反应堆压力容器用SA508 Gr.3钢落锤试验结果异常原因
Causes for abnormal results of drop weight test of SA508 Gr.3 steel for reactor pressure vessel
摘 要
国内某反应堆压力容器部件的母材见证件落锤试验结果出现异常。研究了母材见证件的化学成分、显微组织、焊接工艺、硬度、制样与试验过程，分析了影响落锤试验结果的主要原因，可为相关工作人员提供参考。
落锤试验
无塑性转变温度
reactor pressure vessel
drop weight test
nil-ductility transition temperature
Abstract
The drop weight test results of the base metal witness of a domestic reactor pressure vessel component were abnormal. The chemical composition, microstructure, welding process, hardness, sample preparation and test process of the base metal witness were studied, the main reasons affecting the drop weight test results were analyzed, which provided a reference for relevant staff.
中图分类号 TG115.5+6 DOI 10.11973/lhjy-wl202207007
所属栏目 试验与研究
基金项目
收稿日期 2021/11/10
修改稿日期
网络出版日期
作者单位点击查看
备注刘强(1983-),男,高级工程师,主要从事压水堆和金属块堆主设计和研发工作,157764497@qq.com
引用该论文: LIU Qiang,TU Shenghui,DING Xiangbin,PENG Xiangyang,LU Guangyao,ZHAI Lihong,LIU Qingsong. Causes for abnormal results of drop weight test of SA508 Gr.3 steel for reactor pressure vessel[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2022, 58(7): 28～31
刘强,涂盛辉,丁祥彬,彭祥阳,路广遥,翟立宏,刘青松. 反应堆压力容器用SA508 Gr.3钢落锤试验结果异常原因[J]. 理化检验－物理分册, 2022, 58(7): 28～31
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】赵登志,穆振芬,刘志国,等.核电材料的落锤试验研究[J].理化检验(物理分册),1997,33(1):23-26.
【2】刘钊,朱喜斌,吉宏林,等.核电装备制造中落锤试验的影响因素[J].工程与试验,2011,51(4):34-37.
【2】刘钊,朱喜斌,吉宏林,等.核电装备制造中落锤试验的影响因素[J].工程与试验,2011,51(4):34-37.
相关信息