异种钢Q235B/304L焊接过渡区疑似缺陷的无损检测
Nondestructive testing on suspected defects in welding transition zone ofdissimilar steel Q235B/304L
摘 要
使用超声检测和着色渗透检测，确诊了目视检查中发现的泵塔区异种钢（Q235B和304L）焊接过渡区焊缝表面疑似横向缺陷的性质；通过宏观剖伤分析结合着色渗透检测，进一步验证了横向缺陷的裂纹属性和分布特征；利用PMI（材料金属成份识别-光谱分析法）数据，初步分析了裂纹出现的原因。
疑似横向缺陷
材料金属成分识别
dissimilar steel butt welding transition zone
suspected lateral defect
PMI
Abstract
Ultrasonic testing and color penetrant testing were used to confirm the suspected lateral defects on the weld surface of the dissimilar steel Q235B and 304L in the pump tower area found in the visual inspection. The macroscopic fracture analysis combined with the color penetrant inspection has further verified the findings. The crack attributes and distribution characteristics of the transverse defects were analyzed; the cause of the crack initiation was preliminarily analyzed using PMI (material metal composition identification-spectral analysis method) data.
中图分类号 TG115.28 DOI 10.11973/wsjc202012005
所属栏目 试验研究
基金项目
收稿日期 2020/5/9
修改稿日期
网络出版日期
作者单位点击查看
备注陈志强(1970-),男,硕士,讲师,主要从事无损检测检验、焊接方面的科研及教学工作和国际新能源项目开发及合作
引用该论文: CHEN Zhiqiang,ZHANG Hongbo,CHEN Liu. Nondestructive testing on suspected defects in welding transition zone ofdissimilar steel Q235B/304L[J]. Nondestructive Testing, 2020, 42(12): 20～23
陈志强,张洪波,陈柳. 异种钢Q235B/304L焊接过渡区疑似缺陷的无损检测[J]. 无损检测, 2020, 42(12): 20～23
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】英若采. 熔焊原理及金属材料焊接(第2版)[M].北京:机械工业出版社,2000.
【2】美国金属学会. 金属手册(第十卷)[M].北京:机械工业出版社,1986.
【3】张其枢, 堵耀庭.不锈钢焊接[M].北京:机械工业出版社,2006.
【4】陈志强. 打底焊道裂纹的优化检测方法[J].无损检测,2012,34(10):51-54.
【2】美国金属学会. 金属手册(第十卷)[M].北京:机械工业出版社,1986.
【3】张其枢, 堵耀庭.不锈钢焊接[M].北京:机械工业出版社,2006.
【4】陈志强. 打底焊道裂纹的优化检测方法[J].无损检测,2012,34(10):51-54.
相关信息