电动自行车车架焊缝开裂原因
Cause of Cracking on Weld Seam of Electric Bicycle Frame
摘 要
某公司生产的部分电动自行车出厂使用不久便发生了车架开裂现象，通过宏观观察和金相检验的方法，对车架的开裂原因进行了分析。结果表明：电动自行车车架开裂为固定钢板与车架钢管之间存在焊接未熔合缺陷导致的焊缝开裂，主要原因是车架钢管表面存在严重锈蚀，焊接前未清除干净。
车架
焊缝
未熔合
开裂
electric bicycle
frame
weld seam
lack of fusion
cracking
Abstract
Some electric bicycles produced by a company cracked soon after they were used. The causes of cracking of frame were analyzed by macroscopic observation and metallographic examination. The results show that the cracking of electric bicycle frame was caused by the lack of fusion between the fixed steel plate and the frame steel pipe. The main reason was that the surface of frame steel pipe was seriously rusted and not cleaned before welding.
中图分类号 U484 DOI 10.11973/lhjy-wl202011013
所属栏目 质量控制与失效分析
基金项目
收稿日期 2020/6/8
修改稿日期
网络出版日期
作者单位点击查看
备注许加陆(1974-),男,高级工程师,主要从事优特钢技术质量管理工作,xujialu2008@163.com
引用该论文: XU Jialu,XU Xuanxuan. Cause of Cracking on Weld Seam of Electric Bicycle Frame[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2020, 56(11): 56～58
许加陆,徐旋旋. 电动自行车车架焊缝开裂原因[J]. 理化检验－物理分册, 2020, 56(11): 56～58
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】倪捷. 电动自行车产业20周年发展历程回顾与展望[J].电动自行车,2018(12):25-26.
【2】黄骥,项忠霞,邵一鑫,等.电动自行车结构强度影响因素分析[J].机械设计,2018,35(3):7-11.
【3】史东杰,贾世川,刘翰志,等.某车型车架焊接开裂问题分析[J].汽车工艺与材料,2016(1):34-36.
【4】章友谊,屈金山,杨跃.Domex700MC低合金高强钢药芯焊丝CO2气体保护焊焊接接头的组织与性能[J].机械工程材料,2008,32(11):61-63.
【2】黄骥,项忠霞,邵一鑫,等.电动自行车结构强度影响因素分析[J].机械设计,2018,35(3):7-11.
【3】史东杰,贾世川,刘翰志,等.某车型车架焊接开裂问题分析[J].汽车工艺与材料,2016(1):34-36.
【4】章友谊,屈金山,杨跃.Domex700MC低合金高强钢药芯焊丝CO2气体保护焊焊接接头的组织与性能[J].机械工程材料,2008,32(11):61-63.
相关信息