某铁路桥梁用20MnTiB钢高强螺栓断裂原因
Fracture cause of 20MnTiB steel high strength bolt for a railway bridge
摘 要
某铁路主桥钢桁梁杆间20MnTiB钢高强螺栓发生断裂。采用复检试验、化学成分分析、金相检验、硬度测试、力学性能测试和断口分析等方法,分析了螺栓断裂的原因。结果表明:螺栓的断裂形式为氢致断裂,断裂原因是螺栓中锰元素含量偏高,导致耐腐蚀性下降,长期在潮湿环境下服役,致使螺栓发生氢致断裂。
钢桁梁杆
高强螺栓
氢脆
氢致断裂
20MnTiB steel
steel truss rod
high strength bolt
hydrogen embrittlement
hydrogen induced fracture
Abstract
The 20MnTiB steel high strength bolt between the steel truss rods of a railway main bridge broke. The causes of bolt fracture were analyzed by means of recheck test, chemical composition analysis, metallographic examination, hardness test, mechanical property test and fracture analysis. The results show that the fracture mode of the bolt was hydrogen induced fracture. The fracture cause was that the content of manganese element in the bolt was too high, which led to the decline of corrosion resistance. The bolt had been in service for a long time in a humid environment, resulting in hydrogen induced fracture.
中图分类号 TB31 TG115 TH131.3 DOI 10.11973/lhjy-wl202301011
所属栏目 质量控制与失效分析
基金项目
收稿日期 2022/4/30
修改稿日期
网络出版日期
作者单位点击查看
备注宋艳双(1976-),女,本科,高级工程师,主要从事大型土木工程的施工工作
引用该论文: SONG Yanshuang,ZHOU Youlong,CHEN Haoyu. Fracture cause of 20MnTiB steel high strength bolt for a railway bridge[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2023, 59(1): 39～42
宋艳双,周友龙,陈昊宇. 某铁路桥梁用20MnTiB钢高强螺栓断裂原因[J]. 理化检验－物理分册, 2023, 59(1): 39～42
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】姜招喜,许宗凡,张挺. 紧固件制备与典型失效案例[M]. 北京:国防工业出版社,2015.
【2】齐延生,胡晓峰,王静,等. 高强度螺栓断裂失效分析[J]. 理化检验(物理分册),2018,54(5):359-363.
【3】陆春振. 桥梁用高强度螺栓延迟断裂研究[D]. 北京:中国铁道科学研究院,2019.
【4】焦丽,王国亮,徐向阳,等. 柴油机曲轴断裂原因分析[J]. 金属热处理,2015,40(8):195-198.
【5】焦丽,赵英军,张伟民,等. 12. 9级高强度螺栓断裂原因分析[J]. 热处理,2020,35(4):42-45.
【2】齐延生,胡晓峰,王静,等. 高强度螺栓断裂失效分析[J]. 理化检验(物理分册),2018,54(5):359-363.
【3】陆春振. 桥梁用高强度螺栓延迟断裂研究[D]. 北京:中国铁道科学研究院,2019.
【4】焦丽,王国亮,徐向阳,等. 柴油机曲轴断裂原因分析[J]. 金属热处理,2015,40(8):195-198.
【5】焦丽,赵英军,张伟民,等. 12. 9级高强度螺栓断裂原因分析[J]. 热处理,2020,35(4):42-45.
相关信息