Effect of Slurry Impact Angle on Erosion Behavior of Cr30AHigh Chromium Cast Iron
摘 要
在模拟湿法脱硫浆液流动环境中,研究了NaCl溶液+石英砂酸性浆液冲击角度(与试样冲击表面夹角)对Cr30A高铬铸铁冲蚀行为的影响。结果表明:在浆液以60°和30°角度冲击铸铁后,在腐蚀与磨损的交互作用下铸铁的质量损失较大;浆液垂直冲击铸铁后,铸铁的质量损失较小,质量损失的主要原因是冲击磨损;浆液平行冲击铸铁后,铸铁的质量损失最小,质量损失的主要原因是点蚀。浆液平行冲击时铸铁的冲蚀机理以显微切削为主;浆液以30°角度冲击时的冲蚀机理以切削、犁削为主,铸铁表面存在挤出棱、冲击坑以及浅层片状疲劳剥落现象;浆液以60°角度冲击时的冲蚀机理以深层材料大块脱落和严重腐蚀磨损为主;浆液垂直冲击时的冲蚀机理主要是表层材料脱落,并伴随轻微腐蚀磨损。
Abstract
In simulated wet desulfurization slurry flow environment, the effect of impact angle of NaCl solution+quartz sand acid slurry with sample impact surface on the erosion behavior of Cr30A high chromium cast iron was studied. The results show that the mass loss of the cast iron was relatively large under the interaction of corrosion and abrasion after the slurry impacted the cast iron at angles of 60° and 30°. The mass loss of the cast iron was relatively small after the slurry impacted the cast iron vertically, and the main cause of the mass loss was impact abrasion. The mass loss of the cast iron was the smallest after the slurry impacted cast iron parallelly, and the main cause of the mass loss was pitting. When the cast iron was subjected to the paralled impact of the slurry, its erosion mechanism was mainly micro-cutting. When subjected to the 30° angle impact of the slurry, the erosion mechanism was mainly cutting and plowing, and extrusion edges, impact pits and shallow flaky fatigue peeling existed on the cast iron surface. When subjected to the 60° angle impact of the slurry, the erosion mechanism was mainly deep material layer peeling and severe corrosion abrasion. When subjected to the vertical impact of the slurry, the erosion mechanism was mainly the shedding of surface material, accompanied by slight corrosion abrasion.
中图分类号 TG143.7 DOI 10.11973/jxgccl202102004
所属栏目 试验研究
基金项目 湖南省教育厅科学研究项目重点项目(18A143)
收稿日期 2020/3/11
修改稿日期 2020/11/12
网络出版日期
作者单位点击查看
备注何建军(1974-),男,湖南南县人,教授,博士
引用该论文: HE Jianjun,ZHOU Chengwei,YU Renqiang,LI Wei,REN Yanjie,BAO Jiangyong. Effect of Slurry Impact Angle on Erosion Behavior of Cr30AHigh Chromium Cast Iron[J]. Materials for mechancial engineering, 2021, 45(2): 20~24
何建军,周承伟,余仁强,李微,任延杰,鲍江涌. 浆液冲击角度对Cr30A高铬铸铁冲蚀行为的影响[J]. 机械工程材料, 2021, 45(2): 20~24
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】赵汶, 陈武. 石灰石-石膏湿法脱硫过程中浆液液滴及细颗粒物迁移转化特性研究[J]. 动力工程学报, 2019, 39(3):242-247. ZHAO W,CHEN W.Study on migration and transformation characteristics of slurry droplets and fine particles in limestone gypsum wet desulfurization[J]. Journal of Chinese Society of Power Engineering,2019, 39, (3):242-247.
【2】VENCL A,BOBI AC'G I,BOBI AC'G B,et al.Erosive wear properties of ZA-27 alloy-based nanocomposites:Influence of type,amount,and size of nanoparticle reinforcements[J].Friction, 2019,7(4):340-350.
【3】王光存,李剑峰,贾秀杰,等.离心压缩机叶轮材料FV520B冲蚀规律和机理的研究[J].机械工程学报,2014,50(19):182-190. WANG G Y,LI J F,JIAN X J,et al.Study on the erosion law and mechanism of fv520b material for centrifugal compressor impeller[J]. Journal of Mechanical Engineering, 2014,50(19):182-190.
【4】金浩哲,易玉微,刘旭,等.液固两相流冲洗油管道的冲蚀磨损特性数值模拟及分析[J].摩擦学学报,2016,36(6):695-702. JIN H Z,YI Y W,LIU X,et al.Numerical simulation and analysis of erosion and wear characteristics of liquid-solid two-phase flow flushing oil pipeline[J]. Tribology, 2016,36(6):695-702.
【5】刘嘉宇, 刘亚明, 郝雅洁.湿法脱硫塔内脱硫浆液运动特性[J]. 中南大学学报(自然科学版), 2016, 47(1):330-337. LIU J Y,LIU Y M,HAO Y J.Kinetic characteristics of desulfurization slurry in wet desulfurization tower[J]. Journal of Central South University (Natural Science Edition), 2016, 47(1):330-337.
【6】闫钊,梁杰,贺博.FGD系统中浆液循环泵失效说明及改进[J].机械工程师,2016(8):222-224. LI Z,LIANG J,HE B.Failure description and improvement of slurry circulating pump in FGD system[J]. Mechanical Engineer, 2016, (8):222-224.
【7】GONG Y,YANG Z G.Corrosion evaluation of one wet desulfurization equipment-Flue gas desulfurization unit[J].Fuel Processing Technology, 2018,181:279-293.
【8】CHEN F J,YAO C,YANG Z G.Failure analysis on abnormal wall thinning of heat-transfer titanium tubes of condensers in nuclear power plant Part I:Corrosion and wear[J].Engineering Failure Analysis, 2014,37:29-41.
【9】ZHU Z W,ZHUO Y Q,FAN Y M,et al.Mechanism of mercury vapor release from flue gas desulfurization gypsum[J].Fuel Processing Technology, 2017,156:485-490.
【10】余仁强,何建军,李微.火电厂循环泵叶轮材料Cr30A在脱硫浆液腐蚀环境中的交互损伤失效行为研究[J].中国腐蚀与防护学报,2019,39(4):353-358. YU R Q,HE J J,LI W.Study on the interaction damage failure behavior of Cr30A in the corrosion environment of desulfurized slurry[J]. Journal of Chinese Society for Corrosion and Protection, 2019,39(04):353-358.
【11】STACK M M,ABD EL BADIA T M.On the construction of erosion-corrosion maps for WC/Co-Cr-based coatings in aqueous conditions[J].Wear, 2006,261(11/12):1181-1190.
【12】TIAN H H,ADDIE G R,VISINTAINER R J.Erosion-corrosion performance of high-Cr cast iron alloys in flowing liquid-solid slurries[J].Wear, 2009,267(11):2039-2047.
【13】CHUNG R J,TANG X,LI D Y,et al.Microstructure refinement of hypereutectic high Cr cast irons using hard carbide-forming elements for improved wear resistance[J].Wear, 2013,301(1/2):695-706.
【14】王阳阳,贾晨,杨建锋.高铬铸铁的冲蚀磨损性能研究[J].热加工工艺,2019,48(4):64-66. WANG Y Y,JIA C,YANG J F.Erosion Wear Performance of High-Cr White Casting Iron[J].Hot Working Technology,2019,48(4):64-66.
【15】李秀兰,谢文玲,郭翠霞.高铬铸铁在液-固两相流中的冲蚀磨损行为[J].特种铸造及有色合金,2016,36(10):1027-1030. LI X L,XIE W L,GUO C X.Erosion wear behavior of high chromium cast iron in fluid-solid two-phase flow[J].Special Casting & Nonferrous Alloys,2016,36(10):1027-1030.
【16】王莹,李萍,张洛平.超高铬铸铁的显微组织和腐蚀磨损性能[J].热加工工艺,2015,44(16):81-82. WANG Y,LI P,ZHANG L P.Microstructure and corrosion wear properties of ultrahigh chromium cast iron[J]. Hot Working Technology, 2015,44(16):81-82.
【2】VENCL A,BOBI AC'G I,BOBI AC'G B,et al.Erosive wear properties of ZA-27 alloy-based nanocomposites:Influence of type,amount,and size of nanoparticle reinforcements[J].Friction, 2019,7(4):340-350.
【3】王光存,李剑峰,贾秀杰,等.离心压缩机叶轮材料FV520B冲蚀规律和机理的研究[J].机械工程学报,2014,50(19):182-190. WANG G Y,LI J F,JIAN X J,et al.Study on the erosion law and mechanism of fv520b material for centrifugal compressor impeller[J]. Journal of Mechanical Engineering, 2014,50(19):182-190.
【4】金浩哲,易玉微,刘旭,等.液固两相流冲洗油管道的冲蚀磨损特性数值模拟及分析[J].摩擦学学报,2016,36(6):695-702. JIN H Z,YI Y W,LIU X,et al.Numerical simulation and analysis of erosion and wear characteristics of liquid-solid two-phase flow flushing oil pipeline[J]. Tribology, 2016,36(6):695-702.
【5】刘嘉宇, 刘亚明, 郝雅洁.湿法脱硫塔内脱硫浆液运动特性[J]. 中南大学学报(自然科学版), 2016, 47(1):330-337. LIU J Y,LIU Y M,HAO Y J.Kinetic characteristics of desulfurization slurry in wet desulfurization tower[J]. Journal of Central South University (Natural Science Edition), 2016, 47(1):330-337.
【6】闫钊,梁杰,贺博.FGD系统中浆液循环泵失效说明及改进[J].机械工程师,2016(8):222-224. LI Z,LIANG J,HE B.Failure description and improvement of slurry circulating pump in FGD system[J]. Mechanical Engineer, 2016, (8):222-224.
【7】GONG Y,YANG Z G.Corrosion evaluation of one wet desulfurization equipment-Flue gas desulfurization unit[J].Fuel Processing Technology, 2018,181:279-293.
【8】CHEN F J,YAO C,YANG Z G.Failure analysis on abnormal wall thinning of heat-transfer titanium tubes of condensers in nuclear power plant Part I:Corrosion and wear[J].Engineering Failure Analysis, 2014,37:29-41.
【9】ZHU Z W,ZHUO Y Q,FAN Y M,et al.Mechanism of mercury vapor release from flue gas desulfurization gypsum[J].Fuel Processing Technology, 2017,156:485-490.
【10】余仁强,何建军,李微.火电厂循环泵叶轮材料Cr30A在脱硫浆液腐蚀环境中的交互损伤失效行为研究[J].中国腐蚀与防护学报,2019,39(4):353-358. YU R Q,HE J J,LI W.Study on the interaction damage failure behavior of Cr30A in the corrosion environment of desulfurized slurry[J]. Journal of Chinese Society for Corrosion and Protection, 2019,39(04):353-358.
【11】STACK M M,ABD EL BADIA T M.On the construction of erosion-corrosion maps for WC/Co-Cr-based coatings in aqueous conditions[J].Wear, 2006,261(11/12):1181-1190.
【12】TIAN H H,ADDIE G R,VISINTAINER R J.Erosion-corrosion performance of high-Cr cast iron alloys in flowing liquid-solid slurries[J].Wear, 2009,267(11):2039-2047.
【13】CHUNG R J,TANG X,LI D Y,et al.Microstructure refinement of hypereutectic high Cr cast irons using hard carbide-forming elements for improved wear resistance[J].Wear, 2013,301(1/2):695-706.
【14】王阳阳,贾晨,杨建锋.高铬铸铁的冲蚀磨损性能研究[J].热加工工艺,2019,48(4):64-66. WANG Y Y,JIA C,YANG J F.Erosion Wear Performance of High-Cr White Casting Iron[J].Hot Working Technology,2019,48(4):64-66.
【15】李秀兰,谢文玲,郭翠霞.高铬铸铁在液-固两相流中的冲蚀磨损行为[J].特种铸造及有色合金,2016,36(10):1027-1030. LI X L,XIE W L,GUO C X.Erosion wear behavior of high chromium cast iron in fluid-solid two-phase flow[J].Special Casting & Nonferrous Alloys,2016,36(10):1027-1030.
【16】王莹,李萍,张洛平.超高铬铸铁的显微组织和腐蚀磨损性能[J].热加工工艺,2015,44(16):81-82. WANG Y,LI P,ZHANG L P.Microstructure and corrosion wear properties of ultrahigh chromium cast iron[J]. Hot Working Technology, 2015,44(16):81-82.
相关信息