Pitting Performance of 2205 Duplex Stainless Steel in Oil Field Production Fluid
摘 要
采用动电位和恒电位扫描方法研究了2205双相不锈钢在不同温度、不同极化电位和不同Cl-含量情况下的点蚀行为。结果表明:随着温度升高,2205双相不锈钢的点蚀击穿电位下降,钝化区间变窄;2205双相不锈钢在6% NaCl溶液中的临界点蚀温度约为56 ℃;当Cl-质量分数为6%~24%时,随Cl-含量增大,临界点蚀温度降低,但幅度较小,腐蚀电流增长幅度较大。温度和极化电位对2205双相不锈钢点蚀行为的影响较大,在所研究范围内,Cl-含量的影响较小。
Abstract
Pitting behavior of 2205 duplex stainless steel at different temperatures, different polarization potentials and different Cl- content was studied by potentiodynamic and constant potential scanning. The results showed that as the temperature increased, the pitting breakdown potential of 2205 duplex stainless steel decreased and the passivation interval narrowed.The critical pitting temperature of 2205 duplex stainless steel in 6% NaCl solution was about 56 ℃. When the mass fraction of Cl- was 6% - 24%, with the increase of Cl- content, the critical pitting temperature decreased, but the amplitude was relatively small, and the corrosion current increased greatly. Temperature and polarization potential had a great influence on the pitting behavior of 2205 duplex stainless steel. In the research range, the influence of Cl- content was small.
中图分类号 TG174 DOI 10.11973/fsyfh-202101005
所属栏目 试验研究
基金项目
收稿日期 2019/3/15
修改稿日期
网络出版日期
作者单位点击查看
引用该论文: ZHANG Yingying,ZHANG Yanjun,LI Lingjie,GUO Jiyin,ZHAO Yufei,ZHOU Bing. Pitting Performance of 2205 Duplex Stainless Steel in Oil Field Production Fluid[J]. Corrosion & Protection, 2021, 42(1): 22
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】吴玮巍,蒋益明,廖家兴,等. 0Cr25Ni7Mo4、316与304不锈钢临界点蚀温度研究[J]. 腐蚀科学与防护技术,2006,18(4):285-288.
【2】何进,晏敏胜,杨丽景,等. S32750双相不锈钢在NaCl溶液中的临界点蚀温度及电化学腐蚀机理[J]. 中国腐蚀与防护学报,2015,2(4):106-113.
【3】翁永基,李维锋,李相怡. 电化学噪声方法比较石油用钢的临界点蚀温度[J]. 中国腐蚀与防护学报,2009,29(6):421-425.
【4】宫少涛,李为卫,赵新伟,等. 2205双相不锈钢临界点蚀温度的测定[J]. 管道技术与设备,2006(3):37.
【5】张国超,林冠发,雷丹,等. 超级13Cr不锈钢的临界点蚀温度[J]. 腐蚀与防护,2012,33(9):777-779.
【6】吴玮巍,蒋益明,廖家兴,等. Cl离子对304、306不锈钢临界点蚀温度的影响[J]. 腐蚀科学与防护技术,2007,27(1):16-19.
【7】廖家兴,蒋益明,吴玮巍,等. 含Cl-溶液中SO42-对316L不锈钢临界点蚀温度的影响[J]. 金属学报,2006,42(11):1187-1190.
【2】何进,晏敏胜,杨丽景,等. S32750双相不锈钢在NaCl溶液中的临界点蚀温度及电化学腐蚀机理[J]. 中国腐蚀与防护学报,2015,2(4):106-113.
【3】翁永基,李维锋,李相怡. 电化学噪声方法比较石油用钢的临界点蚀温度[J]. 中国腐蚀与防护学报,2009,29(6):421-425.
【4】宫少涛,李为卫,赵新伟,等. 2205双相不锈钢临界点蚀温度的测定[J]. 管道技术与设备,2006(3):37.
【5】张国超,林冠发,雷丹,等. 超级13Cr不锈钢的临界点蚀温度[J]. 腐蚀与防护,2012,33(9):777-779.
【6】吴玮巍,蒋益明,廖家兴,等. Cl离子对304、306不锈钢临界点蚀温度的影响[J]. 腐蚀科学与防护技术,2007,27(1):16-19.
【7】廖家兴,蒋益明,吴玮巍,等. 含Cl-溶液中SO42-对316L不锈钢临界点蚀温度的影响[J]. 金属学报,2006,42(11):1187-1190.
相关信息