Analysis of Corrosion and Thinning Causes for a High Temperature Steam Drum Head in Boiler
摘 要
采用光学显微镜、扫描电子显微镜、能谱分析、硬度测试、化学成分分析等多种材料学分析手段并结合现场的实际运行情况对某锅炉汽包封头腐蚀减薄的原因进行了分析。结果表明:汽包封头材料的各项性能都正常,腐蚀与封头材料无关;介质水中存在溶解氧和硫酸盐类物质是汽包封头发生腐蚀的主要原因,高温加速了腐蚀进程;同时汽包结构设计不合理,使高温水汽直接对汽包封头进行冲刷,导致封头区域的减薄速度大于其他区域的。
Abstract
By means of optical microscopy, scanning electron microscopy, energy spectrum analysis, hardness testing, chemical composition analysis and other means of material science analysis, combined with the actual operation situation on site, the causes of corrosion and thinning of a steam drum head were analyzed. The results show that properties of the material for steam drum were normal, so material was not the reason for corrosion of steam drum. The presence of dissolved oxygen and sulfates in medium water was the main reason for the corrosion of the drum head, and high temperature accelerated the corrosion process. The design of drum structure was unreasonable, so that high temperature water vapor directly eroded the head of drum, which resulted in the speed of thinning of the head area faster than that of other areas.
中图分类号 TK22 DOI 10.11973/fsyfh-202006015
所属栏目 失效分析
基金项目
收稿日期 2018/6/12
修改稿日期
网络出版日期
作者单位点击查看
联系人作者刘元(35372497@qq.com)
引用该论文: LIU Yuan,ZHU Guobin,SUN Guofeng. Analysis of Corrosion and Thinning Causes for a High Temperature Steam Drum Head in Boiler[J]. Corrosion & Protection, 2020, 41(6): 71
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】高全,张军营,邱纪华,等. 燃煤电站锅炉高温腐蚀特征的研究[J]. 热能动力工程,2007,22(3):292-296.
【2】车畅,钱公,钱林峰,等. 某超临界锅炉低温再热器管腐蚀原因分析[J]. 热能动力工程,2017,32(2):121-126.
【3】郭平. 余热锅炉汽包的腐蚀分析[J]. 品牌与标准化,2010(14):18.
【4】林涛,李信. 某汽包封头减薄泄漏原因分析[J]. 化工管理,2017(20):122.
【2】车畅,钱公,钱林峰,等. 某超临界锅炉低温再热器管腐蚀原因分析[J]. 热能动力工程,2017,32(2):121-126.
【3】郭平. 余热锅炉汽包的腐蚀分析[J]. 品牌与标准化,2010(14):18.
【4】林涛,李信. 某汽包封头减薄泄漏原因分析[J]. 化工管理,2017(20):122.
相关信息