Effect of Solution Treatment on Properties of a New Building Weathering Steel
摘 要
在固溶温度(1 025~1 200℃)对新型建筑耐候钢进行了固溶处理,通过显微形貌观察、力学性能试验和电化学试验研究了固溶温度对其显微组织、力学性能和耐腐蚀性能的影响。结果表明,热轧态和固溶态耐候钢的显微组织都为铁素体和奥氏体,固溶温度为1 175℃时,耐候钢中铁素体和奥氏体含量接近1∶1;相对于热轧态耐候钢,固溶态耐候钢的强度和洛氏硬度偏低,但是断后伸长率、断面收缩率、冲击吸收能较高,固溶温度为1 175℃时,耐候钢具有较高的强度和硬度,且韧塑性和冲击吸收能都获得最大值;极化曲线和电化学阻抗谱测试结果显示,固溶温度为1 175℃时,耐候钢具有最好的耐蚀性能。
Abstract
A new building weathering steel was treated at solution treatment temperatures of 1 025-1 200 ℃. The effects of solution treatment temperature on the microstructure, mechanical properties and corrosion resistance of the new building weathering steel were studied by observation of micro morphology, mechamical property testing and electrochemical testing. The results show that ferrite and austenite were the microstructure for both hot-rolled weathering steel and solution-treated weathering steel. when the solution treatment temperature was 1 175 ℃, the ratio of ferrite content and austenite content in the weathering steel was close to 1∶1. The strength and Rockwell hardness of the solution-treated weathering steel were lower, but the percentage elongation after fracture, percentage reduction of area and impact absorbed energy were higher, comparing with the hot-rolled weathering steel. At solution treatment temperature of 1 175 ℃, the weathering steel had high strength and hardness, and got the maximum values in toughness, plasticity and impact absorbed energy. The polarization curves and electrochemical impedance spectroscopy results show that the weathering steel had the best corrosion resistance when the solution temperature was 1 175 ℃.
中图分类号 TG142.1 DOI 10.11973/fsyfh-202012003
所属栏目 试验研究
基金项目 国家自然科学青年基金项目(51571026);河北省自然科学基金项目(2017209218)
收稿日期 2019/4/16
修改稿日期
网络出版日期
作者单位点击查看
引用该论文: ZHANG Shuna,HE Yu,JIAO Lijun,LU Zhiwen,LIU Jun. Effect of Solution Treatment on Properties of a New Building Weathering Steel[J]. Corrosion & Protection, 2020, 41(12): 15
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】郝增宝. 电沉积镀层对建筑钢结构耐蚀性的影响[J]. 电镀与环保,2014,34(4):14-16.
【2】贾汝达. 热处理对高强建筑用钢组织和力学性能的影响[J]. 热加工工艺,2017,46(16):199-201.
【3】任非. 建筑用热轧耐候钢组织和性能研究[J]. 锻压技术,2016,41(1):142-145.
【4】陈健,陈玉鑫,黄涛,等. 不同铬含量耐候钢在高湿热模拟环境中的耐腐蚀性能[J]. 机械工程材料,2019,43(4):53-58.
【5】MURUGAN N,KANNAN T. Effects of flux cored arc welding parameters on pitting corrosion resistance of duplex stainless steel clad metals[J]. Corrosion Engineering,Science and Technology,2007,42(1):29-35.
【6】杨欢,邹德宁,那璇,等. 中温时效对超级双相不锈钢2507组织及性能的影响[J]. 材料保护,2018,51(10):31-34.
【7】侯冠宇,郭一二,项洪涛,等. 时效处理对S32750超级双相不锈钢在低温海水中腐蚀行为的影响[J]. 材料保护,2018,51(11):46-50.
【8】郑娟,葛文杰,束必清. 热处理工艺对微合金建筑用钢力学性能的影响[J]. 热加工工艺,2016,45(16):186-189.
【9】TANG S,LIU Z Y,WANG G D. Development of high strength plates with low yield ratio by the combination of TMCP and inter-critical quenching and tempering[J]. Steel Research International,2011,82(7):772-778.
【10】GERASIMOV V Y,GERASIMOVA O A. Influence of the mechanical properties of carbon steel on the hardening of rod blanks in upsetting[J]. Russian Engineering Research,2012,32(2):177-178.
【11】HUI W J,SHAO C W,ZHANG Y J,et al. Influence of vanadium on fracture splitting property of medium carbon steel[J]. Journal of Iron and Steel Research International,2016,23(5):475-483.
【12】张潇华,于思荣,谭哲,等. 304不锈钢在Al-6Si-10Cu储能合金液中的腐蚀行为[J]. 材料导报,2019,33(10):1681-1684.
【13】朱金阳,郑子易,许立宁,等. 高温高压环境下不同浓度KBr溶液对13Cr不锈钢的腐蚀行为影响[J]. 工程科学学报,2019,41(5):625-632.
【14】丰涵,宋志刚,吴晓涵,等. 022Cr25Ni7Mo4N双相不锈钢选择性腐蚀行为与两相组织的关系研究[J]. 中国腐蚀与防护学报,2019(2):138-144.
【15】HUI W J,CHEN S L,ZHANG Y J,et al. Effect of vanadium on the high-cycle fatigue fracture properties of medium-carbon microalloyed steel for fracture splitting connecting rod[J]. Materials & Design,2015,66:227-234.
【2】贾汝达. 热处理对高强建筑用钢组织和力学性能的影响[J]. 热加工工艺,2017,46(16):199-201.
【3】任非. 建筑用热轧耐候钢组织和性能研究[J]. 锻压技术,2016,41(1):142-145.
【4】陈健,陈玉鑫,黄涛,等. 不同铬含量耐候钢在高湿热模拟环境中的耐腐蚀性能[J]. 机械工程材料,2019,43(4):53-58.
【5】MURUGAN N,KANNAN T. Effects of flux cored arc welding parameters on pitting corrosion resistance of duplex stainless steel clad metals[J]. Corrosion Engineering,Science and Technology,2007,42(1):29-35.
【6】杨欢,邹德宁,那璇,等. 中温时效对超级双相不锈钢2507组织及性能的影响[J]. 材料保护,2018,51(10):31-34.
【7】侯冠宇,郭一二,项洪涛,等. 时效处理对S32750超级双相不锈钢在低温海水中腐蚀行为的影响[J]. 材料保护,2018,51(11):46-50.
【8】郑娟,葛文杰,束必清. 热处理工艺对微合金建筑用钢力学性能的影响[J]. 热加工工艺,2016,45(16):186-189.
【9】TANG S,LIU Z Y,WANG G D. Development of high strength plates with low yield ratio by the combination of TMCP and inter-critical quenching and tempering[J]. Steel Research International,2011,82(7):772-778.
【10】GERASIMOV V Y,GERASIMOVA O A. Influence of the mechanical properties of carbon steel on the hardening of rod blanks in upsetting[J]. Russian Engineering Research,2012,32(2):177-178.
【11】HUI W J,SHAO C W,ZHANG Y J,et al. Influence of vanadium on fracture splitting property of medium carbon steel[J]. Journal of Iron and Steel Research International,2016,23(5):475-483.
【12】张潇华,于思荣,谭哲,等. 304不锈钢在Al-6Si-10Cu储能合金液中的腐蚀行为[J]. 材料导报,2019,33(10):1681-1684.
【13】朱金阳,郑子易,许立宁,等. 高温高压环境下不同浓度KBr溶液对13Cr不锈钢的腐蚀行为影响[J]. 工程科学学报,2019,41(5):625-632.
【14】丰涵,宋志刚,吴晓涵,等. 022Cr25Ni7Mo4N双相不锈钢选择性腐蚀行为与两相组织的关系研究[J]. 中国腐蚀与防护学报,2019(2):138-144.
【15】HUI W J,CHEN S L,ZHANG Y J,et al. Effect of vanadium on the high-cycle fatigue fracture properties of medium-carbon microalloyed steel for fracture splitting connecting rod[J]. Materials & Design,2015,66:227-234.
相关信息