钛合金高锁螺栓断裂原因分析
Cause Analysis on Fracture of Titanium Alloy High Lock Bolts
摘 要
某飞机用钛合金高锁螺栓在装配过程中发生断裂。通过宏观分析、微观分析、金相检验、力学性能复查和装配现场调查等方法对螺栓的断裂原因进行了分析。结果表明：该钛合金高锁螺栓为单边弯曲应力造成的过载断裂，与螺栓制造质量无关。螺栓装配区域操作空间狭小，安装时扳手的转动平面易发生倾转，从而在螺栓上形成弯曲应力，建议改进装配工具。
高锁螺栓
过载断裂
装配应力
titanium alloy
high lock bolt
overload fracture
assembly stress
Abstract
The titanium alloy high lock bolts of an aircraft fractured during assembly. The causes of bolts fracture were analyzed by means of macro analysis, micro analysis, metallographic examination, mechanical property recheck and assembly site investigation. The results show that the bolts were an overload fracture caused by single side bending stress, which has nothing to do with the bolts manufacturing quality. The operation space of the bolts assembly area was narrow, and the rotation plane of the wrench was prone to tilt during installation, thus formed bending stress on the bolt. It is suggested to improve the assembly tool.
中图分类号 TG115.2 DOI 10.11973/lhjy-wl202008016
所属栏目 质量控制与失效分析
基金项目
收稿日期 2020/1/2
修改稿日期
网络出版日期
作者单位点击查看
备注何军(1970-),女,高级工程师,主要从事金属材料的失效分析工作,hejun132@163.com
引用该论文: HE Jun,WANG Haoyu,WANG Dawei,DING Yahong,LI Guoqing,ZHU Ling. Cause Analysis on Fracture of Titanium Alloy High Lock Bolts[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2020, 56(8): 66～69
何军,王浩宇,王大为,丁亚红,李国庆,朱苓. 钛合金高锁螺栓断裂原因分析[J]. 理化检验－物理分册, 2020, 56(8): 66～69
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】张卫方,刘德林,刘昌奎,等.钛合金螺钉脆性断裂原因分析[J].失效分析与预防,2007(2):29-33.
【2】任翀,刘风雷,赵庆云,等.轻型英制钛合金高锁螺栓制造工艺技术[J].先进连接技术,2010(23):79-81.
【3】庞小超,白明远.钛合金螺栓断裂原因分析[J].失效分析与预防,2011,6(3):182-185.
【4】张栋,钟培道,陶春虎,等.失效分析[M].北京:国防工业出版社,2013.
【5】陶春虎,刘庆瑔,曹春晓,等.航空用钛合金的失效及其预防[M].北京:国防工业出版社,2002.
【6】董新权,杨冬梅.新能源客车电容支架安装螺栓的断裂原因分析[J].理化检验(物理分册),2017,53(3):214-216.
【2】任翀,刘风雷,赵庆云,等.轻型英制钛合金高锁螺栓制造工艺技术[J].先进连接技术,2010(23):79-81.
【3】庞小超,白明远.钛合金螺栓断裂原因分析[J].失效分析与预防,2011,6(3):182-185.
【4】张栋,钟培道,陶春虎,等.失效分析[M].北京:国防工业出版社,2013.
【5】陶春虎,刘庆瑔,曹春晓,等.航空用钛合金的失效及其预防[M].北京:国防工业出版社,2002.
【6】董新权,杨冬梅.新能源客车电容支架安装螺栓的断裂原因分析[J].理化检验(物理分册),2017,53(3):214-216.
相关信息