制样参数对聚丙烯透明料雾度的影响
Effect of Sample Preparation Parameters on Haze of Polypropylene Transparent Material
摘 要
以无规共聚聚丙烯透明料为例，采用正交试验方法，研究了制样参数对聚丙烯透明料雾度的影响，并以此为标准确定了最佳的制样参数。结果表明：影响雾度的主要制样参数分别为注射压力、注射速度、模具温度、熔体温度。最佳制样参数为注射压力75 MPa，注射速度40 mm·s-1，模具温度40 ℃，熔体温度200 ℃。
无规共聚聚丙烯
雾度
制样参数
polypropylene transparent material
random copolymerized polypropylene
haze
sample preparation parameter
Abstract
Taking random copolymerized polypropylene transparent material as an example, the influence of sample preparation parameters on haze of polypropylene transparent material was determined by orthogonal test method, and the best sample preparation parameters were determined. The results show that the main parameters affecting haze were injection pressure, injection speed, mold temperature and melt temperature. The best sample preparation parameters were injection pressure 75 MPa, injection speed 40 mm·s-1, mold temperature 40 ℃, melt temperature 200 ℃.
中图分类号 TQ325.1+2 DOI 10.11973/lhjy-wl202008004
所属栏目 试验技术与方法
基金项目
收稿日期 2020/5/9
修改稿日期
网络出版日期
作者单位点击查看
备注封春艳(1986-),女,工程师,主要从事树脂及橡胶的分析检验工作,fengcy_zh@petrochina.com.cn
引用该论文: FENG Chunyan,HUANG Li,LIU Guoqiang,LIU Yonghui,CHEN Weihua. Effect of Sample Preparation Parameters on Haze of Polypropylene Transparent Material[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2020, 56(8): 16～18
封春艳,黄莉,刘国强,刘永辉,陈伟华. 制样参数对聚丙烯透明料雾度的影响[J]. 理化检验－物理分册, 2020, 56(8): 16～18
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】王加龙,石文鹏.塑料注塑工[M].1版.北京:化学工业出版社,2006.
【2】周维祥.塑料测试技术[M].北京:化学工业出版社,1997.
【3】马德柱,何平笙,徐种德,等.高聚物的结构与性能[M].北京:科学出版社,1995.
【4】励杭泉,张晨.聚合物物理学[M].北京:化学工业出版社,2007.
【5】蔡恒志,谢树清,王文广.注塑操作工[M].广州:广东科技出版社,2008.
【6】吴唯.注射成型的温控与时控参数对聚丙烯性能的影响[J].合成树脂及塑料,1994,11(1):18-22.
【2】周维祥.塑料测试技术[M].北京:化学工业出版社,1997.
【3】马德柱,何平笙,徐种德,等.高聚物的结构与性能[M].北京:科学出版社,1995.
【4】励杭泉,张晨.聚合物物理学[M].北京:化学工业出版社,2007.
【5】蔡恒志,谢树清,王文广.注塑操作工[M].广州:广东科技出版社,2008.
【6】吴唯.注射成型的温控与时控参数对聚丙烯性能的影响[J].合成树脂及塑料,1994,11(1):18-22.
相关信息