试验温度对金属材料焊接接头拉伸试验结果的影响
Influence of Test Temperature on Tensile Test Results of Metallic Material Welded Joints
摘 要
对比分析了国内外金属材料焊接接头拉伸试验标准中对试验温度的要求，在10，23，35℃条件下分别进行了Q355B钢焊接接头的横向拉伸试验。结果表明：在10~35℃进行试验时，温度对Q355B钢焊接接头抗拉强度的影响并不显著。对GB/T 2651—2008提出了修订建议。
焊接接头
标准
试验温度
拉伸试验
metallic material
welded joint
standard
test temperature
tensile test
Abstract
The test temperature requirements of the tensile test standards for metallic materical welded joints at home and abroad were compared and analyzed. Transverse tensile tests of Q355B steel welded joints were separately carried out at 10, 23 and 35 ℃. The results show that under the condition of 10-35 ℃, the influence on the temperature on the tensile strength of Q355B steel welded joints was not scgnificant. The revision suggestions of GB/T 2651—2008 were put forward.
中图分类号 TG115.5 DOI 10.11973/lhjy-wl202012010
所属栏目 标准化
基金项目
收稿日期 2020/9/11
修改稿日期
网络出版日期
作者单位点击查看
备注金静静(198-),女,工程师,主要从事焊缝试验与检验标准化工作,jinjingjing2014@163.com
引用该论文: JIN Jingjing. Influence of Test Temperature on Tensile Test Results of Metallic Material Welded Joints[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2020, 56(12): 39～42
金静静. 试验温度对金属材料焊接接头拉伸试验结果的影响[J]. 理化检验－物理分册, 2020, 56(12): 39～42
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】高怡斐, 李颖.金属材料室温拉伸试验国内外标准比较[C]//中国力学学会办公室.中国力学大会——2013论文摘要集.西安:西安交通大学,2013.
【2】吴伟.金属材料高温拉伸试验新旧国家标准对比分析[J].物理测试,2017,35(2):54-60.
【3】荣建,李晶,吕海青,等.金属材料拉伸试验影响因素及应对措施[J].冶金与材料,2019,39(5):46-48.
【4】焦少阳,张宏伟,王宝顺,等.试验温度对不同热处理状态核电站用P280GH钢弯头拉伸性能的影响[J].理化检验(物理分册),2020,56(3):1-7.
【5】姚宙,刘红艳,杜琦铭,等.工程机械刃具钢30CrMnB焊接接头的显微组织和力学性能[J].热加工工艺,2020,49(2):122-124.
【2】吴伟.金属材料高温拉伸试验新旧国家标准对比分析[J].物理测试,2017,35(2):54-60.
【3】荣建,李晶,吕海青,等.金属材料拉伸试验影响因素及应对措施[J].冶金与材料,2019,39(5):46-48.
【4】焦少阳,张宏伟,王宝顺,等.试验温度对不同热处理状态核电站用P280GH钢弯头拉伸性能的影响[J].理化检验(物理分册),2020,56(3):1-7.
【5】姚宙,刘红艳,杜琦铭,等.工程机械刃具钢30CrMnB焊接接头的显微组织和力学性能[J].热加工工艺,2020,49(2):122-124.
相关信息