Project validation method of AUT inspection based on DNV GL standard
摘 要
耐腐蚀合金复合材料(CRA)海底管道主要应用于高酸性油气介质的输送。规格通常是管径为168.3~508 mm,壁厚为14.1~31.6 mm,耐腐蚀合金层厚度为3 mm。根据标准DNV-OS-F101(2013)《海底管线系统》要求,全自动超声波检测(AUT)工艺需要经过验证,确保AUT与宏观切片评定的缺陷高度差值小于1 mm。由于CRA复合材料海底管道规格各异,AUT检测工艺也需要进行相应的调整。文章基于管径为508 mm、壁厚为31.6 mm (CRA厚度为3 mm)的管道进行了项目验证,通过AUT试块校准、人工缺陷焊缝制作、缺陷焊缝扫查、宏观切片和数据分析,最终评定出AUT检测工艺的缺陷检出能力和缺陷高度定量精度。有望在耐腐蚀合金复合材料(CRA)海底管道环焊缝检测工作中得到应用。
Abstract
CRA pipeline was designed for transferring the gas and oil with high acidic. The diameter of the CRA pipeline is from 168.3 mm to 508 mm with its wall thickness being between 14.1 to 31.6mm with 3mm cladding inside the pipe. Based on the requirement of DNV-OS-F101 (2013), a validation test shall be performed to verify that the height-sizing difference between AUT and macro section of the defect shall be within ±1mm. Due to the difference of the dimension of the CRA pipeline, the AUT technique shall need some adjustment. Based on the pipe with the dimension O.D 508 mm, W.T 31.6mm (internal cladding 3 mm), the article describes the details of project validation method, which includes AUT calibration, defective welds manufacturing, scanning, macro sectioning and data analysis, so as to evaluate the detection ability and height sizing accuracy of the AUT technique. It is hopeful that the practical application of the above-mentioned method in the inspection of the girth welds of CRA subsea pipeline shall be realized.
中图分类号 TG115.28
所属栏目 试验研究
基金项目
收稿日期 2020/2/27
修改稿日期
网络出版日期
作者单位点击查看
联系人作者裴彪(yimignet@163.com)
备注裴彪(1987-),男,高级工程师,主要从事海底管线质量控制及AUT技术应用方面的工作
引用该论文: PEI Biao,ZHAO Mingda,LI Yang. Project validation method of AUT inspection based on DNV GL standard[J]. Nondestructive Testing, 2020, 42(9): 28~32
裴彪,赵明达,李洋. 基于DNVGL标准的全自动超声波检测项目验证方法[J]. 无损检测, 2020, 42(9): 28~32
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】裴彪, 徐振,常宇. 耐腐蚀合金复合材料海底管道环焊缝各区域全自动超声波检测[J].无损检测,2016,38(9):46-48.
【2】孙晓明, 裴彪,尤卫宏,等. 海底管道环焊缝AUT检测缺陷高度定量分析[J].中国造船,2013,54(2):353-357.
【2】孙晓明, 裴彪,尤卫宏,等. 海底管道环焊缝AUT检测缺陷高度定量分析[J].中国造船,2013,54(2):353-357.
相关信息