Causes of leakage of water wall tube of boiler in a 200 MW coal-fired power plant
摘 要
某200 MW燃煤电厂锅炉水冷壁管在A级检修水压试验过程中发生泄漏。采用宏观观察、拉伸试验、金相检验、扫描电镜及能谱分析等方法,分析了该水冷壁管泄漏的原因。结果表明:因锅炉水质较差、停炉保护不到位、管子传热不良等原因,使富含氧化铁及氧化铜的水渣在锅炉水冷壁管向火面内壁产生沉积,形成垢下氢腐蚀,造成管子强度降低,最终导致管子泄漏。
Abstract
The water wall tube of boiler in a 200 MW coal-fired power plant leaked during the A-level maintenance hydraulic test.By means of macroscopic observation,tensile test,metallographic inspection,scanning electron microscope and energy spectrum analysis,the reasons for the leakage of water wall tube were analyzed.The results showed that due to the poor water quality of the boiler,the ineffective shutdown protection and the poor heat transfer of the pipe,the water slag rich in iron oxide and copper oxide was deposited on the inner wall of the fire surface of boiler water wall tube,resulting in under-deposit hydrogen corrosion.Caused a reduction in the strength of the pipe,which eventually led to leakage of pipe.
中图分类号 TG115.2 DOI 10.11973/lhjy-wl202203017
所属栏目 质量控制与失效分析
基金项目
收稿日期 2021/3/4
修改稿日期
网络出版日期
作者单位点击查看
备注赵林松(1979-),男,高级工程师,主要从事电站金属材料检测评估及失效分析工作,zhaolinsong@cgnpc.com.cn
引用该论文: ZHAO Linsong,MA Qinzheng,ZHAO Pengfei,LIU Xianliang. Causes of leakage of water wall tube of boiler in a 200 MW coal-fired power plant[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2022, 58(3): 63~65
赵林松,马芹征,赵朋飞,刘献良. 某200 MW燃煤电厂锅炉水冷壁管泄漏原因[J]. 理化检验-物理分册, 2022, 58(3): 63~65
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】龙会国,谢国胜,龙毅,等.锅炉水冷壁管沉积物下氧化腐蚀特征及其机理[J].腐蚀与防护,2014,35(6):579-583.
【2】李彦林.锅炉热管失效分析及预防[M].北京:中国电力出版社,2006.
【3】王敏.锅炉水冷壁腐蚀及爆裂的原因分析和防止对策[J].腐蚀与防护,2006,27(4):215-216.
【4】王鹏举,王荣文,张宗棠,等.锅炉水冷壁腐蚀失效的原因[J].腐蚀与防护,2016,37(3):255-258,262.
【2】李彦林.锅炉热管失效分析及预防[M].北京:中国电力出版社,2006.
【3】王敏.锅炉水冷壁腐蚀及爆裂的原因分析和防止对策[J].腐蚀与防护,2006,27(4):215-216.
【4】王鹏举,王荣文,张宗棠,等.锅炉水冷壁腐蚀失效的原因[J].腐蚀与防护,2016,37(3):255-258,262.
相关信息