Al-Zn-Ga低驱动电位牺牲阳极的设计及其电化学性能
Design and Electrochemical Performance of Al-Zn-Ga Sacrificial Anodes with Low Driving Voltage
摘 要
根据正交试验表设计了16种Al-Zn-Ga低驱动电位牺牲阳极的合金配方，采用恒电流法评价了这些阳极的电化学性能，并观察其腐蚀形貌。结果表明：随着阳极中Zn和Ga含量的升高，阳极工作电位负移；其中，最佳Al-Zn-Ga阳极的合金配方为Al-0.25Zn-0.05Ga，该配方牺牲阳极的工作电位为-800~-750 mV，电容量最高，达到2 426 A·h/kg。
牺牲阳极
电容量
镓
low driving voltage
sacrificial anode
electric capacity
gallium
Abstract
16 kinds of alloy formulas of Al-Zn-Ga sacrificial anodes with low driving voltage were designed in terms of orthogonal test table. The electrochemical performance of the Al-Zn-Ga anodes was studied by galvanostatic method. And the corrosion morphology of the anodes was observered. The results indicated that with the increase of Zn and Ga content in the anodes, the working potentials of the anodes shifted negatively. The best alloy formula of Al-Zn-Ga anode was Al-0.25Zn-0.05Ga, which had working potentials in a range from -800 mV to -750 mV, and had the highest electric capacity up to 2 426 A·h/kg.
中图分类号 TG174.3 DOI 10.11973/fsyfh-202211006
所属栏目 试验研究
基金项目
收稿日期 2021/11/6
修改稿日期
网络出版日期
作者单位点击查看
联系人作者许实(xushi@sunrui.net)
引用该论文: XU Shi,WANG Tingyong,WANG Hui,WANG Haitao. Design and Electrochemical Performance of Al-Zn-Ga Sacrificial Anodes with Low Driving Voltage[J]. Corrosion & Protection, 2022, 43(11): 31
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】杨朝晖, 刘斌, 李向阳, 等. 牺牲阳极在舰船阴极保护中的应用和进展[J]. 中国材料进展, 2014, 33(9/10):618-622.
【2】LEMIEUX E, GROLLEAU A, HOGAN E, et al. Performance evaluation of low voltage anodes for cathodic protection[C]//Corrosion 2002. Houston, TX:NACE International, 2002:02016.
【3】李凯, 马力, 闫永贵, 等. 低驱动电位牺牲阳极的研究[J]. 材料保护, 2010, 43(4):95-97, 118.
【4】马力, 李威力, 曾红杰, 等. 低驱动电位Al-Ga合金牺牲阳极及其活化机制[J]. 中国腐蚀与防护学报, 2010, 30(4):329-332.
【5】马力, 曲本文, 闫永贵, 等. 低驱动电位铝合金牺牲阳极的研制[J]. 材料开发与应用, 2014, 29(3):61-65.
【6】曲本文, 马力, 闫永贵, 等. 海水温度对Al-Zn-Ga-Si低电位牺牲阳极性能的影响[J]. 腐蚀科学与防护技术, 2015, 27(3):259-263.
【7】袁传军, 梁成浩, 安晓雯. Ga对Al-Zn-In合金牺牲阳极电化学性能影响[J]. 大连理工大学学报, 2004, 44(4):502-505.
【2】LEMIEUX E, GROLLEAU A, HOGAN E, et al. Performance evaluation of low voltage anodes for cathodic protection[C]//Corrosion 2002. Houston, TX:NACE International, 2002:02016.
【3】李凯, 马力, 闫永贵, 等. 低驱动电位牺牲阳极的研究[J]. 材料保护, 2010, 43(4):95-97, 118.
【4】马力, 李威力, 曾红杰, 等. 低驱动电位Al-Ga合金牺牲阳极及其活化机制[J]. 中国腐蚀与防护学报, 2010, 30(4):329-332.
【5】马力, 曲本文, 闫永贵, 等. 低驱动电位铝合金牺牲阳极的研制[J]. 材料开发与应用, 2014, 29(3):61-65.
【6】曲本文, 马力, 闫永贵, 等. 海水温度对Al-Zn-Ga-Si低电位牺牲阳极性能的影响[J]. 腐蚀科学与防护技术, 2015, 27(3):259-263.
【7】袁传军, 梁成浩, 安晓雯. Ga对Al-Zn-In合金牺牲阳极电化学性能影响[J]. 大连理工大学学报, 2004, 44(4):502-505.
相关信息