钢板表面星形裂纹的形成原因
Reasons of star cracks on steel plate surface
摘 要
某钢厂生产的钢板表面经常出现星形裂纹,采用宏观观察、金相检验、扫描电子显微镜分析和能谱分析等方法对该类裂纹产生原因进行分析,得出钢板表面星形裂纹产生的主要原因是铸坯表面存在气泡、晶间裂纹,或铸坯的低熔点物质选择性氧化或其含量高。最后提出了相应的改进措施。
星形裂纹
气泡
晶间裂纹
低熔点物质
steel plate
star crack
bubble
intergranular crack
low melting point substance
Abstract
Star cracks often appear on the surface of steel plate produced by a steel plant, the reasons of such cracks were analyzed by means of macroscopic observation, metallographic examination, scanning electron microscopy analysis and energy spectrum analysis. It was concluded that the main reasons of star cracks on the surface of steel plate were the existence of bubbles and intergranular cracks on the surface of slab, or the selective oxidation or high content of low melting point substances in slab. Finally, the corresponding improvement measures were put forward.
中图分类号 TG115.5 DOI 10.11973/lhjy-wl202208010
所属栏目 质量控制与失效分析
基金项目
收稿日期 2022/2/18
修改稿日期
网络出版日期
作者单位点击查看
备注童云峰(1987-),女,学士,工程师,主要从事钢铁产品的失效分析及新品的研发工作,woshitongyunfenghh@163.com
引用该论文: TONG Yunfeng. Reasons of star cracks on steel plate surface[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2022, 58(8): 36～38
童云峰. 钢板表面星形裂纹的形成原因[J]. 理化检验－物理分册, 2022, 58(8): 36～38
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】赵鹏,潘清红,邹宗树.Q235钢板表面裂纹形成原因分析[J].理化检验(物理分册), 2016,52(3):4.
【2】祝桂合,万友堂,张继明,等.钢板表面裂纹及氧化物圆点形成条件模拟试验[J].山东冶金,2012,34(2):30-33.
【3】许庆太,魏伯,赵晓飞,等.钢板表面纵向裂纹的金相检验和分析[J].理化检验(物理分册),2006,52(12):634-636.
【4】祝桂合,蒋雪军.钢板表面裂纹成因分析[J].河北冶金,2014(3):21-24.
【2】祝桂合,万友堂,张继明,等.钢板表面裂纹及氧化物圆点形成条件模拟试验[J].山东冶金,2012,34(2):30-33.
【3】许庆太,魏伯,赵晓飞,等.钢板表面纵向裂纹的金相检验和分析[J].理化检验(物理分册),2006,52(12):634-636.
【4】祝桂合,蒋雪军.钢板表面裂纹成因分析[J].河北冶金,2014(3):21-24.
相关信息