Corrosion Resistance Evaluation and On-Site Application of Low Alloy Corrosion-Resistant Pipes in Changqing Oilfield
摘 要
长庆油田重点腐蚀区单一内防腐蚀技术无法满足现场需要。本工作介绍了长庆油田低合金耐蚀管材的优选,通过室内高温高压试验和现场挂环试验,对其耐蚀性进行了评价,并在油田现场实现了规模应用。结果表明:各因素中温度对腐蚀速率影响最大,相同腐蚀条件下,宝钢和包钢生产的5Cr低合金耐蚀钢的平均腐蚀速率和局部腐蚀速率较N80钢分别低50%以上和40%以上,其预测寿命可达10a,5Cr低合金钢是有效降低长庆油田重点腐蚀区域局部腐蚀且经济的选材方案。
Abstract
Single internal anti-corrosion technology in key corrosion areas of Changqing oilfield cannot meet the needs of on-site. This paper introduced the optimization of low alloy corrosion-resistant pipe in the oilfield, which evaluated the corrosion resistance through indoor high temperature and high pressure test and field hanging ring test, and realized large-scale application on-site. The results showed that temperature had the greatest effect on the corrosion rate. Under the same corrosion conditions, the average corrosion rate and local corrosion rate of 5Cr low alloy corrosion resistant steel produced by Baosteel and Baotou Steel was lower than those of N80 steel by more than 50% and 40%, respectively, and its predicted life could reach 10 years. 5Cr low alloy corrosion resistant steel is an effective and economical material selection scheme to reduce local corrosion in key corrosion areas of Changqing oilfield.
中图分类号 TG174 DOI 10.11973/fsyfh-202212013
所属栏目 应用技术
基金项目
收稿日期 2021/5/26
修改稿日期
网络出版日期
作者单位点击查看
引用该论文: GUO Gang,LIU Guangsheng,WANG Xiaopeng,LI Qiongwei,YANG Lihua,SUN Yulai,ZHOU Zhiping. Corrosion Resistance Evaluation and On-Site Application of Low Alloy Corrosion-Resistant Pipes in Changqing Oilfield[J]. Corrosion & Protection, 2022, 43(12): 83
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】万章,孔韦海,张强. 耐蚀合金临界点蚀温度标准试验方法比较[J]. 腐蚀与防护,2019,40(2):105-109.
【2】张玉碧,王东哲,刘海定,等. 一种新型国产高性能耐蚀合金在湿H2S环境中的应力腐蚀性能[J]. 腐蚀与防护,2011,32(12):939-943.
【3】顾浚祥. 化工环境用不锈类耐蚀合金的局部腐蚀[J]. 腐蚀与防护,1991,12(6):311-316,307.
【4】李娜,荣海波,赵国仙. 耐蚀油套管管材的国内外研究现状[J]. 材料科学与工程学报,2011,29(3):471-477.
【5】吕祥鸿,赵国仙,张建兵,等. 低Cr耐蚀管材的国内外研究进展[J]. 材料导报,2009,23(5):72-76.
【6】孙芳萍,成杰,罗慧娟,等. 油田某管道管材耐蚀性分析评价[J]. 材料保护,2019,52(6):161-167.
【7】曲艳双,韩明轩,许诺. 胺类固化环氧GFRP管材输运含CO2流体耐蚀性研究[J]. 纤维复合材料,2017,34(2):36-40.
【8】李慧,奚运涛,李琼玮,等. 储气库耐蚀合金管材的环空保护液研制及应用[J]. 天然气与石油,2017,35(2):91-95.
【9】罗慧娟,张志浩. 苏里格气田集输管道管材的耐蚀性评价[J]. 石油工程建设,2015,41(2):82-85.
【2】张玉碧,王东哲,刘海定,等. 一种新型国产高性能耐蚀合金在湿H2S环境中的应力腐蚀性能[J]. 腐蚀与防护,2011,32(12):939-943.
【3】顾浚祥. 化工环境用不锈类耐蚀合金的局部腐蚀[J]. 腐蚀与防护,1991,12(6):311-316,307.
【4】李娜,荣海波,赵国仙. 耐蚀油套管管材的国内外研究现状[J]. 材料科学与工程学报,2011,29(3):471-477.
【5】吕祥鸿,赵国仙,张建兵,等. 低Cr耐蚀管材的国内外研究进展[J]. 材料导报,2009,23(5):72-76.
【6】孙芳萍,成杰,罗慧娟,等. 油田某管道管材耐蚀性分析评价[J]. 材料保护,2019,52(6):161-167.
【7】曲艳双,韩明轩,许诺. 胺类固化环氧GFRP管材输运含CO2流体耐蚀性研究[J]. 纤维复合材料,2017,34(2):36-40.
【8】李慧,奚运涛,李琼玮,等. 储气库耐蚀合金管材的环空保护液研制及应用[J]. 天然气与石油,2017,35(2):91-95.
【9】罗慧娟,张志浩. 苏里格气田集输管道管材的耐蚀性评价[J]. 石油工程建设,2015,41(2):82-85.
相关信息