高频变压器引脚的腐蚀原因
Corrosion Failure Analysis of Pins of High Frequency Transformer
摘 要
通过现场腐蚀产物的能谱分析，0.2%（质量分数） H2SO4酸雾和5%（质量分数） NaCl盐雾试验对售后高频变压器的腐蚀失效原因进行了研究。结果表明：高频变压器的腐蚀引脚上存在明显的S元素，在潮湿、酸性及盐雾环境中引脚腐蚀较为严重；引脚镀层破损时，内部铁基体腐蚀明显，漆包线与焊锡交界处也极易诱发腐蚀；采用磷青铜为引脚材料、对外露漆包线部分涂覆清漆作保护层可以有效提高引脚的耐腐蚀性能。
引脚
腐蚀
耐腐蚀性能
high frequency transformer
pin
corrosion
corrosion resistance
Abstract
The reasons for corrosion failure of after-sale high frequency transformers were studied through energy spectrum analysis of corrosion products in field, 0.2% (mass fraction) H2SO4 acid spraying test and 5% (mass fraction) NaCl salt spraying test. The results show that there was obvious sulfur element in corroded pins of high frequency transformers, and the corrosion of pins was more serious in wet, acid and salt spray environments. The iron substrate of pins with damaged coating corroded seriously, and corrosion was induced easily on the border of enamelled wire and solder. Using phosphor bronze as pin material and coating exposed enamelled wires with varnish water as protection layer could improve the corrosion resistance of pins effectively.
中图分类号 TG174 DOI 10.11973/fsyfh-202105016
所属栏目 失效分析
基金项目
收稿日期 2019/7/8
修改稿日期
网络出版日期
作者单位点击查看
引用该论文: OU Yuying,LU Zhenghua. Corrosion Failure Analysis of Pins of High Frequency Transformer[J]. Corrosion & Protection, 2021, 42(5): 78
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】郗亮. 高频变压器发展的研究[J]. 通信电源技术,2018,35(3):237-238.
【2】周松,许良,回丽,等. 不同腐蚀环境下高强铝合金腐蚀行为[J]. 中国机械工程,2017,28(16):2000-2007.
【3】王秀通,王丽媛,孙好芬,等. SO2与NaCl对铜大气腐蚀的影响[J]. 材料保护,2011,44(9):28-31.
【4】马海涛. 高温氯盐环境中金属材料的腐蚀[D]. 大连:大连理工大学,2003.
【5】李金灵,朱世东,屈撑囤,等. 元素硫腐蚀研究进展[J]. 热加工工艺,2015,44(2):20-24.
【6】侯娟,俞国军,孙华,等. 熔盐堆中结构材料的腐蚀研究[J]. 核科学与工程,2018,38(2):171-185.
【7】张婧,李海新,殷子强,等. 焊接接头的腐蚀研究进展[J]. 腐蚀科学与防护技术,2018,30(6):661-670.
【8】WANG S Q,ZHANG D K,WANG D G,et al. Electrochemical corrosion behavior of steel wires in a coalmine with a corrosive medium[J]. Mining Science and Technology (China),2011,21(1):71-76.
【9】ZHANG X G,WANG J,ZHOU Y W. Analytical modeling for corrosion-induced cover cracking of corrosive reinforced concrete structures[J]. Transactions of Tianjin University,2012,18(4):285-290.
【10】郑铭天. 超薄铜箔材料的腐蚀行为研究[D]. 北京:北京化工大学,2010.
【11】赵慧萍,赵文娟,张晓芳. 金属电化学腐蚀与防腐浅析[J]. 化学工程与装备,2013(10):135-136.
【12】MUNTERER F,PRAUTZSCH G,STIER T. 防止电化学腐蚀的有效方法新型预防失效的电中性材料[J]. 汽车与配件,2018(11):60-62.
【2】周松,许良,回丽,等. 不同腐蚀环境下高强铝合金腐蚀行为[J]. 中国机械工程,2017,28(16):2000-2007.
【3】王秀通,王丽媛,孙好芬,等. SO2与NaCl对铜大气腐蚀的影响[J]. 材料保护,2011,44(9):28-31.
【4】马海涛. 高温氯盐环境中金属材料的腐蚀[D]. 大连:大连理工大学,2003.
【5】李金灵,朱世东,屈撑囤,等. 元素硫腐蚀研究进展[J]. 热加工工艺,2015,44(2):20-24.
【6】侯娟,俞国军,孙华,等. 熔盐堆中结构材料的腐蚀研究[J]. 核科学与工程,2018,38(2):171-185.
【7】张婧,李海新,殷子强,等. 焊接接头的腐蚀研究进展[J]. 腐蚀科学与防护技术,2018,30(6):661-670.
【8】WANG S Q,ZHANG D K,WANG D G,et al. Electrochemical corrosion behavior of steel wires in a coalmine with a corrosive medium[J]. Mining Science and Technology (China),2011,21(1):71-76.
【9】ZHANG X G,WANG J,ZHOU Y W. Analytical modeling for corrosion-induced cover cracking of corrosive reinforced concrete structures[J]. Transactions of Tianjin University,2012,18(4):285-290.
【10】郑铭天. 超薄铜箔材料的腐蚀行为研究[D]. 北京:北京化工大学,2010.
【11】赵慧萍,赵文娟,张晓芳. 金属电化学腐蚀与防腐浅析[J]. 化学工程与装备,2013(10):135-136.
【12】MUNTERER F,PRAUTZSCH G,STIER T. 防止电化学腐蚀的有效方法新型预防失效的电中性材料[J]. 汽车与配件,2018(11):60-62.
相关信息