Effect of Al-5Ti-1B Refiner Addition Amount on Microstructure and Tensile Properties of Cast Aluminum Alloy Containing Ce
摘 要
在添加质量分数0.1%铈的基础上,对比研究Al-5Ti-1B细化剂质量分数(0~0.4%)对A356铸造铝合金组织及拉伸性能的影响。结果表明:随着Al-5Ti-1B细化剂含量的增加,α-Al树枝晶的平均二次枝晶间距先降后增,当细化剂的质量分数为0.2%时,平均二次枝晶间距最小,为37.3 μm;添加适量细化剂能促使共晶硅由狭长纤维状向粗短棒状的转变,从而降低共晶硅的等效直径和长宽比,过量细化剂则会引起共晶硅的尖锐化;添加细化剂后,铝合金的抗拉强度和断后伸长率均提高,且随着细化剂含量的增加呈先增后降的趋势;添加质量分数0.2%细化剂时铝合金的综合变质效果最佳,此时铝合金的拉伸性能最佳,抗拉强度和断后伸长率较未添加细化剂时的分别提高了20.7%和66.7%。
Abstract
On the basis of adding 0.1wt% Ce, the effect of the Al-5Ti-1B refiner content (0wt%-0.4wt%) on the microstructure and tensile properties of A356 cast aluminum alloy was comparatively studied. The results show that with increasing content of Al-5Ti-1B refiner, the average secondary dendrite spacing of α-Al dendrite decreased first and then increased, and reached the smallest value of 37.3 μm when the content of refiner was 0.2wt%. The proper amount of refiner promoted the eutectic silicon shape changing from long and narrow fibrous to thick and short rods, and resulted in the reduction of equivalent diameter and aspect ratio of eutectic silicon; but the excessive amount of refiner caused the sharpening of eutectic silicon. After adding the refiner, the tensile strength and percentage elongation after fracture of the aluminum alloy all increased, and increased first and then decreased with increasing refiner content. The comprehensive modification effect of the aluminum alloy after adding 0.2wt% refiner was the best, and the tensile properties were the best; the tensile strength and percentage elongation after fracture increased by 20.7% and 66.7% compared with those without adding refiner, respectively.
中图分类号 TG292 DOI 10.11973/jxgccl202005005
所属栏目 试验研究
基金项目 湖南省自然科学基金资助项目(2018JJ5054);湖南省教育厅科学研究项目(19C1877);江西省教育厅科学研究项目(GJJ161558)
收稿日期 2020/1/5
修改稿日期 2020/4/9
网络出版日期
作者单位点击查看
备注王波(1987-),女,湖南张家界人,讲师,硕士
引用该论文: WANG Bo,LIU Rangxian,YU Hongwei,LUO Weichao,ZHAO Wenlong. Effect of Al-5Ti-1B Refiner Addition Amount on Microstructure and Tensile Properties of Cast Aluminum Alloy Containing Ce[J]. Materials for mechancial engineering, 2020, 44(5): 21~27
王波,刘让贤,余洪伟,罗伟超,赵文龙. Al-5Ti-1B细化剂添加量对含铈铸造铝合金组织和拉伸性能的影响[J]. 机械工程材料, 2020, 44(5): 21~27
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】谢丽君.用于汽车工业的铸造铝合金评述[J].轻金属,2013(11):57-59.
【2】文浩,罗斌,谢达明.压铸铝合金在汽车上的应用及发展[J].世界有色金属,2017(14):269.
【3】李龙,夏承东,宋友宝,等.铝合金在新能源汽车工业的应用现状及展望[J].轻合金加工技术,2017,45(9):18-25.
【4】沈小岑.稀土Sc及微量元素复合添加对A356/7合金微观组织与力学性能的影响[D].天津:天津大学,2017.
【5】LI M,LI Y D,HUANG X F,et al.Solidification behavior and rheo-diecasting microstructure of A356 aluminum alloy prepared by self-inoculation method[J].China Foundry, 2017,14(1):1-9.
【6】欧阳晓贤.汽车铝合金转向节挤压铸造成形技术的研究[D].广州:华南理工大学,2011.
【7】LIU X R, ZHANG Y D, BEAUSIR B, et al. Twin-controlled growth of eutectic Si in unmodified and Sr-modified Al-12.7%Si alloys investigated by SEM/EBSD[J].Acta Materialia, 2015,97:338-347.
【8】仲召军,李龙,周德敬.铸造Al-Si合金细化变质处理技术的研究进展[J].铸造,2016,65(3):242-247.
【9】姜峰,索忠源,刘祥玲,等.热处理对不同Sr含量变质A356合金组织及力学性能的影响[J].铸造,2019,68(1):29-33.
【10】MIRESMAEILI S M,SHABESTARI S G,BOUTORABI S M A.Effect of melt filtration on porosity formation in Sr-modified A356 aluminium alloy[J].International Journal of Cast Metals Research, 2003,16(6):541-548.
【11】MAN Z, YANG G C, YAO L J, et al. Influence of Al-Ti-B addition on the microstructure and mechanical properties of A356 alloys[J]. Rare Metals, 2009, 28(2):181-186.
【12】潘复生,周守则,石功奇,等.稀土铝合金中稀土作用的研究现状和展望[J].兵器材料科学与工程,1990,13(2):17-26.
【13】段海丽,张恒华,邵光杰,等.镧对A356铝合金变质及其机制的研究[J].中国稀土学报,2005,23(增刊2):94-98.
【14】杨怀德,龙思远,朱姝晴,等.硼化物、富Ce混合稀土对再生Al-Si合金中富铁相变质行为的影响[J].稀有金属材料与工程,2016,45(1):187-191.
【15】杨军军,聂祚仁,付静波,等.稀土在铝合金中的作用及研究进展[J].北京工业大学学报,2002,28(4):500-505.
【16】LU L,DAHLE A K.Effects of combined additions of Sr and AlTiB grain refiners in hypoeutectic Al-Si foundry alloys[J].Materials Science and Engineering:A,2006,435/436:288-296.
【17】陈鸿玲,傅高升,黄利光,等.AlTiBRE中间合金中各元素含量优化及RE作用分析[J].铸造,2008,57(5):436-441.
【18】马自力. 新型Al-Sr-RE复合细化变质剂及其在ZL102合金中的作用[J]. 稀有金属, 2001, 25(1):60-63.
【19】李苗.Al-Ti-C-RE细化剂的低温绿色制备及其细化行为研究[D].郑州:郑州大学,2011.
【20】LIAO H C,SUN G X.Mutual poisoning effect between Sr and B in Al-Si casting alloys[J].Scripta Materialia, 2003,48(8):1035-1039.
【21】陈亚军,许庆彦,黄天佑.稀土铝钛硼中间合金的细化能力与长效性[J].中国有色金属学报,2007,17(8):1232-1239.
【22】WANG X J,XU C,MUHAMMAD A,et al.Effects of Al-Ti-B-RE grain refiner on microstructure and mechanical properties of Al-7.0Si-0.55Mg alloy[J].Transactions of Nonferrous Metals Society of China, 2014,24(7):2244-2250.
【2】文浩,罗斌,谢达明.压铸铝合金在汽车上的应用及发展[J].世界有色金属,2017(14):269.
【3】李龙,夏承东,宋友宝,等.铝合金在新能源汽车工业的应用现状及展望[J].轻合金加工技术,2017,45(9):18-25.
【4】沈小岑.稀土Sc及微量元素复合添加对A356/7合金微观组织与力学性能的影响[D].天津:天津大学,2017.
【5】LI M,LI Y D,HUANG X F,et al.Solidification behavior and rheo-diecasting microstructure of A356 aluminum alloy prepared by self-inoculation method[J].China Foundry, 2017,14(1):1-9.
【6】欧阳晓贤.汽车铝合金转向节挤压铸造成形技术的研究[D].广州:华南理工大学,2011.
【7】LIU X R, ZHANG Y D, BEAUSIR B, et al. Twin-controlled growth of eutectic Si in unmodified and Sr-modified Al-12.7%Si alloys investigated by SEM/EBSD[J].Acta Materialia, 2015,97:338-347.
【8】仲召军,李龙,周德敬.铸造Al-Si合金细化变质处理技术的研究进展[J].铸造,2016,65(3):242-247.
【9】姜峰,索忠源,刘祥玲,等.热处理对不同Sr含量变质A356合金组织及力学性能的影响[J].铸造,2019,68(1):29-33.
【10】MIRESMAEILI S M,SHABESTARI S G,BOUTORABI S M A.Effect of melt filtration on porosity formation in Sr-modified A356 aluminium alloy[J].International Journal of Cast Metals Research, 2003,16(6):541-548.
【11】MAN Z, YANG G C, YAO L J, et al. Influence of Al-Ti-B addition on the microstructure and mechanical properties of A356 alloys[J]. Rare Metals, 2009, 28(2):181-186.
【12】潘复生,周守则,石功奇,等.稀土铝合金中稀土作用的研究现状和展望[J].兵器材料科学与工程,1990,13(2):17-26.
【13】段海丽,张恒华,邵光杰,等.镧对A356铝合金变质及其机制的研究[J].中国稀土学报,2005,23(增刊2):94-98.
【14】杨怀德,龙思远,朱姝晴,等.硼化物、富Ce混合稀土对再生Al-Si合金中富铁相变质行为的影响[J].稀有金属材料与工程,2016,45(1):187-191.
【15】杨军军,聂祚仁,付静波,等.稀土在铝合金中的作用及研究进展[J].北京工业大学学报,2002,28(4):500-505.
【16】LU L,DAHLE A K.Effects of combined additions of Sr and AlTiB grain refiners in hypoeutectic Al-Si foundry alloys[J].Materials Science and Engineering:A,2006,435/436:288-296.
【17】陈鸿玲,傅高升,黄利光,等.AlTiBRE中间合金中各元素含量优化及RE作用分析[J].铸造,2008,57(5):436-441.
【18】马自力. 新型Al-Sr-RE复合细化变质剂及其在ZL102合金中的作用[J]. 稀有金属, 2001, 25(1):60-63.
【19】李苗.Al-Ti-C-RE细化剂的低温绿色制备及其细化行为研究[D].郑州:郑州大学,2011.
【20】LIAO H C,SUN G X.Mutual poisoning effect between Sr and B in Al-Si casting alloys[J].Scripta Materialia, 2003,48(8):1035-1039.
【21】陈亚军,许庆彦,黄天佑.稀土铝钛硼中间合金的细化能力与长效性[J].中国有色金属学报,2007,17(8):1232-1239.
【22】WANG X J,XU C,MUHAMMAD A,et al.Effects of Al-Ti-B-RE grain refiner on microstructure and mechanical properties of Al-7.0Si-0.55Mg alloy[J].Transactions of Nonferrous Metals Society of China, 2014,24(7):2244-2250.
相关信息