Corrosion Condition and Protection of High Reflective Ag Coating for Radiation Cooling Film
摘 要
高反射Ag薄膜在空气中易老化,通过改变环境中的湿度、温度、反应气体浓度三个条件对Ag薄膜的腐蚀行为进行研究。结果显示:Ag薄膜试样在60℃,90% RH大气环境中12 d后的黄边占比为7.2%,湿度对Ag薄膜腐蚀的影响最显著,温度次之。反应气体浓度降低到水中溶解度时对Ag薄膜的腐蚀抑制效果明显。SiNx/Ag-Cu/SiNx膜系结构可以减少水汽吸附,延缓反应气体在薄膜中的扩散并阻隔水汽,实现对Ag薄膜的防护。在60℃,90% RH大气环境中12 d后,SiNx/Ag-Cu/SiNx反射膜未观察到腐蚀。
Abstract
The highly reflective Ag film is easy to age in air. The corrosion behavior of the Ag film was studied by changing the three conditions of humidity, temperature and reaction gas concentration in the environment. The results showed that the yellow edge ratio of the Ag film sample was 7.2% after 12 d in the atmosphere of 60℃ and 90% RH. Humidity had the most significant effect on the corrosion of Ag film, by followed temperature. When the concentration of reaction gas was reduced to the solubility in water, the corrosion inhibition effect on the Ag film was obvious. The SiNx/Ag-Cu/SiNx film structure could reduce water vapor adsorption, delay the diffusion of reactive gases in the film and block water vapor, so as to protect the Ag film. No corrosion was observed on the surface of SiNx/Ag-Cu/SiNx reflective film after 12 d in 60℃, 90% RH atmosphere.
中图分类号 TG174.4 DOI 10.11973/fsyfh-202202003
所属栏目 试验研究
基金项目 宁波市科技计划(2019B10136)
收稿日期 2020/8/12
修改稿日期
网络出版日期
作者单位点击查看
引用该论文: YAN Yulei,YIN Zhengjie,ZHAO Jinling,ZHAI Huailun,WANG Minghui. Corrosion Condition and Protection of High Reflective Ag Coating for Radiation Cooling Film[J]. Corrosion & Protection, 2022, 43(2): 18
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】SAHU D R, LIN S Y, HUANG J L. ZnO/Ag/ZnO multilayer films for the application of a very low resistance transparent electrode[J]. Applied Surface Science, 2006, 252(20):7509-7514.
【2】ANDO E, MIYAZAKI M. Moisture degradation mechanism of silver-based low-emissivity coatings[J]. Thin Solid Films, 1999, 351(1/2):308-312.
【3】ANDO E, MIYAZAKI M. Moisture resistance of the low-emissivity coatings with a layer structure of Al-doped ZnO/Ag/Al-doped ZnO[J]. Thin Solid Films, 2001, 392(2):289-293.
【4】ANDO E, SUZUKI S, AOMINE N, et al. Sputtered silver-based low-emissivity coatings with high moisture durability[J]. Vacuum, 2000, 59(2/3):792-799.
【5】WANG Z G, CAI X, CHEN Q L, et al. Effects of Ti transition layer on stability of silver/titanium dioxide multilayered structure[J]. Thin Solid Films, 2007, 515(5):3146-3150.
【6】LEE H C, KIM J Y, NOH C H, et al. Selective metal pattern formation and its EMI shielding efficiency[J]. Applied Surface Science, 2006, 252(8):2665-2672.
【7】SARTO M S, SARTO F, LARCIPRETE M C, et al. Nanotechnology of transparent metals for radio frequency electromagnetic shielding[J]. IEEE Transactions on Electromagnetic Compatibility, 2003, 45(4):586-594.
【8】ZHAI Y, MA Y G, DAVID S N, et al. Scalable-manufactured randomized glass-polymer hybrid metamaterial for daytime radiative cooling[J]. Science, 2017, 355(6329):1062-1066.
【9】GRAEDEL T E. Corrosion mechanisms for silver exposed to the atmosphere[J]. Journal of the Electrochemical Society, 1992, 139(7):1963-1970.
【10】LEYGRAF C, WALLINDER I O, TIDBLAD J, et al. Atmospheric Corrosion[M]. Hoboken, NJ, USA:John Wiley & Sons, 2016.
【11】杨晓东, 赵青南, 韩宾, 等. 银纳米薄膜在室温大气条件下的氧化机理[J]. 硅酸盐学报, 2008, 36(7):954-959.
【12】大连理工大学无机化学教研室. 无机化学[M]. 4版.北京:高等教育出版社, 2001.
【2】ANDO E, MIYAZAKI M. Moisture degradation mechanism of silver-based low-emissivity coatings[J]. Thin Solid Films, 1999, 351(1/2):308-312.
【3】ANDO E, MIYAZAKI M. Moisture resistance of the low-emissivity coatings with a layer structure of Al-doped ZnO/Ag/Al-doped ZnO[J]. Thin Solid Films, 2001, 392(2):289-293.
【4】ANDO E, SUZUKI S, AOMINE N, et al. Sputtered silver-based low-emissivity coatings with high moisture durability[J]. Vacuum, 2000, 59(2/3):792-799.
【5】WANG Z G, CAI X, CHEN Q L, et al. Effects of Ti transition layer on stability of silver/titanium dioxide multilayered structure[J]. Thin Solid Films, 2007, 515(5):3146-3150.
【6】LEE H C, KIM J Y, NOH C H, et al. Selective metal pattern formation and its EMI shielding efficiency[J]. Applied Surface Science, 2006, 252(8):2665-2672.
【7】SARTO M S, SARTO F, LARCIPRETE M C, et al. Nanotechnology of transparent metals for radio frequency electromagnetic shielding[J]. IEEE Transactions on Electromagnetic Compatibility, 2003, 45(4):586-594.
【8】ZHAI Y, MA Y G, DAVID S N, et al. Scalable-manufactured randomized glass-polymer hybrid metamaterial for daytime radiative cooling[J]. Science, 2017, 355(6329):1062-1066.
【9】GRAEDEL T E. Corrosion mechanisms for silver exposed to the atmosphere[J]. Journal of the Electrochemical Society, 1992, 139(7):1963-1970.
【10】LEYGRAF C, WALLINDER I O, TIDBLAD J, et al. Atmospheric Corrosion[M]. Hoboken, NJ, USA:John Wiley & Sons, 2016.
【11】杨晓东, 赵青南, 韩宾, 等. 银纳米薄膜在室温大气条件下的氧化机理[J]. 硅酸盐学报, 2008, 36(7):954-959.
【12】大连理工大学无机化学教研室. 无机化学[M]. 4版.北京:高等教育出版社, 2001.
相关信息