镀锡板点状缺陷产生原因
Spot Defects Causes of Tinplate
摘 要
某镀锡板表面出现点状缺陷，采用宏观分析、微观分析、盐雾加速腐蚀分析、孔隙率分析等方法，对镀锡板表面点状缺陷产生的原因进行了分析。结果表明：淬水槽中的锡污泥、空气尘埃及助熔剂中有机物的残留附着于镀锡板带钢表面，在过度沸腾的作用下嵌入镀层，吸收水分发生氧化后，最终生成镀锡板表面的点状缺陷。
点状缺陷
盐雾加速腐蚀
孔隙率
tinplate
spot defect
salt spray accelerated corrosion
porosity
Abstract
Spot defects appeared on the surface of a tinplate. The causes of spot defects were analyzed by macro analysis, micro analysis, salt spray accelerated corrosion analysis and porosity analysis. The results show that the tin sludge, air dust and organic matter residues in additive in flux in quenching tank adhered to the surface of the tinplate. The above substances were embedded in the coating under the effect of transitional boiling, absorbed water and oxidized, resulted in the formation of the spot defects on the surface of tinplate.
中图分类号 TG115 DOI 10.11973/lhjy-wl202106018
所属栏目 质量控制与失效分析
基金项目
收稿日期 2021/1/5
修改稿日期
网络出版日期
作者单位点击查看
备注薄炜(1980-),男,工程师,主要从事金属材料电镀方面的工作,bowei@baosteel.com
引用该论文: BO Wei. Spot Defects Causes of Tinplate[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2021, 57(6): 78～81
薄炜. 镀锡板点状缺陷产生原因[J]. 理化检验－物理分册, 2021, 57(6): 78～81
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】刘爱平. 高端镀锡基板表面质量的控制研究[J].河北冶金,2018(7):66-68.
【2】王熙禹,黎德育,李宁,等.软熔参数和基板对镀锡板锡铁合金层性能的影响[J].电镀与涂饰,2019,38(24):1349-1356.
【3】王莉莉,黄久贵,李建中.镀锡产品的市场环境及发展趋势[J].有色矿冶,2012,28(3):102-106.
【4】张清东,张勃洋,李瑞,等.镀锡钢板表面光泽度轧制转印控制[J].机械工程学报,2016,52(14):48-57.
【2】王熙禹,黎德育,李宁,等.软熔参数和基板对镀锡板锡铁合金层性能的影响[J].电镀与涂饰,2019,38(24):1349-1356.
【3】王莉莉,黄久贵,李建中.镀锡产品的市场环境及发展趋势[J].有色矿冶,2012,28(3):102-106.
【4】张清东,张勃洋,李瑞,等.镀锡钢板表面光泽度轧制转印控制[J].机械工程学报,2016,52(14):48-57.
相关信息