60Si2Mn钢弹簧断裂原因
Fracture reason of 60Si2Mn steel spring
摘 要
某单元制动缸的缓解弹簧在检修测试过程中发生断裂。采用宏观观察、化学成分分析、硬度测试、金相检验、扫描电镜分析等方法对该弹簧的断裂原因进行了分析。结果表明：该弹簧加载后在应力与氢的交互作用下，逐渐形成平整的裂纹源区，裂纹快速扩展，最终发生脆性断裂。
弹簧
60Si2Mn钢
氢脆
断裂
unit brake cylinder
spring
60Si2Mn steel
hydrogen embrittlement
fracture
Abstract
The release spring of a unit brake cylinder broke during the maintenance and test. The fracture reason of the spring was analyzed by means of macroscopic observation, chemical composition analysis, hardness test, metallographic examination and scanning electron microscope analysis. The results show that the spring gradually formed a flat crack source region under the interaction of stress and hydrogen after loading, and the crack expanded rapidly, and finally brittle fracture occurred.
中图分类号 TG142.1+5 DOI 10.11973/lhjy-wl202207014
所属栏目 质量控制与失效分析
基金项目
收稿日期 2021/11/3
修改稿日期
网络出版日期
作者单位点击查看
备注宫高丽(1993-),女,助理工程师,主要从事金属材料理化检验检测工作,763980351@qq.com
引用该论文: GONG Gaoli. Fracture reason of 60Si2Mn steel spring[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2022, 58(7): 53～55
宫高丽. 60Si2Mn钢弹簧断裂原因[J]. 理化检验－物理分册, 2022, 58(7): 53～55
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】赵江,郝志超,孙俊喜,等.60Si2Mn弹簧断裂原因分析[J].河北冶金,2020(7):66-69.
【2】赵志江,杨宝利.弹簧的氢脆断裂特征与原因分析[J].国防技术基础,2006(8):41-43.
【3】周弘.弹簧电镀产生氢脆断裂预防对策[J].电镀与环保,1994,14(2):37.
【4】邱文鹏,常序华,王仁智.圆柱螺旋弹簧氢脆断裂失效分析[J].金属制品,2007,33(1):24-27.
【5】王挺,李振华.镀锌螺钉断裂分析[J].理化检验(物理分册),2015,51(9):668-670.
【2】赵志江,杨宝利.弹簧的氢脆断裂特征与原因分析[J].国防技术基础,2006(8):41-43.
【3】周弘.弹簧电镀产生氢脆断裂预防对策[J].电镀与环保,1994,14(2):37.
【4】邱文鹏,常序华,王仁智.圆柱螺旋弹簧氢脆断裂失效分析[J].金属制品,2007,33(1):24-27.
【5】王挺,李振华.镀锌螺钉断裂分析[J].理化检验(物理分册),2015,51(9):668-670.
相关信息