高参数发电机组腐蚀的原因及其防范措施
Corrosion Causes of a High Parameter Generator Unit and Preventive Measures
摘 要
在某600MW发电机组大修过程中，发现汽轮机低压缸的叶片和隔板发生了腐蚀。从腐蚀形貌，腐蚀产物成分和工作情况等不同方面进行了分析，发现该汽轮机产生腐蚀的原因为氯离子腐蚀，并提出了相应的防范措施。
氯离子
腐蚀
防范措施
low-pressure cylinder
chloride ion
corrosion
preventive measure
Abstract
During the overhaul of a 600MW generator unit, corrosion was found in the blades and baffles of a low-pressure cylinder of steam turbine. It was found that the corrosion of the steam turbine was caused by chloride ion corrosion through analyzing the corrosion morphology, corrosion product composition and working conditions. And some corresponding measures were proposed to prevent the corrosion.
中图分类号 V261.4+2 DOI 10.11973/fsyfh-202105017
所属栏目 失效分析
基金项目
收稿日期 2019/7/8
修改稿日期
网络出版日期
作者单位点击查看
引用该论文: XU Wenqiang. Corrosion Causes of a High Parameter Generator Unit and Preventive Measures[J]. Corrosion & Protection, 2021, 42(5): 82
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】黄丽萍. 炉水中氯离子浓度高的原因分析与预防措施[J]. 宁夏电力,2010(6):60-64.
【2】周景云. 汽轮机低压末级叶片腐蚀原因分析及其表面防护处理[J]. 中国新技术新产品,2009(13):112.
【3】雷勤,钱军. 汽轮机末两级叶片水蚀的原因浅析及防范措施[J]. 泸天化科技,2008(4):352-356.
【2】周景云. 汽轮机低压末级叶片腐蚀原因分析及其表面防护处理[J]. 中国新技术新产品,2009(13):112.
【3】雷勤,钱军. 汽轮机末两级叶片水蚀的原因浅析及防范措施[J]. 泸天化科技,2008(4):352-356.
相关信息