S13Cr110马氏体不锈钢油管在高温高压Weigh4完井液中的应力腐蚀开裂性能
Stress Corrosion Cracking Performance of S13Cr110 Martensitic Stainless Steel Tubing in High Temperature and High Pressure Weigh4 Completion Fluid
摘 要
采用C环试验，研究了S13Cr110马氏体不锈钢油管在高温高压Weigh4完井液中的应力腐蚀开裂（SCC）性能。结果表明：S13Cr110油管在高pH的Weigh4完井液中存在一定的SCC风险，少量泥浆的存在会增强S13Cr110油管的应力腐蚀敏感性。在含O2且混有少量泥浆的Weigh4完井液中，S13CR110油管会发生应力腐蚀开裂。
Weigh4完井液
应力腐蚀开裂
S13Cr110油管
C环试验
high temperature and high pressure well
Weigh4 completion fluid
stress corrosion cracking
S13Cr110 tubing
C-ring test
Abstract
C-ring test was used to study the stress corrosion cracking (SCC) performance of S13Cr110 martensitic stainless steel tubing in high temperature and high pressure Weigh4 completion fluids. The results showed that S13Cr110 tubing had a certain risk of SCC in the high pH Weigh4 completion fluid, and the presence of a small amount of mud would enhance stress corrosion sensitivity of S13Cr110 tubing. In the Weigh4 completion fluid containing O2 and a small amount of mud, S13CR110 tubing suffered stress corrosion cracking.
中图分类号 TE983 DOI 10.11973/fsyfh-202109007
所属栏目 试验研究
基金项目 国家自然科学基金（51707158）；陕西省重点研发项目（2019KW-045）
收稿日期 2020/2/10
修改稿日期
网络出版日期
作者单位点击查看
引用该论文: XUE Jijun. Stress Corrosion Cracking Performance of S13Cr110 Martensitic Stainless Steel Tubing in High Temperature and High Pressure Weigh4 Completion Fluid[J]. Corrosion & Protection, 2021, 42(9): 35
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】李晓岚,李玲,赵永刚,等. 套管环空保护液的研究与应用[J]. 钻井液与完井液,2010,27(6):61-64,100.
【2】李慧,奚运涛,李琼玮,等. 储气库耐蚀合金管材的环空保护液研制及应用[J]. 天然气与石油,2017,35(2):91-95.
【3】赵密锋,付安庆,秦宏德,等. 高温高压气井管柱腐蚀现状及未来研究展望[J]. 表面技术,2018,47(6):44-50.
【4】杨向同,沈新普,王克林,等. 完井作业油管柱失效的力学机理——以塔里木盆地某高温高压井为例[J]. 天然气工业,2018,38(7):86-92.
【5】谢俊峰,薛艳,李岩,等. S13Cr110油管表面抗应力腐蚀开裂性能研究[J]. 石油工业技术监督,2019,35(8):49-52.
【6】申泽骥,姜炳焕,苏贵桥,等. 奥氏体铸体和18-8不锈钢在烧碱中的腐蚀行为[J]. 材料科学与工艺,1999,7(3):10-13.
【7】杨向同,吕祥鸿,谢俊峰,等. 高强15Cr马氏体不锈钢在有机盐完井液中的腐蚀行为[J]. 腐蚀与防护,2018,39(12):901-905,911.
【2】李慧,奚运涛,李琼玮,等. 储气库耐蚀合金管材的环空保护液研制及应用[J]. 天然气与石油,2017,35(2):91-95.
【3】赵密锋,付安庆,秦宏德,等. 高温高压气井管柱腐蚀现状及未来研究展望[J]. 表面技术,2018,47(6):44-50.
【4】杨向同,沈新普,王克林,等. 完井作业油管柱失效的力学机理——以塔里木盆地某高温高压井为例[J]. 天然气工业,2018,38(7):86-92.
【5】谢俊峰,薛艳,李岩,等. S13Cr110油管表面抗应力腐蚀开裂性能研究[J]. 石油工业技术监督,2019,35(8):49-52.
【6】申泽骥,姜炳焕,苏贵桥,等. 奥氏体铸体和18-8不锈钢在烧碱中的腐蚀行为[J]. 材料科学与工艺,1999,7(3):10-13.
【7】杨向同,吕祥鸿,谢俊峰,等. 高强15Cr马氏体不锈钢在有机盐完井液中的腐蚀行为[J]. 腐蚀与防护,2018,39(12):901-905,911.
相关信息