Small sample test technology for strength of X70 pipeline girth weld
摘 要
采用小拉伸试样分层试验的方法测试了X70管道环焊缝的力学性能,从小试样的试验结果中不仅可以得到对接环焊缝的抗拉强度,还可以得到环焊缝不同区域的抗拉强度分布。结果表明:该对接环焊缝的屈服强度低于母材的屈服强度约20%,且环焊缝内部不同层的屈服强度也有较大差别。
Abstract
The mechanical properties of X70 pipeline girth weld were tested layer-by-layer by small tensile method. From the test results of small samples, not only the tensile strength of the butt girth weld could be obtained, but also the tensile strength distribution of different regions of the weld could be obtained. The results show that the yield strength of butt girth weld was about 20% lower than that of base metal, and the yield strength of different layers in the weld was also quite different.
中图分类号 TG457.6 DOI 10.11973/lhjy-wl202205001
所属栏目 试验与研究
基金项目
收稿日期 2021/7/15
修改稿日期
网络出版日期
作者单位点击查看
备注孙永辉(1986-),男,工程师,主要从事金属材料常规力学测试评价、材料微损测试评价、新能源材料测试评价工作
引用该论文: SUN Yonghui,YOU Jingze,SHANG Xuexin,LIU Kai,WANG Hankui. Small sample test technology for strength of X70 pipeline girth weld[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2022, 58(5): 1~3
孙永辉,尤景泽,商学欣,刘凯,王汉奎. X70管道环焊缝强度的小试样测试技术[J]. 理化检验-物理分册, 2022, 58(5): 1~3
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】孙德新.X70螺旋焊管焊接的工程应用研究[D].天津:天津大学,2007.
【2】任伟.管道环焊缝可靠性分析[D].北京:中国石油大学(北京),2017.
【3】吕向阳.X70管线钢焊接工艺研究[D].天津:天津大学,2006.
【4】乔宁.X70管线钢焊接接头韧性影响因素分析与改善措施[D].天津:天津大学,2014.
【5】吴立斌.抗大变形X70管线钢焊接技术研究[D].成都:西南石油大学,2015.
【6】刘雪梅,高连才,张彦华.X70管线钢焊接性分析[J].电焊机,2004,34(7):14-15,23.
【2】任伟.管道环焊缝可靠性分析[D].北京:中国石油大学(北京),2017.
【3】吕向阳.X70管线钢焊接工艺研究[D].天津:天津大学,2006.
【4】乔宁.X70管线钢焊接接头韧性影响因素分析与改善措施[D].天津:天津大学,2014.
【5】吴立斌.抗大变形X70管线钢焊接技术研究[D].成都:西南石油大学,2015.
【6】刘雪梅,高连才,张彦华.X70管线钢焊接性分析[J].电焊机,2004,34(7):14-15,23.
相关信息