20G钢锅炉烟道管开裂原因
Cracking reasons of 20G steel boiler flue pipe
摘 要
某厂所用的20G钢锅炉烟道管在使用过程中发生开裂。采用宏观观察、化学成分分析、金相检验、力学性能测试及能谱分析等方法分析其开裂的原因。结果表明：Cu元素的富集以及组织存在过热现象是造成锅炉烟道管在使用过程中发生开裂的主要原因。
组织过热
元素富集
晶界氧化
20G steel boiler flue pipe
microstructure overheating
element enrichment
grain boundary oxidation
Abstract
The 20G steel boiler flue pipe used in a factory cracked during operation. Macroscopic observation, chemical composition analysis, metallographic examination, mechanical properties test and energy spectrum analysis were used to analyze the reasons for the cracking of the boiler flue pipe. The results show that the enrichment of Cu element and the overheating of the microstructure were the main reasons for the cracking of the boiler flue pipe during operation.
中图分类号 TG115.2 DOI 10.11973/lhjy-wl202209009
所属栏目 质量控制与失效分析
基金项目
收稿日期 2022/1/4
修改稿日期
网络出版日期
作者单位点击查看
备注胡曼(1993-),女,助理工程师,主要从事钢铁材料的物理检验工作,838491892@qq.com
引用该论文: HU Man,NI Wenxiao,XUE Junfeng,WANG Dong,WANG Litao. Cracking reasons of 20G steel boiler flue pipe[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2022, 58(9): 35～38
胡曼,倪文啸,薛俊峰,王栋,王立涛. 20G钢锅炉烟道管开裂原因[J]. 理化检验－物理分册, 2022, 58(9): 35～38
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】秦建平, 朱艳春,楚志兵.热轧无缝钢管短流程生产工艺研究[J].钢管,2021,50(3):46-49.
【2】卢书媛,王卫忠,俞璐,等.锅炉过热器管爆裂原因分析[J].理化检验(物理分册),2016,52(11):807-810.
【3】马向东,贾益军,李秀坤,等.20G钢管焊接接头断裂失效分析[J].焊接技术,2020,49(增刊):185-187.
【4】马庆谦,游菊.锅炉水冷壁管爆管原因分析[J].理化检验(物理分册),2004,40(9):465-468.
【5】李智超,赵立东,鲍泽斌.20g钢魏氏组织韧性及微观断口形貌研究[J].物理测试,2003,21(5):7-10.
【2】卢书媛,王卫忠,俞璐,等.锅炉过热器管爆裂原因分析[J].理化检验(物理分册),2016,52(11):807-810.
【3】马向东,贾益军,李秀坤,等.20G钢管焊接接头断裂失效分析[J].焊接技术,2020,49(增刊):185-187.
【4】马庆谦,游菊.锅炉水冷壁管爆管原因分析[J].理化检验(物理分册),2004,40(9):465-468.
【5】李智超,赵立东,鲍泽斌.20g钢魏氏组织韧性及微观断口形貌研究[J].物理测试,2003,21(5):7-10.
相关信息