轮毂螺栓在加工过程中断裂的原因
Fracture Causes of Hub Bolts during Machining
摘 要
某厂生产的40Cr钢轮毂螺栓在车削过程中出现小批量断裂事故。采用断口分析、化学成分分析、金相检验及硬度测试等方法，对轮毂螺栓的断裂原因进行了分析。结果表明：轮毂螺栓在加热炉中发生局部过烧，使得该部位的晶间结合力降低，导致螺栓在车削过程中发生脆性断裂。
过烧
断裂
晶间结合力
车削
hub bolt
over burnt
fracture
intergranular adhesion
turning
Abstract
A small number of fracture accidents occurred in the turning process of 40Cr steel hub bolts produced by a factory. The fracture causes of the hub bolts were analyzed by means of fracture analysis, chemical composition analysis, metallographic examination and hardness test. The results show that the hub bolts were burned locally in the heating furnace, which reduced the intergranular adhesion of this part, and caused brittle fracture of the bolts in the turning process.
中图分类号 TG115.2 DOI 10.11973/lhjy-wl202010012
所属栏目 质量控制与失效分析
基金项目
收稿日期 2020/8/3
修改稿日期
网络出版日期
作者单位点击查看
备注范德国(1986-),男,助理工程师,主要从事金属材料的理化检验与失效分析工作,fdg0536@163.com
引用该论文: FAN Deguo. Fracture Causes of Hub Bolts during Machining[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2020, 56(10): 51～53
范德国. 轮毂螺栓在加工过程中断裂的原因[J]. 理化检验－物理分册, 2020, 56(10): 51～53
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】甘美露,张强,王书强,等.42CrMo钢蜗杆开裂原因分析[J].理化检验(物理分册),2020,56(2):39-43.
【2】蔡晓文.S48C锻件开裂原因分析与研究[J].热加工工艺,2013,42(23):203-206.
【3】龚丹梅,袁鹏斌,余世杰,等.S135钢级钻杆管体断裂原因分析[J].金属热处理,2013,38(7):173-175.
【2】蔡晓文.S48C锻件开裂原因分析与研究[J].热加工工艺,2013,42(23):203-206.
【3】龚丹梅,袁鹏斌,余世杰,等.S135钢级钻杆管体断裂原因分析[J].金属热处理,2013,38(7):173-175.
相关信息