Causes of cylinder tube explosion of hydraulic cylinder
摘 要
采用宏观观察、化学成分分析、力学性能测试、金相检验等方法对某液压油缸缸筒的爆裂原因进行了分析。结果表明:液压油缸缸筒组织不均匀,存在混晶,导致材料的脆性较强;焊接工艺不当导致在焊接起弧点附近出现裂纹,引起应力集中,在较大应力作用下,裂纹快速扩展导致油缸缸筒爆裂。
Abstract
Macroscopic observation, chemical composition analysis, mechanical property test, metallographic examination and other methods were used to analyze the explosion reason of cylinder tube of an hydraulic cylinder. The results show that the structure of cylinder tube of hydraulic cylinder was uneven and there was mischcrystal, which led to the strong brittleness of the material. Improper welding process led to cracks near the welding arc point, which caused stress concentration. Under the action of large stress, the rapid propagation of cracks led to the explosion of the cylinder.
中图分类号 TG115.5 DOI 10.11973/lhjy-wl202208016
所属栏目 质量控制与失效分析
基金项目
收稿日期 2021/11/25
修改稿日期
网络出版日期
作者单位点击查看
备注张强(1986-),男,硕士,高级工程师,主要从事金属材料疲劳性能和腐蚀性能等的测试及失效分析工作,zhangq0514@163.com
引用该论文: ZHANG Qiang,WANG Shuqiang,WANG Wei. Causes of cylinder tube explosion of hydraulic cylinder[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2022, 58(8): 58~60
张强,王书强,王伟. 液压油缸缸筒爆裂原因[J]. 理化检验-物理分册, 2022, 58(8): 58~60
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】王荣.液压油缸外筒爆裂分析[J].理化检验(物理分册),2011,47(9):570-574.
【2】王温银,顾永琴,叶海燕.液压油缸开裂失效分析[J].金属热处理,2014,39(5):150-153.
【3】孙永庆,刘振宝,李文辉,等.05Cr17Ni4Cu4Nb钢液压油缸开裂失效分析[J].金属热处理,2018,43(11):239-242.
【4】杨晓,王世宁,张先锋,等.34CrNi3Mo钢制轧辊断裂原因分析[J].理化检验(物理分册),2019,55(10):741-744.
【5】马小明,熊烨.高压水泵主轴断裂失效分析[J].石油化工设备技术,2010,31(4):35-37.
【6】钟群鹏,周煜,张峥.裂纹学[M].北京:高等教育出版社,2014.
【2】王温银,顾永琴,叶海燕.液压油缸开裂失效分析[J].金属热处理,2014,39(5):150-153.
【3】孙永庆,刘振宝,李文辉,等.05Cr17Ni4Cu4Nb钢液压油缸开裂失效分析[J].金属热处理,2018,43(11):239-242.
【4】杨晓,王世宁,张先锋,等.34CrNi3Mo钢制轧辊断裂原因分析[J].理化检验(物理分册),2019,55(10):741-744.
【5】马小明,熊烨.高压水泵主轴断裂失效分析[J].石油化工设备技术,2010,31(4):35-37.
【6】钟群鹏,周煜,张峥.裂纹学[M].北京:高等教育出版社,2014.
相关信息