氯离子对电站常用金属材料腐蚀行为的影响
Influence of Chlorine Ion on Corrosion Behavior of Metal Materials Used in Power Plants
摘 要
介绍了氯离子对电站常用碳钢、低合金钢和不锈钢在电站停用期间腐蚀行为（简称停用腐蚀）影响的研究进展，讨论了氯离子对碳钢、低合金钢和不锈钢的停用腐蚀作用机理和影响因素。结果表明：碳钢、低合金钢和不锈钢的停用腐蚀作用机理不同，碳钢和低合金钢停用腐蚀的主要诱因是凝结水和水中溶解氧存在，不锈钢停用腐蚀的发生主要归因于表面溶液介质中氯离子的浓缩。降低空气湿度、金属表面成膜和隔绝空气是抑制氯离子对金属材料造成停用腐蚀的较好方法。
碳钢
低合金钢
不锈钢
停用腐蚀
chloride ion
carbon steel
low alloy steel
stainless steel
shutdown corroson
Abstract
The research progress of the effect of chloride ion on the corrosion behavior of carbon steel, low-alloy steel and stainless steel commonly used in power stations during power station shutdown (abbreviated as shutdown corrosion) is introduced. The mechanism and influence factors of chloride ion on the shutdown corrosion of carbon steel, low alloy steel and stainless steel are discussed. The results show that the shutdown corrosion mechanisms of carbon steel, low alloy steel and stainless steel are different. The main cause of shutdown corrosion of carbon steel and low alloy steel is the presence of condensed water and dissolved oxygen in the water. The shutdown corrosion of stainless steel is mainly attributed to the concentration of chloride ion in the surface solution medium. Reducing air humidity, forming a film on the metal surface and isolating the air are good ways to inhibit the shutdown corrosion of metal materials induced by chloride ion.
中图分类号 TG174 DOI 10.11973/fsyfh-202104003
所属栏目 专论
基金项目 国家科技重大专项（2018ZX06906013）
收稿日期 2019/6/25
修改稿日期
网络出版日期
作者单位点击查看
引用该论文: ZHANG Guiquan,SUN Yaping,SU Yao,YAO Hongmeng,YAO Jiantao,LONG Guojun,GONG Bing. Influence of Chlorine Ion on Corrosion Behavior of Metal Materials Used in Power Plants[J]. Corrosion & Protection, 2021, 42(4): 14
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】李明辉,王剑,王建祥. 锅炉给水中氯离子危害浅析[J]. 装备制造技术,2012(9):240-241.
【2】李茂东,曾彬,杨麟,等. 含Cl-炉水对锅炉水冷壁管腐蚀行为的影响[J]. 材料保护,2013,46(11):61-64.
【3】袁曹龙,李新民,邓佳杰,等. 阴离子对600镍基合金腐蚀行为影响的研究[J]. 全面腐蚀控制,2011,25(6):45-48.
【4】林丁. 汽轮机叶片点蚀现象的分析[J]. 广东电力,2000,13(6):44-46.
【5】孙婷婷,陈映彤,陈映余. 水中氯离子对锅炉的危害及防护措施[J]. 科技风,2014(20):138.
【6】钱洲亥,曹求洋,宋小宁,等. 高参数机组炉水氯离子腐蚀性研究[J]. 浙江电力,2008,27(4):13-16.
【7】刘忠厚. 工业锅炉停炉保护[J]. 工业锅炉,2003(1):43-46.
【8】张瀚升. 火力发电机组停炉保护[J]. 中国新技术新产品,2016(18):76-77.
【9】朱巍,陈雪华. 停用锅炉防腐处理的研究[J]. 工业锅炉,2008(3):29-32.
【10】陈惠玲,李晓娟,魏雨. 碳钢在含氯离子环境中腐蚀机理的研究[J]. 腐蚀与防护,2007,28(1):17-19.
【11】石声泰,徐乃欣,张承典,等. 中性水中氯离子对碳钢和不锈钢腐蚀的影响[J]. 腐蚀与防护,1984,5(1):1-7.
【12】郭明晓,潘晨,王振尧,等. 碳钢在模拟海洋工业大气环境中初期腐蚀行为研究[J]. 金属学报,2018,54(1):65-75.
【13】张春亚,张奇,李继高,等. 碳钢及低合金钢在氯离子溶液中夹杂物诱发点蚀位置显微腐蚀实验探讨[J]. 冶金分析,2014,34(1):22-27.
【14】林昌健,谢兆雄. 不锈钢点腐蚀发生的早期过程:Ⅱ.电化学扫描隧道显微研究[J]. 腐蚀科学与防护技术,1997,9(4):259-264.
【15】张广文,胡杨,刘锋,等. 俄供机组低温再热器腐蚀分析[J]. 热力发电,2017,462(2):120-124.
【16】高新亮,付贵勤,朱苗勇,等. 低合金耐候钢在含氯离子环境中的腐蚀行为[J]. 北京科技大学学报,2012,34(11):1282-1287.
【17】潘旭东,王向明. 循环水中氯离子控制及对不锈钢腐蚀机理探讨[J]. 工业水处理,2013,33(3):14-16,20.
【18】邓博,蒋益明,郝允卫,等. F-和Cl-对316不锈钢临界点蚀温度的协同作用[J]. 中国腐蚀与防护学报,2008,28(1):30-33.
【19】吴玮巍,蒋益明,廖家兴,等. Cl离子对304、316不锈钢临界点蚀温度的影响[J]. 腐蚀科学与防护技术,2007,19(1):16-19.
【20】陈林海. 奥氏体不锈钢管道水压试验中氯离子腐蚀的原因分析[J]. 低碳世界,2017(24):25-26.
【21】巩春锋,张聚涛,李宏磊,等. 某核电项目换热器的换热管腐蚀原因分析[J]. 设备监理,2018(6):52-55.
【22】史艳华,于洋,梁平,等. 316L不锈钢在氯离子环境中的腐蚀行为[J]. 材料保护,2015,48(8):29-32.
【23】吕国诚,许淳淳,程海东. 304不锈钢应力腐蚀的临界氯离子浓度[J]. 化工进展,2008,27(8):1284-1287.
【24】廖家兴,蒋益明,吴玮巍,等. 含Cl-溶液中SO42-对316不锈钢临界点蚀温度的影响[J]. 金属学报,2006,42(11):1187-1190.
【25】汪轩义,吴荫顺,张琳. 316L不锈钢钝化膜在Cl-介质中的耐蚀机制[J]. 腐蚀科学与防护技术,2000,12(6):311.
【26】李岩,方可伟,刘飞华. Cl-对304L不锈钢从点蚀到应力腐蚀转变行为的影响[J]. 腐蚀与防护,2012,33(11):955-959.
【27】张贵泉,宁军,贺旺民,等. 电站锅炉复合有机胺停用保护剂机理研究及工程应用[J]. 热力发电,2018,47(2):131-137.
【28】张广文,刘锋,李佳,等. 俄供机组低温再热器管停用腐蚀及保养[J]. 热力发电,2017,46(11):85-90.
【29】李志成,张竞杰,靳江波,等. 真空干燥法停炉保护过程控制与效果评价[J]. 华北电力技术,2015(8):42-45.
【30】张玉福. 热力设备停(备)用期间成膜胺防腐的应用技术[J]. 中国电力,2001,34(6):28-30,80.
【31】VIKNESHVARAN S,VELMATHI S. Adsorption of L-Tryptophan-derived chiral bases on stainless steel surface for the prevention of corrosion in acidic environment: Experimental,theoretical and surface studies[J]. Surface and Interfaces,2017,6:134-142.
【2】李茂东,曾彬,杨麟,等. 含Cl-炉水对锅炉水冷壁管腐蚀行为的影响[J]. 材料保护,2013,46(11):61-64.
【3】袁曹龙,李新民,邓佳杰,等. 阴离子对600镍基合金腐蚀行为影响的研究[J]. 全面腐蚀控制,2011,25(6):45-48.
【4】林丁. 汽轮机叶片点蚀现象的分析[J]. 广东电力,2000,13(6):44-46.
【5】孙婷婷,陈映彤,陈映余. 水中氯离子对锅炉的危害及防护措施[J]. 科技风,2014(20):138.
【6】钱洲亥,曹求洋,宋小宁,等. 高参数机组炉水氯离子腐蚀性研究[J]. 浙江电力,2008,27(4):13-16.
【7】刘忠厚. 工业锅炉停炉保护[J]. 工业锅炉,2003(1):43-46.
【8】张瀚升. 火力发电机组停炉保护[J]. 中国新技术新产品,2016(18):76-77.
【9】朱巍,陈雪华. 停用锅炉防腐处理的研究[J]. 工业锅炉,2008(3):29-32.
【10】陈惠玲,李晓娟,魏雨. 碳钢在含氯离子环境中腐蚀机理的研究[J]. 腐蚀与防护,2007,28(1):17-19.
【11】石声泰,徐乃欣,张承典,等. 中性水中氯离子对碳钢和不锈钢腐蚀的影响[J]. 腐蚀与防护,1984,5(1):1-7.
【12】郭明晓,潘晨,王振尧,等. 碳钢在模拟海洋工业大气环境中初期腐蚀行为研究[J]. 金属学报,2018,54(1):65-75.
【13】张春亚,张奇,李继高,等. 碳钢及低合金钢在氯离子溶液中夹杂物诱发点蚀位置显微腐蚀实验探讨[J]. 冶金分析,2014,34(1):22-27.
【14】林昌健,谢兆雄. 不锈钢点腐蚀发生的早期过程:Ⅱ.电化学扫描隧道显微研究[J]. 腐蚀科学与防护技术,1997,9(4):259-264.
【15】张广文,胡杨,刘锋,等. 俄供机组低温再热器腐蚀分析[J]. 热力发电,2017,462(2):120-124.
【16】高新亮,付贵勤,朱苗勇,等. 低合金耐候钢在含氯离子环境中的腐蚀行为[J]. 北京科技大学学报,2012,34(11):1282-1287.
【17】潘旭东,王向明. 循环水中氯离子控制及对不锈钢腐蚀机理探讨[J]. 工业水处理,2013,33(3):14-16,20.
【18】邓博,蒋益明,郝允卫,等. F-和Cl-对316不锈钢临界点蚀温度的协同作用[J]. 中国腐蚀与防护学报,2008,28(1):30-33.
【19】吴玮巍,蒋益明,廖家兴,等. Cl离子对304、316不锈钢临界点蚀温度的影响[J]. 腐蚀科学与防护技术,2007,19(1):16-19.
【20】陈林海. 奥氏体不锈钢管道水压试验中氯离子腐蚀的原因分析[J]. 低碳世界,2017(24):25-26.
【21】巩春锋,张聚涛,李宏磊,等. 某核电项目换热器的换热管腐蚀原因分析[J]. 设备监理,2018(6):52-55.
【22】史艳华,于洋,梁平,等. 316L不锈钢在氯离子环境中的腐蚀行为[J]. 材料保护,2015,48(8):29-32.
【23】吕国诚,许淳淳,程海东. 304不锈钢应力腐蚀的临界氯离子浓度[J]. 化工进展,2008,27(8):1284-1287.
【24】廖家兴,蒋益明,吴玮巍,等. 含Cl-溶液中SO42-对316不锈钢临界点蚀温度的影响[J]. 金属学报,2006,42(11):1187-1190.
【25】汪轩义,吴荫顺,张琳. 316L不锈钢钝化膜在Cl-介质中的耐蚀机制[J]. 腐蚀科学与防护技术,2000,12(6):311.
【26】李岩,方可伟,刘飞华. Cl-对304L不锈钢从点蚀到应力腐蚀转变行为的影响[J]. 腐蚀与防护,2012,33(11):955-959.
【27】张贵泉,宁军,贺旺民,等. 电站锅炉复合有机胺停用保护剂机理研究及工程应用[J]. 热力发电,2018,47(2):131-137.
【28】张广文,刘锋,李佳,等. 俄供机组低温再热器管停用腐蚀及保养[J]. 热力发电,2017,46(11):85-90.
【29】李志成,张竞杰,靳江波,等. 真空干燥法停炉保护过程控制与效果评价[J]. 华北电力技术,2015(8):42-45.
【30】张玉福. 热力设备停(备)用期间成膜胺防腐的应用技术[J]. 中国电力,2001,34(6):28-30,80.
【31】VIKNESHVARAN S,VELMATHI S. Adsorption of L-Tryptophan-derived chiral bases on stainless steel surface for the prevention of corrosion in acidic environment: Experimental,theoretical and surface studies[J]. Surface and Interfaces,2017,6:134-142.
相关信息