Fracture Causes of Centrifuge Drum
摘 要
某公司离心机转鼓体使用仅1 a(年)就发生了断裂,采用宏观分析、化学成分分析、硬度测试、力学性能试验、金相检验、扫描电镜分析及能谱分析等方法对转鼓体的断裂原因进行了分析。结果表明:材料为双相不锈钢的转鼓体在固溶处理时操作不当,使得其显微组织中存在大量硬脆的σ相,转鼓体在高速运转时会产生较大的离心力,在离心力的作用下,σ相密集处会萌生裂纹并扩展,最终导致转鼓体发生断裂。
Abstract
The centrifuge drum of a company fractured after only one year of service. The fracture causes of drum were analyzed by means of macroscopic analysis, chemical composition analysis, hardness test, mechanical property test, metallographic examination, scanning electron microscope analysis and energy spectrum analysis. The results show that there were a lot of hard and brittle σ phase in the microstructure of the drum made of duplex stainless steel due to improper operation during solution treatment. When the drum was running at high speed, a large centrifugal force will be generated. Under the action of centrifugal force, cracks will be initiated and propagated in the dense part of σ phase, which eventually led to the fracture of the drum.
中图分类号 TG115.2 DOI 10.11973/lhjy-wl202010015
所属栏目 质量控制与失效分析
基金项目
收稿日期 2020/6/17
修改稿日期
网络出版日期
作者单位点击查看
备注杨永(1984-),男,工程师,主要从事钢铁材料的失效分析工作,15283026@qq.com
引用该论文: YANG Yong,TAN Deli. Fracture Causes of Centrifuge Drum[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2020, 56(10): 61~65
杨永,谭德力. 离心机转鼓体断裂原因[J]. 理化检验-物理分册, 2020, 56(10): 61~65
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】张贤, 钱张信.立辊压下对2507超级双相不锈钢边裂的影响[J].甘肃冶金,2020,42(1):41-43.
【2】王军,靳彤,马一鸣,等.高残余应力下2507双相不锈钢应力腐蚀开裂行为[J].压力容器,2020,37(3):50-52.
【3】李国平,裴海祥,李建春,等.σ相对S32760超级双相不锈钢组织和性能的影响[J].工程科学学报,2016,38(3):365-367.
【4】钟群鹏,赵子华.断口学[M].北京:高等教育出版社,2006.
【5】金昊昀,王荣,付洋洋.304不锈钢止回阀断裂原因分析[J].理化检验(物理分册),2020,56(4):32-35.
【2】王军,靳彤,马一鸣,等.高残余应力下2507双相不锈钢应力腐蚀开裂行为[J].压力容器,2020,37(3):50-52.
【3】李国平,裴海祥,李建春,等.σ相对S32760超级双相不锈钢组织和性能的影响[J].工程科学学报,2016,38(3):365-367.
【4】钟群鹏,赵子华.断口学[M].北京:高等教育出版社,2006.
【5】金昊昀,王荣,付洋洋.304不锈钢止回阀断裂原因分析[J].理化检验(物理分册),2020,56(4):32-35.
相关信息