Corrosion Resistance of 22MnB5 Hot-Stamped and Quenched Parts
摘 要
根据汽车用22MnB5零件的制造工艺,对无涂层板、Al-Si涂层板、热镀锌板进行热冲压淬火处理及无涂层板热冲压淬火后电镀锌处理。利用光学显微镜观察了热冲压淬火前后零件涂层的形貌变化。通过中性盐雾试验研究了不同工艺处理零件的耐腐蚀性能。结果表明:对热压冲淬火后零件进行电镀锌处理,得到的涂层致密均匀没有破损,且具有极好的阴极保护效果,该零件的耐腐蚀性能远优于Al-Si涂层板、热镀锌板和无涂层板的;热压冲淬火后电镀锌处理可以提高汽车零件的耐腐蚀性能。
Abstract
According to the manufacturing process of 22MnB5 parts for automobiles, uncoated steel sheet, Al-Si coated steel sheet and hot galvanized steel sheet were treated by hot-stamping and quenching, and the uncoated steel sheet was galvanized after hot-stamping and quenching. The changes in the morphology of the part coating before and after hot-stamping and quenching were observed by optical microscope. The corrosion resistance of parts treated by different processes was studied by neutral salt-spray test. The coating obtained by galvanization after hot-stamping and quenching on a part was dense and uniform without damage, and had excellent cathodic protection effect. The corrosion resistance of the part was far superior to that of Al-Si coated steel sheet, hot galvanized steel sheet and uncoated plate. Galvanization after hot-stamping and quenching can improve the corrosion resistance of automobile parts.
中图分类号 TG DOI 10.11973/fsyfh-202111009
所属栏目 试验研究
基金项目
收稿日期 2019/2/20
修改稿日期
网络出版日期
作者单位点击查看
引用该论文: CHEN Hanjie,AN Jian,LI Dongcheng. Corrosion Resistance of 22MnB5 Hot-Stamped and Quenched Parts[J]. Corrosion & Protection, 2021, 42(11): 61
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】MORI K, ITO D. Prevention of oxidation in hot stamping of quenchable steel sheet by oxidation preventive oil[J]. CIRP Annals, 2009, 58(1):267-270.
【2】KONDRATIUK J, KUHN P, KOYER M, et al. A ner coating solution for hot press forming[C]//8th International Conference on Zinc and Zinc Alloy Coated Steel Sheet.[S.l.]:[s.n.], 2011:182.
【3】FADERL J, KOLNBERGER S, ROSNER M, et al. Continuou galvanizing meets press-harding[C]//8th International Conference on Zinc and Zinc Alloy Coated Steel Sheet.[S.l.]:[s.n.], 2011:161.
【4】FAN D W, KIM H S, OH J K, et al. Coating degradation in hot press forming[J]. ISIJ International, 2010, 50(4):561-568.
【5】李兵, 张春, 王敏, 等. 汽车底板纵梁用带Al-Si涂层硼钢板的热冲压[J]. 金属热处理, 2017, 42(6):39-42.
【6】GUI Z X, LIANG W K, ZHANG Y S. Formability of aluminum-silicon coated boron steel in hot stamping process[J]. Transactions of Nonferrous Metals Society of China, 2014, 24(6):1750-1757.
【7】MAKI J, KUROSAKI M, KUSUMI K, et al. Effect of heating condition and hot forming on corrosion resistance of hot stamped aluminized steels[C]//Proceedings of 3rd International Conference on Hot Sheet Metal Forming of High-Performance Steel.[S.l.]:[s.n.], 2011:499-507.
【8】SEINHOFF K, BARBAKEDZE N, SCHUPFER M. Press harding-from galvanized UHSS to body-in-white application[C]//8th International Conference on Zinc and Zinc Alloy Coated Steel Sheet.[S.l.]:[s.n.], 2011:12-15.
【9】CHO L, KANG H, LEE C, et al. Microstructure of liquid metal embrittlement cracks on Zn-coated 22MnB5 press-hardened steel[J]. Scripta Materialia, 2014, 90/91:25-28.
【10】张杰. 超高强度热成形钢镀层组织和性能研究[D]. 沈阳:东北大学, 2014:114-115.
【11】AKIOKA K, NISHIBATA T, IMAI K, et al. Layer structure and properties of galvannealed steel sheet after hot stamping[C]//8th International Conference on Zinc and Zinc Alloy Coated Steel Sheet.[S.l.]:[s.n.], 2011:363-369.
【12】FLEISCHANDERL M, KOLNBERGER S, FADERL J, et al. Method for producing a hardened steel part:US20070256808[P]. 2019-02-20.
【13】邱肖盼, 张杰, 江社明, 等. 冲压温度对镀锌22MnB5钢板镀层中裂纹的影响[J]. 腐蚀与防护, 2018, 39(4):302-306.
【2】KONDRATIUK J, KUHN P, KOYER M, et al. A ner coating solution for hot press forming[C]//8th International Conference on Zinc and Zinc Alloy Coated Steel Sheet.[S.l.]:[s.n.], 2011:182.
【3】FADERL J, KOLNBERGER S, ROSNER M, et al. Continuou galvanizing meets press-harding[C]//8th International Conference on Zinc and Zinc Alloy Coated Steel Sheet.[S.l.]:[s.n.], 2011:161.
【4】FAN D W, KIM H S, OH J K, et al. Coating degradation in hot press forming[J]. ISIJ International, 2010, 50(4):561-568.
【5】李兵, 张春, 王敏, 等. 汽车底板纵梁用带Al-Si涂层硼钢板的热冲压[J]. 金属热处理, 2017, 42(6):39-42.
【6】GUI Z X, LIANG W K, ZHANG Y S. Formability of aluminum-silicon coated boron steel in hot stamping process[J]. Transactions of Nonferrous Metals Society of China, 2014, 24(6):1750-1757.
【7】MAKI J, KUROSAKI M, KUSUMI K, et al. Effect of heating condition and hot forming on corrosion resistance of hot stamped aluminized steels[C]//Proceedings of 3rd International Conference on Hot Sheet Metal Forming of High-Performance Steel.[S.l.]:[s.n.], 2011:499-507.
【8】SEINHOFF K, BARBAKEDZE N, SCHUPFER M. Press harding-from galvanized UHSS to body-in-white application[C]//8th International Conference on Zinc and Zinc Alloy Coated Steel Sheet.[S.l.]:[s.n.], 2011:12-15.
【9】CHO L, KANG H, LEE C, et al. Microstructure of liquid metal embrittlement cracks on Zn-coated 22MnB5 press-hardened steel[J]. Scripta Materialia, 2014, 90/91:25-28.
【10】张杰. 超高强度热成形钢镀层组织和性能研究[D]. 沈阳:东北大学, 2014:114-115.
【11】AKIOKA K, NISHIBATA T, IMAI K, et al. Layer structure and properties of galvannealed steel sheet after hot stamping[C]//8th International Conference on Zinc and Zinc Alloy Coated Steel Sheet.[S.l.]:[s.n.], 2011:363-369.
【12】FLEISCHANDERL M, KOLNBERGER S, FADERL J, et al. Method for producing a hardened steel part:US20070256808[P]. 2019-02-20.
【13】邱肖盼, 张杰, 江社明, 等. 冲压温度对镀锌22MnB5钢板镀层中裂纹的影响[J]. 腐蚀与防护, 2018, 39(4):302-306.
相关信息