12.9级高强度内六角螺栓应力腐蚀断裂原因
Cause of Stress Corrosion Fracture on Grade 12. 9 High Strength Hexagon Socket Bolt
摘 要
某12.9级高强度内六角螺栓用于车床刀具的固定，在服役过程中发生断裂。通过宏观观察、断口分析和化学成分分析等方法，结合螺栓安装位置和工作环境对螺栓的断裂原因进行了分析。结果表明：刀具在清洗时，清洗液从刀盘和刀夹缝隙中渗入，引起腐蚀，并在工作应力的作用下发生应力腐蚀断裂。
螺栓
应力腐蚀断裂
沿晶
应力
40Cr steel
bolt
stress corrosion fracture
intergranular
stress
Abstract
A grade 12. 9 high strength hexagon socket bolt was used to fix the lathe tool, which fractured in service. The causes of fracture were analyzed by means of macroscopic observation, fracture analysis and chemical composition analysis, combined with bolt installation position and working environment. The results show that the cleaning fluid entered from the gap between cutter head and tool holder during tool cleaning, which resulted in corrosion and stress corrosion fracture occurred under the working stress.
中图分类号 TG113.22 DOI 10.11973/lhjy-wl202011010
所属栏目 质量控制与失效分析
基金项目
收稿日期 2020/3/3
修改稿日期
网络出版日期
作者单位点击查看
备注刘华东(1990-),男,工程师,主要从事紧固件质量管理及失效分析工作,lhdliuhuadong@126.com
引用该论文: LIU Huadong. Cause of Stress Corrosion Fracture on Grade 12. 9 High Strength Hexagon Socket Bolt[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2020, 56(11): 43～45
刘华东. 12.9级高强度内六角螺栓应力腐蚀断裂原因[J]. 理化检验－物理分册, 2020, 56(11): 43～45
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】包锡桂. 某挖掘机高强螺栓断裂原因分析[J].理化检验(物理分册),2017,53(3):204-207.
【2】虞祯君.发动机凸轮轴正时带轮紧固螺栓断裂原因分析[J].理化检验(物理分册),2020,56(1):41-43.
【3】李炯辉.金属材料金相图谱[M].北京:机械工业出版社,2006.
【4】任颂赞,叶俭,陈德华.金相分析原理及技术[M].上海:上海科学技术文献出版社,2013.
【5】孙智,江利,应鹏展.失效分析——基础与应用[M].北京:机械工业出版社,2005.
【6】钟群鹏.材料失效诊断、预测和预防[M].长沙:中南大学出版社,2009.
【7】张栋,钟培道,陶春虎,等.失效分析[M].北京:国防工业出版社,2004.
【2】虞祯君.发动机凸轮轴正时带轮紧固螺栓断裂原因分析[J].理化检验(物理分册),2020,56(1):41-43.
【3】李炯辉.金属材料金相图谱[M].北京:机械工业出版社,2006.
【4】任颂赞,叶俭,陈德华.金相分析原理及技术[M].上海:上海科学技术文献出版社,2013.
【5】孙智,江利,应鹏展.失效分析——基础与应用[M].北京:机械工业出版社,2005.
【6】钟群鹏.材料失效诊断、预测和预防[M].长沙:中南大学出版社,2009.
【7】张栋,钟培道,陶春虎,等.失效分析[M].北京:国防工业出版社,2004.
相关信息