Microstructure and Abrasive Wear Properties ofHot Rolled Ultra-High Strength Steel M1200HS
摘 要
采用热轧和在线直接淬火工艺制备热轧超高强钢M1200HS,研究了其显微组织、力学性能及在石英砂与水的混合物中的磨粒磨损性能,并与传统低合金耐磨钢NM400和NM450作对比。结果表明:M1200HS钢的显微组织为马氏体和极少量铁素体,其马氏体板条尺寸较大,大角度晶界占比较小;M1200HS钢的抗拉强度和硬度分别为1 387 MPa和403 HB,均符合GB/T 24186-2009标准,且与NM400钢近乎相当,但低于NM450钢;3种试验钢的磨损机制均为微观切削机制,M1200HS钢与NM400钢的耐磨粒磨损性能相当,但低于NM450钢。
Abstract
A hot rolled ultra-high strength steel M1200HS was produced by hot rolling and online direct quenching processes. The microstructure, mechanical properties, and abrasive wear behavior in a mixture of quatz sand and water of M1200HS steel were studied and compared with those of traditional low alloy wear-resisting steels NM400 and NM450. The results show that the microstructure of M1200HS steel was martensite and very little ferrite, the size of martensite lath was large and the proportion of large angle grain boundary was small. The tensile strength and hardness of M1200HS steel were 1 387 MPa and 403 HB, respectively, which were conform to GB/T 24186-2009 standard, and almost equal to those of NM400 steel, but lower than those of NM450 steel. The wear mechanism of the three kinds of test steel was micro cutting. The abrasive wear resistance of M1200HS steel was similar to that of NM400 steel, but lower than that of NM450 steel.
中图分类号 TG142.1 DOI 10.11973/jxgccl202201011
所属栏目 新材料 新工艺
基金项目 安徽省科技重大专项资助项目(18030901075)
收稿日期 2020/12/8
修改稿日期 2021/11/2
网络出版日期
作者单位点击查看
备注彭欢(1988-),男,安徽寿县人,硕士
引用该论文: PENG Huan,HU Xuewen,WANG Haibo,WANG Chengjian,SHI Dongya. Microstructure and Abrasive Wear Properties ofHot Rolled Ultra-High Strength Steel M1200HS[J]. Materials for mechancial engineering, 2022, 46(1): 68~72
彭欢,胡学文,王海波,王承剑,石东亚. 热轧超高强钢M1200HS的显微组织与磨粒磨损性能[J]. 机械工程材料, 2022, 46(1): 68~72
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】李文斌,费静,曹忠孝,等.我国低合金高强度耐磨钢的生产现状及发展方向[J].机械工程材料,2012,36(2):6-10. LI W B,FEI J,CAO Z X,et al.Production status and development direction of wear resistant steel with low alloy and high strength in China[J].Materials for Mechanical Engineering,2012,36(2):6-10.
【2】王玥瑶,何青,赵征志,等.卷取温度对热轧高强度搅拌罐用钢性能的影响[J].中国冶金,2020,30(3):40-44. WANG Y Y,HE Q,ZHAO Z Z,et al.Influence of coiling temperature on properties of hot-rolled high strength steel used for mixing tank[J].China Metallurgy,2020,30(3):40-44.
【3】温东辉,章德刚,蔡正,等.新型耐磨钢在混凝土搅拌车上的轻量化应用[J].专用汽车,2018(11):108-111. WEN D H, ZHANG D H, CAI Z,et al.Lightweight application of new wear-resistant steel in concrete mixer truck[J].Special Purpose Vehicle,2018(11):108-111.
【4】朱伏先,肖桂枝,陈炳张,等.直接淬火技术在中厚钢板生产中的工业应用[J].钢铁研究学报,2010,22(7):1-5. ZHU F X,XIAO G Z,CHEN B Z,et al.Industrial applications of direct quenching technology in medium plate production[J].Journal of Iron and Steel Research,2010,22(7):1-5.
【5】吴涛,刘宝良,武杰,等.高强耐磨钢板直接淬火板型控制工艺研究[J].宽厚板,2012,18(3):1-4. WU T,LIU B L,WU J,et al.Process study on flatness control of high strength wear resistant steel plate during direct quenching[J].Wide and Heavy Plate,2012,18(3):1-4.
【6】王明娣,刘东权,武会宾.淬火工艺对低合金耐磨钢组织与力学性能的影响[J].金属热处理,2018,43(8):156-161. WANG M D,LIU D Q,WU H B.Influence of quenching on microstructure and mechanical properties of low alloy wear-resistant steel[J].Heat Treatment of Metals,2018,43(8):156-161.
【7】张宇斌.耐磨钢Mn13热轧薄板的组织与性能[J].金属热处理,2019,44(7):161-162. ZHANG Y B.Microstructure and properties of hot rolled sheet Mn13 steel[J].Heat Treatment of Metals,2019,44(7):161-162.
【8】李大军,侯蕊.Mn13高锰钢的热处理工艺研究[J].热加工工艺,2010,39(16):158-160. LI D J,HOU R.Study on heat treatment process for Mn13 high manganese steel[J].Hot Working Technology,2010,39(16):158-160.
【9】邓想涛,王昭东,王国栋.工艺参数对NM500耐磨钢力学性能和三体冲击磨损性能的影响[J].材料热处理学报,2012,33(9):65-69. DENG X T,WANG Z D,WANG G D.Effects of process parameters on mechanical property and three-body impact abrasive wear of abrasion resistant steel NM500[J].Transactions of Materials and Heat Treatment,2012,33(9):65-69.
【10】梁亮,邓想涛,吴开明,等.低合金高强度耐磨钢的冲蚀磨损性能研究[J].轧钢,2018,35(1):10-16. LIANG L,DENG X T,WU K M,et al.Erosion wear behavior of low alloy abrasion resistance steel plates[J].Steel Rolling,2018,35(1):10-16.
【11】付贵,吴安成,李克天.耐磨机械设备用耐磨钢磨料磨损性能的研究[J].热加工工艺,2019,48(8):70-72. FU G,WU A C,LI K T.Research on abrasive wear properties of wear-resistant steels for wear-resisting machinery[J].Hot Working Technology,2019,48(8):70-72.
【12】巨彪,武会宾,车英健,等.回火温度对超高强耐磨钢板磨粒磨损特性的影响[J].热加工工艺,2015,44(16):220-222. JU B,WU H B,CHE Y J,et al.Effect of tempering temperature on abrasive wear behavior of ultrahigh strength wear resistance steel[J].Hot Working Technology,2015,44(16):220-222.
【13】徐祖耀.条状马氏体形态对钢力学性质的影响[J].热处理,2009,24(3):1-6. XU Z Y.Effect of lath martensite morphology on the mechanical properties of steel[J].Heat Treatment,2009,24(3):1-6.
【14】MORITO S,YOSHIDA H,MAKI T,et al.Effect of block size on the strength of lath martensite in low carbon steels[J].Materials Science and Engineering:A,2006,438/439/440:237-240.
【15】王春芳,王毛球,时捷,等.低碳马氏体钢的微观组织及其对强度的影响[J].钢铁,2007,42(11):57-60. WANG C F,WANG M Q,SHI J,et al.Microstructural characterization and its effect on strength of low carbon martensitic steel[J].Iron & Steel,2007,42(11):57-60.
【2】王玥瑶,何青,赵征志,等.卷取温度对热轧高强度搅拌罐用钢性能的影响[J].中国冶金,2020,30(3):40-44. WANG Y Y,HE Q,ZHAO Z Z,et al.Influence of coiling temperature on properties of hot-rolled high strength steel used for mixing tank[J].China Metallurgy,2020,30(3):40-44.
【3】温东辉,章德刚,蔡正,等.新型耐磨钢在混凝土搅拌车上的轻量化应用[J].专用汽车,2018(11):108-111. WEN D H, ZHANG D H, CAI Z,et al.Lightweight application of new wear-resistant steel in concrete mixer truck[J].Special Purpose Vehicle,2018(11):108-111.
【4】朱伏先,肖桂枝,陈炳张,等.直接淬火技术在中厚钢板生产中的工业应用[J].钢铁研究学报,2010,22(7):1-5. ZHU F X,XIAO G Z,CHEN B Z,et al.Industrial applications of direct quenching technology in medium plate production[J].Journal of Iron and Steel Research,2010,22(7):1-5.
【5】吴涛,刘宝良,武杰,等.高强耐磨钢板直接淬火板型控制工艺研究[J].宽厚板,2012,18(3):1-4. WU T,LIU B L,WU J,et al.Process study on flatness control of high strength wear resistant steel plate during direct quenching[J].Wide and Heavy Plate,2012,18(3):1-4.
【6】王明娣,刘东权,武会宾.淬火工艺对低合金耐磨钢组织与力学性能的影响[J].金属热处理,2018,43(8):156-161. WANG M D,LIU D Q,WU H B.Influence of quenching on microstructure and mechanical properties of low alloy wear-resistant steel[J].Heat Treatment of Metals,2018,43(8):156-161.
【7】张宇斌.耐磨钢Mn13热轧薄板的组织与性能[J].金属热处理,2019,44(7):161-162. ZHANG Y B.Microstructure and properties of hot rolled sheet Mn13 steel[J].Heat Treatment of Metals,2019,44(7):161-162.
【8】李大军,侯蕊.Mn13高锰钢的热处理工艺研究[J].热加工工艺,2010,39(16):158-160. LI D J,HOU R.Study on heat treatment process for Mn13 high manganese steel[J].Hot Working Technology,2010,39(16):158-160.
【9】邓想涛,王昭东,王国栋.工艺参数对NM500耐磨钢力学性能和三体冲击磨损性能的影响[J].材料热处理学报,2012,33(9):65-69. DENG X T,WANG Z D,WANG G D.Effects of process parameters on mechanical property and three-body impact abrasive wear of abrasion resistant steel NM500[J].Transactions of Materials and Heat Treatment,2012,33(9):65-69.
【10】梁亮,邓想涛,吴开明,等.低合金高强度耐磨钢的冲蚀磨损性能研究[J].轧钢,2018,35(1):10-16. LIANG L,DENG X T,WU K M,et al.Erosion wear behavior of low alloy abrasion resistance steel plates[J].Steel Rolling,2018,35(1):10-16.
【11】付贵,吴安成,李克天.耐磨机械设备用耐磨钢磨料磨损性能的研究[J].热加工工艺,2019,48(8):70-72. FU G,WU A C,LI K T.Research on abrasive wear properties of wear-resistant steels for wear-resisting machinery[J].Hot Working Technology,2019,48(8):70-72.
【12】巨彪,武会宾,车英健,等.回火温度对超高强耐磨钢板磨粒磨损特性的影响[J].热加工工艺,2015,44(16):220-222. JU B,WU H B,CHE Y J,et al.Effect of tempering temperature on abrasive wear behavior of ultrahigh strength wear resistance steel[J].Hot Working Technology,2015,44(16):220-222.
【13】徐祖耀.条状马氏体形态对钢力学性质的影响[J].热处理,2009,24(3):1-6. XU Z Y.Effect of lath martensite morphology on the mechanical properties of steel[J].Heat Treatment,2009,24(3):1-6.
【14】MORITO S,YOSHIDA H,MAKI T,et al.Effect of block size on the strength of lath martensite in low carbon steels[J].Materials Science and Engineering:A,2006,438/439/440:237-240.
【15】王春芳,王毛球,时捷,等.低碳马氏体钢的微观组织及其对强度的影响[J].钢铁,2007,42(11):57-60. WANG C F,WANG M Q,SHI J,et al.Microstructural characterization and its effect on strength of low carbon martensitic steel[J].Iron & Steel,2007,42(11):57-60.
相关信息