青岛室内大气环境中铁质试样的腐蚀劣化的行为
Corrosion and Deterioration Behavior of Iron Specimens in Qingdao Indoor Atmospheric Environment
摘 要
在无温湿度控制的青岛室内环境中进行了为期一年的环境监测，同时将白口铸铁和灰口铸铁置于此环境中考察了其腐蚀情况，采用超景深显微镜、SEM-EDS和激光拉曼光谱对试样表面的腐蚀产物进行分析，探讨了室内环境因素对馆藏铁质文物的腐蚀机制。结果表明：两种试样腐蚀初期的产物都以Fe2O3为主，随后检测到γ-FeOOH、α-FeOOH和少量β-FeOOH；随腐蚀时间的延长，Fe2O3和γ-FeOOH的含量出现先增多后减少的趋势，α-FeOOH含量呈增多的趋势；试样的腐蚀程度与室内环境因素密切相关，相同条件下，灰口铸铁的锈蚀程度小于白口铸铁。
灰口铸铁
大气腐蚀
预防性保护
white cast iron
gray cast iron
atmospheric corrosion
preventive conservation
Abstract
One-year environmental monitoring was carried out in Qingdao indoor environment without temperature and humidity control, and white cast iron and gray cast iron were placed in this environment to investigate the corrosion of the two samples. The corrosion products on the surface of the samples were analyzed by ultra-depth-of-field microscopy, SEM-EDS and laser Raman spectroscopy, and the corrosion mechanism of indoor environmental factors on iron cultural relics in museums was discussed. The results showed that Fe2O3 was the main product in the initial corrosion stage of the two samples, and γ-FeOOH, α-FeOOH and a small amount of β-FeOOH were subsequently detected. With the prolongation of corrosion time, the content of Fe2O3 and γ-FeOOH increased first and then decreased, and the content of α-FeOOH increased. The corrosion degree of the sample was closely related to the indoor environmental factors. Under the same conditions, the corrosion degree of gray cast iron was less than that of white cast iron.
中图分类号 TG174 DOI 10.11973/fsyfh-202207004
所属栏目 金属文物保护技术
基金项目 国家重点研发计划（2020YFC1522102）
收稿日期 2022/3/14
修改稿日期
网络出版日期
作者单位点击查看
引用该论文: LIANG Yifan,WANG Yazheng,WANG Quanyu. Corrosion and Deterioration Behavior of Iron Specimens in Qingdao Indoor Atmospheric Environment[J]. Corrosion & Protection, 2022, 43(7): 24
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】柯俊. 现代科技和科技史研究[C]//考古文物与现代科技:现代科技考古研讨会论文汇编. 北京:人民出版社, 2001:4.
【2】张钰, 马金香, 冯露菲, 等. 天津博物馆文物保存环境调查与监测分析——以2015年1月监测数据为例[J]. 文物保护与考古科学, 2017, 29(2):94-99.
【3】余健. 博物馆文物馆藏环境调查研究——以四川广汉三星堆博物馆为例[J]. 科技资讯, 2010, 32(30):186-187.
【4】赵阳, 徐东良, 陈玉珍. 吐鲁番博物馆馆藏纸质文物的储存与展示环境评估[J]. 吐鲁番学研究, 2015(1):104-117.
【5】张月玲. 中国国家博物馆环境空气质量监测报告[J]. 文物保护与考古科学, 2006, 18(2):41-45.
【6】李晓刚. 金属大气腐蚀初期行为与机理[M]. 北京:科学出版社, 2009.
【7】林翠, 肖志刚. 碳钢在NaCl薄液膜下的电化学腐蚀行为[J]. 腐蚀与防护, 2014, 35(4):316-320.
【8】董希青, 许淳淳, 王紫色. 土壤介质中HCO3-对仿古铸铁腐蚀的影响[J]. 铸造技术, 2008, 29(1):102-106.
【9】许淳淳, 王紫色, 王菊琳. 模拟土壤介质中仿古铸铁腐蚀产物的形貌及其生长过程[J]. 化工学报, 2005, 12(12):2373-2379.
【10】贾明浩, 胡沛, 胡钢. 儿茶素对模拟古代铁质文物的稳定化保护[J]. 腐蚀与防护, 2022, 43(1):1-7.
【11】刘雨薇, 赵洪涛, 王振尧. 碳钢和耐候钢在南沙海洋大气环境中的初期腐蚀行为[J]. 金属学报, 2020, 56(9):1247-1254.
【12】王振尧, 于全成, 汪川, 等. 在含硫污染的海洋大气环境中核电用钢的腐蚀行为[J]. 科学通报, 2012, 57(31):2991-2998.
【13】陈新彦, 陈大明, 陈旭, 等. 热带海洋大气环境中耐候钢腐蚀特征与机理的研究[J]. 腐蚀科学与防护技术, 2018, 30(2):150-156.
【14】OH S J, COOK D C, TOWNSEND H E. Atmospheric corrosion of different steels in marine, rural and industrial environments[J]. Corrosion Science, 1999, 41(9):1687-1702.
【15】邹衡. 天马-曲村[M]. 北京:科学出版社, 2000:1178-1180.
【16】中国社会科学院考古所. 满城汉墓发掘报告[M]. 北京:文物出版社, 1980:369-376.
【17】曹公望, 刘雨薇, 张丹丹, 等. Q235和Q345钢在红沿河大气环境中的腐蚀行为[J]. 腐蚀与防护, 2018, 39(1):24-28, 34.
【18】宋学鑫, 黄松鹏, 汪川, 等. 碳钢在红沿河海洋工业大气环境中的初期腐蚀行为[J]. 金属学报, 2020, 56(10):1355-1365.
【19】DE LA FUENTE D, DÍAZ I, SIMANCAS J, et al. Long-term atmospheric corrosion of mild steel[J]. Corrosion Science, 2011, 53(2):604-617.
【20】李华, 胡塔峰, 杜维莎. 秦兵马俑和汉阳陵遗址保存环境之比较[J]. 文物保护与考古科学, 2019, 31(2):53-60.
【21】RAMAN A, KUBAN B, RAZVAN A. The application of infrared spectroscopy to the study of atmospheric rust systems-I. Standard spectra and illustrative applications to identify rust phases in natural atmospheric corrosion products[J]. Corrosion Science, 1991, 32(12):1295-1306.
【22】刘月娥, 林翠, 赵晴. 碳钢在SO2大气环境中的腐蚀行为[J]. 中国腐蚀与防护学报, 2010, 30(1):51-57.
【23】刘秀晨, 安成强. 金属腐蚀学[M]. 北京:国防工业出版社, 2002.
【24】林翠, 刘月娥. 高湿度无污染大气中温度对碳钢腐蚀的影响[J]. 腐蚀与防护, 2009, 30(12):874-878.
【25】WEISSENRIEDER J, KLEBER C, SCHREINER M, et al. In Situ Studies of Sulfate Nest Formation on Iron[J]. Journal of The Electrochemical Society, 2004, 151(9):B497-B504.
【26】王振尧, 于全成, 陈军君, 等. 周期干湿浸条件下P265GH钢和Q235钢的大气腐蚀行为[J]. 中国腐蚀与防护学报, 2014, 34(1):53-58.
【27】屈庆, 严川伟, 张蕾, 等. NaCl和SO2在A3钢初期大气腐蚀中的协同效应[J]. 金属学报, 2002(10):1062-1066.
【28】MISAWA T, ASAMI K, HASHIMOTO K, et al. The mechanism of atmospheric rusting and the protective amorphous rust on low alloy steel[J]. Corrosion Science, 1974, 14(4):279-289.
【29】林翠, 赵晴, 刘月娥, 等. 含SO2大气中20碳钢腐蚀产物的演变[J]. 金属学报, 2010, 46(3):358-365.
【30】STRATMANN M, BOHNENKAMP K, ENGELL H J. An Electrochemical Study of Phase-Transitions in Rust Layers[J]. Corrosion Science, 1983, 23(9):969-985.
【31】EVANS U R, TAYLOR C. Mechanism of atmospheric rusting[J]. Corrosion Science, 1972, 12(3):227-246.
【32】王蕙贞, 朱虹, 宋迪生, 等. 秦汉铁器锈蚀机理探讨及保护方法研究[J]. 文物保护与考古科学, 2003(1):7-11.
【33】DAWSON J L, FERREIRA M. Electrochemical studies of the pitting of austenitic stainless steel[J]. Corrosion, 1986, 26(12):1009-1026.
【34】徐方圆, 吴来明, 解玉林, 等. 文物保存环境中温湿度评估方法研究[J]. 文物保护与考古科学, 2012, 24(S1):6-12.
【35】WANG Q. Effects of relative humidity on the corrosion of iron:an experimental view[J]. The British Museum Technical Research Bulletin, 2007(1):65-73.
【36】王蕙贞. 文物保护学[M]. 北京:文物出版社, 2009:411.
【37】中华人民共和国住房和城乡建设部. 博物馆建筑设计规范:JGJ 66-2015[S]. 北京:中国建筑工业出版社.
【38】BØHM B, RYHL-SVENDSEN M. Analysis of the thermal conditions in an unheated museum store in a temperate climate. On the thermal interaction of earth and store[J]. Energy and Buildings, 2011, 43(12):3337-3342.
【39】RIMMER M, THICKETT D, WATKINSON D, et al. Guidelines for the storage and display of archaeological metalwork[R].[S.l]:[s.n.], 2013.
【2】张钰, 马金香, 冯露菲, 等. 天津博物馆文物保存环境调查与监测分析——以2015年1月监测数据为例[J]. 文物保护与考古科学, 2017, 29(2):94-99.
【3】余健. 博物馆文物馆藏环境调查研究——以四川广汉三星堆博物馆为例[J]. 科技资讯, 2010, 32(30):186-187.
【4】赵阳, 徐东良, 陈玉珍. 吐鲁番博物馆馆藏纸质文物的储存与展示环境评估[J]. 吐鲁番学研究, 2015(1):104-117.
【5】张月玲. 中国国家博物馆环境空气质量监测报告[J]. 文物保护与考古科学, 2006, 18(2):41-45.
【6】李晓刚. 金属大气腐蚀初期行为与机理[M]. 北京:科学出版社, 2009.
【7】林翠, 肖志刚. 碳钢在NaCl薄液膜下的电化学腐蚀行为[J]. 腐蚀与防护, 2014, 35(4):316-320.
【8】董希青, 许淳淳, 王紫色. 土壤介质中HCO3-对仿古铸铁腐蚀的影响[J]. 铸造技术, 2008, 29(1):102-106.
【9】许淳淳, 王紫色, 王菊琳. 模拟土壤介质中仿古铸铁腐蚀产物的形貌及其生长过程[J]. 化工学报, 2005, 12(12):2373-2379.
【10】贾明浩, 胡沛, 胡钢. 儿茶素对模拟古代铁质文物的稳定化保护[J]. 腐蚀与防护, 2022, 43(1):1-7.
【11】刘雨薇, 赵洪涛, 王振尧. 碳钢和耐候钢在南沙海洋大气环境中的初期腐蚀行为[J]. 金属学报, 2020, 56(9):1247-1254.
【12】王振尧, 于全成, 汪川, 等. 在含硫污染的海洋大气环境中核电用钢的腐蚀行为[J]. 科学通报, 2012, 57(31):2991-2998.
【13】陈新彦, 陈大明, 陈旭, 等. 热带海洋大气环境中耐候钢腐蚀特征与机理的研究[J]. 腐蚀科学与防护技术, 2018, 30(2):150-156.
【14】OH S J, COOK D C, TOWNSEND H E. Atmospheric corrosion of different steels in marine, rural and industrial environments[J]. Corrosion Science, 1999, 41(9):1687-1702.
【15】邹衡. 天马-曲村[M]. 北京:科学出版社, 2000:1178-1180.
【16】中国社会科学院考古所. 满城汉墓发掘报告[M]. 北京:文物出版社, 1980:369-376.
【17】曹公望, 刘雨薇, 张丹丹, 等. Q235和Q345钢在红沿河大气环境中的腐蚀行为[J]. 腐蚀与防护, 2018, 39(1):24-28, 34.
【18】宋学鑫, 黄松鹏, 汪川, 等. 碳钢在红沿河海洋工业大气环境中的初期腐蚀行为[J]. 金属学报, 2020, 56(10):1355-1365.
【19】DE LA FUENTE D, DÍAZ I, SIMANCAS J, et al. Long-term atmospheric corrosion of mild steel[J]. Corrosion Science, 2011, 53(2):604-617.
【20】李华, 胡塔峰, 杜维莎. 秦兵马俑和汉阳陵遗址保存环境之比较[J]. 文物保护与考古科学, 2019, 31(2):53-60.
【21】RAMAN A, KUBAN B, RAZVAN A. The application of infrared spectroscopy to the study of atmospheric rust systems-I. Standard spectra and illustrative applications to identify rust phases in natural atmospheric corrosion products[J]. Corrosion Science, 1991, 32(12):1295-1306.
【22】刘月娥, 林翠, 赵晴. 碳钢在SO2大气环境中的腐蚀行为[J]. 中国腐蚀与防护学报, 2010, 30(1):51-57.
【23】刘秀晨, 安成强. 金属腐蚀学[M]. 北京:国防工业出版社, 2002.
【24】林翠, 刘月娥. 高湿度无污染大气中温度对碳钢腐蚀的影响[J]. 腐蚀与防护, 2009, 30(12):874-878.
【25】WEISSENRIEDER J, KLEBER C, SCHREINER M, et al. In Situ Studies of Sulfate Nest Formation on Iron[J]. Journal of The Electrochemical Society, 2004, 151(9):B497-B504.
【26】王振尧, 于全成, 陈军君, 等. 周期干湿浸条件下P265GH钢和Q235钢的大气腐蚀行为[J]. 中国腐蚀与防护学报, 2014, 34(1):53-58.
【27】屈庆, 严川伟, 张蕾, 等. NaCl和SO2在A3钢初期大气腐蚀中的协同效应[J]. 金属学报, 2002(10):1062-1066.
【28】MISAWA T, ASAMI K, HASHIMOTO K, et al. The mechanism of atmospheric rusting and the protective amorphous rust on low alloy steel[J]. Corrosion Science, 1974, 14(4):279-289.
【29】林翠, 赵晴, 刘月娥, 等. 含SO2大气中20碳钢腐蚀产物的演变[J]. 金属学报, 2010, 46(3):358-365.
【30】STRATMANN M, BOHNENKAMP K, ENGELL H J. An Electrochemical Study of Phase-Transitions in Rust Layers[J]. Corrosion Science, 1983, 23(9):969-985.
【31】EVANS U R, TAYLOR C. Mechanism of atmospheric rusting[J]. Corrosion Science, 1972, 12(3):227-246.
【32】王蕙贞, 朱虹, 宋迪生, 等. 秦汉铁器锈蚀机理探讨及保护方法研究[J]. 文物保护与考古科学, 2003(1):7-11.
【33】DAWSON J L, FERREIRA M. Electrochemical studies of the pitting of austenitic stainless steel[J]. Corrosion, 1986, 26(12):1009-1026.
【34】徐方圆, 吴来明, 解玉林, 等. 文物保存环境中温湿度评估方法研究[J]. 文物保护与考古科学, 2012, 24(S1):6-12.
【35】WANG Q. Effects of relative humidity on the corrosion of iron:an experimental view[J]. The British Museum Technical Research Bulletin, 2007(1):65-73.
【36】王蕙贞. 文物保护学[M]. 北京:文物出版社, 2009:411.
【37】中华人民共和国住房和城乡建设部. 博物馆建筑设计规范:JGJ 66-2015[S]. 北京:中国建筑工业出版社.
【38】BØHM B, RYHL-SVENDSEN M. Analysis of the thermal conditions in an unheated museum store in a temperate climate. On the thermal interaction of earth and store[J]. Energy and Buildings, 2011, 43(12):3337-3342.
【39】RIMMER M, THICKETT D, WATKINSON D, et al. Guidelines for the storage and display of archaeological metalwork[R].[S.l]:[s.n.], 2013.
相关信息