Causes of Fractured Y-Type Tee in Adsorption Desulfurization Unit
摘 要
针对某石化企业吸附脱硫装置Y型三通发生断裂,通过宏观观察、化学成分分析、扫描电镜分析、硬度检测和力学性能试验,并结合有限元分析,分析了三通断裂的原因。结果表明:三通的断裂形式为脆性断裂,断口存在显著的应力集中,这是造成三通断裂的根本原因;同时,在长期高温含氢环境作用下,三通出现了明显的材质劣化,硬度和断后伸长率偏低,室温下的冲击功仅为5.0J,具有缺口敏感性高和脆性显著等缺点。
Abstract
In view of the fracture of Y-type tee in adsorption desulfurization unit of a petrochemical enterprise, the fracture causes mode the were analyzed by macroscopic observation, chemical composition analysis, scanning electron microscope analysis, hardness detection and mechanical properties test, combined with finite element analysis. The results showed that the fracture mode was brittle fracture, and there was obvious stress concentration on the fracture surface, which was the fundamental cause of tee fracture. Meanwhile under the long-term high temperature and hydrogen-containing environment, the tee exhibited obvious material degradation, low hardness and elongation after fracture, and the impact energy at room temperature was only 5.0 J, which had the disadvantages of high notch sensitivity and obvious brittleness.
中图分类号 TG174 DOI 10.11973/fsyfh-202212017
所属栏目 失效分析
基金项目 国家市场监督管理总局科技计划项目(2021MK087);广东省特种设备检测研究院科技项目(2020CY02,2021CY-1-01)
收稿日期 2022/8/4
修改稿日期
网络出版日期
作者单位点击查看
引用该论文: HU Huasheng,CHEN Junyang,DENG Cong. Causes of Fractured Y-Type Tee in Adsorption Desulfurization Unit[J]. Corrosion & Protection, 2022, 43(12): 104
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】杨燕鹏,罗云,曾珠,等. 压力管道社会风险可接受准则研究[J]. 中国安全科学学报,2014,24(9):128-133.
【2】何仁洋,栾湘东,张庆春,等. 压力管道安全完整性技术法规与标准体系研究[J]. 压力容器,2012,29(7):44-50.
【3】李德君,高华,孔祥路,等. 20钢等径三通失效分析[J]. 金属热处理,2022,47(2):262-266.
【4】郑文祥,吴跃,刘俊建. 给水三通阀阀杆断裂失效分析[J]. 理化检验(物理分册),2016,52(10):755-758.
【5】吉章红. 炼油厂二甲苯装置吸附塔格栅用管件开裂原因分析及处置[J]. 压力容器,2020,37(6):48-53.
【6】刘文生. 某电厂高压调汽门EH油管断裂原因[J]. 理化检验-物理分册,2021,57(7):61-64.
【7】钟群鹏,赵子华. 断口学[M]. 北京:高等教育出版社,2006.
【8】廖景娱. 金属构件失效分析[M]. 北京:化学工业出版社,2003.
【9】杨王玥,强文江. 材料力学行为[M]. 北京:化学工业出版社,2009.
【10】李炯辉. 金属材料金相图谱[M]. 北京:机械工业出版社,2006.
【11】SHI J,WANG J,SONG W,et al. Failure analysis of flange sealing surface of outlet pipeline of wax oil hydrogenation reactor[C]//ASME 2020 Pressure Vessels & Piping Conference.[S.l.]:[s.n.],2020.
【12】汪凤,范玉然,尹长华,等. 16Mn钢管道工程用三通表面裂纹成因分析[J]. 金属热处理,2011,36(S1):161-164.
【13】SUBRAMANIAN C. Leakage of gasoil from side cut piping in crude distillation unit of a petroleum refinery[J]. Journal of Pipeline Science and Engineering,2022,2(1):97-108.
【2】何仁洋,栾湘东,张庆春,等. 压力管道安全完整性技术法规与标准体系研究[J]. 压力容器,2012,29(7):44-50.
【3】李德君,高华,孔祥路,等. 20钢等径三通失效分析[J]. 金属热处理,2022,47(2):262-266.
【4】郑文祥,吴跃,刘俊建. 给水三通阀阀杆断裂失效分析[J]. 理化检验(物理分册),2016,52(10):755-758.
【5】吉章红. 炼油厂二甲苯装置吸附塔格栅用管件开裂原因分析及处置[J]. 压力容器,2020,37(6):48-53.
【6】刘文生. 某电厂高压调汽门EH油管断裂原因[J]. 理化检验-物理分册,2021,57(7):61-64.
【7】钟群鹏,赵子华. 断口学[M]. 北京:高等教育出版社,2006.
【8】廖景娱. 金属构件失效分析[M]. 北京:化学工业出版社,2003.
【9】杨王玥,强文江. 材料力学行为[M]. 北京:化学工业出版社,2009.
【10】李炯辉. 金属材料金相图谱[M]. 北京:机械工业出版社,2006.
【11】SHI J,WANG J,SONG W,et al. Failure analysis of flange sealing surface of outlet pipeline of wax oil hydrogenation reactor[C]//ASME 2020 Pressure Vessels & Piping Conference.[S.l.]:[s.n.],2020.
【12】汪凤,范玉然,尹长华,等. 16Mn钢管道工程用三通表面裂纹成因分析[J]. 金属热处理,2011,36(S1):161-164.
【13】SUBRAMANIAN C. Leakage of gasoil from side cut piping in crude distillation unit of a petroleum refinery[J]. Journal of Pipeline Science and Engineering,2022,2(1):97-108.
相关信息