵蚀性比较[J]. 华东电力,2003,31(12):1-3.
【3】樊海燕. 水驱在用埋地钢管腐蚀失效原因[J]. 油气田地面工程,2012,31(1):59-60.
【4】苏怀,张劲军,杨楠,等. 大型天然气管网可靠性评价方法研究进展[J]. 油气储运,2016,35(1):7-15.
【5】邓志龙,雒设计,申毅,等. X80管线钢在阴极极化条件下的点腐蚀行为[J]. 材料保护,2016,49(3):34-38.
【6】张皓玥,王津梅. 金属缝隙腐蚀的成因及实验验证[J]. 表面技术,2017,46(2):204-207.
【7】曹楚南. 腐蚀电化学原理[M]. 北京:化学工业出版社,2004.
【2】解群,翟祥华,葛红花. 氯离子和硫离子对不锈钢侵蚀性比较[J]. 华东电力,2003,31(12):1-3.
【3】樊海燕. 水驱在用埋地钢管腐蚀失效原因[J]. 油气田地面工程,2012,31(1):59-60.
【4】苏怀,张劲军,杨楠,等. 大型天然气管网可靠性评价方法研究进展[J]. 油气储运,2016,35(1):7-15.
【5】邓志龙,雒设计,申毅,等. X80管线钢在阴极极化条件下的点腐蚀行为[J]. 材料保护,2016,49(3):34-38.
【6】张皓玥,王津梅. 金属缝隙腐蚀的成因及实验验证[J]. 表面技术,2017,46(2):204-207.
【7】曹楚南. 腐蚀电化学原理[M]. 北京:化学工业出版社,2004.
相关信息