Cause of Corrosion Perforation on Heating Surface Tube of a HRSG
摘 要
某焦炉尾气余热锅炉受热面管发生泄漏,通过宏观分析、金相检验、扫描电镜分析、能谱分析、化学成分分析和硬度测试等方法,分析了受热面管的泄漏原因。结果表明:锅炉内水质不合格,导致受热面管在高温、高压的运行环境中发生了沸腾气泡腐蚀。腐蚀反应侵蚀了管子内壁的钝化层,且管子在水、汽两相区腐蚀反应进行的最剧烈,腐蚀深度最深,形成了不断加深的腐蚀沟槽,最终导致泄漏。
Abstract
The heating surface tube of a coke oven exhaust HRSG leaked. The causes of leakage on heating surface tube were analyzed by means of macroscopic analysis, metallographic examination, scanning electron microscope analysis, energy spectrum analysis, chemical composition analysis, hardness test. The results show that the water quality in boiler was not up to standard, which led to boiling bubble of heating surface tube in high temperature and high pressure operation environment. The corrosion reaction eroded the passivation layer on the inner wall of tube. The corrosion reaction of tube was the most severe and the corrosion depth was the deepest in the water and steam two-phase region, which formed a deepening corrosion groove and eventually led to leakage.
中图分类号 TG142.1+5 DOI 10.11973/lhjy-wl202011012
所属栏目 质量控制与失效分析
基金项目 浙江省质监系统NOI科研计划(20180109)
收稿日期 2020/3/16
修改稿日期
网络出版日期
作者单位点击查看
备注张方(1983-),男,高级工程师,主要从事金属材料失效分析及预防工作,zf961983@126.com
引用该论文: ZHANG Fang,WEI Wei,WANG Jie. Cause of Corrosion Perforation on Heating Surface Tube of a HRSG[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2020, 56(11): 51~55
张方,魏薇,王杰. 某余热锅炉受热面管腐蚀穿孔原因[J]. 理化检验-物理分册, 2020, 56(11): 51~55
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】徐柏民, 颜飞龙.锅炉压力容器入门解读[M].杭州:杭州出版社,2009.
【2】王荣.机械装备的失效分析(续前)第4讲金相分析技术(下)[J].理化检验(物理分册),2017,53(4):225-234.
【3】周昊,池作和,李凤瑞,等.根据爆口特征判断爆管原因[J].热力发电,1999(5):43-45.
【4】孙智,江利,应鹏展,等.失效分析——基础与应用[M].北京:机械工业出版社,2005.
【5】赵永宁,邱玉堂.火力发电厂金属监督[M].北京:中国电力出版社,2007.
【6】吴非文.火力发电厂高温金属运行[M].北京:水利电力出版社,1979.
【7】朱丽霞,李金凤,瞿婷婷,等.某油田用油管断裂失效分析[J].理化检验(物理分册),2017,53(7):510-514.
【8】中国腐蚀与防护学会,肖纪美.腐蚀总论——材料的腐蚀及其控制方法[M].北京:化学工业出版社,1994.
【9】张栓成,张兆杰.锅炉水处理技术[M].2版.郑州:黄河水利出版社,2010.
【10】JIN M, SHORT M. Multiphysics modeling of two-phase film boiling within porous corrosion deposits[J].Journal of Computational Physics,2016,316:504-518.
【2】王荣.机械装备的失效分析(续前)第4讲金相分析技术(下)[J].理化检验(物理分册),2017,53(4):225-234.
【3】周昊,池作和,李凤瑞,等.根据爆口特征判断爆管原因[J].热力发电,1999(5):43-45.
【4】孙智,江利,应鹏展,等.失效分析——基础与应用[M].北京:机械工业出版社,2005.
【5】赵永宁,邱玉堂.火力发电厂金属监督[M].北京:中国电力出版社,2007.
【6】吴非文.火力发电厂高温金属运行[M].北京:水利电力出版社,1979.
【7】朱丽霞,李金凤,瞿婷婷,等.某油田用油管断裂失效分析[J].理化检验(物理分册),2017,53(7):510-514.
【8】中国腐蚀与防护学会,肖纪美.腐蚀总论——材料的腐蚀及其控制方法[M].北京:化学工业出版社,1994.
【9】张栓成,张兆杰.锅炉水处理技术[M].2版.郑州:黄河水利出版社,2010.
【10】JIN M, SHORT M. Multiphysics modeling of two-phase film boiling within porous corrosion deposits[J].Journal of Computational Physics,2016,316:504-518.
相关信息