高强度螺柱断裂原因
Fracture reason of high strength stud
摘 要
某高强度螺柱在服役10个月后发生断裂，采用宏观观察、化学成分分析、扫描电镜分析、金相检验以及力学性能测试等方法对螺柱断裂原因进行了研究。结果表明：在较大交变载荷的作用下，断裂螺柱螺纹牙底的折叠位置萌生裂纹并扩展，最终发生疲劳断裂。
疲劳断裂
交变载荷
折叠
high strength stud
fatigue fracture
alternating load
folding
Abstract
The high strength stud was fractured after 10 months of service. The causes of stud fracture were studied by means of macroscopic observation, chemical composition analysis, scanning electron microscope analysis, metallographic examination and mechanical property test. The results show that under the action of large alternating load, cracks initiated and propagated at the folding position of the screw thread bottom of the fractured stud, and finally fatigue fracture occured.
中图分类号 TB31 TG115.5 DOI 10.11973/lhjy-wl202302011
所属栏目 质量控制与失效分析
基金项目 中国机械科学研究总院集团有限公司技术发展基金项目（36062101Y）
收稿日期 2022/3/8
修改稿日期
网络出版日期
作者单位点击查看
备注金双峰(1982-),女,高级工程师,主要从事理化检验和失效分析工作,jinshuangfeng6602@163.com
引用该论文: JIN Shuangfeng,DOU Zhi,DU Shuai. Fracture reason of high strength stud[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2023, 59(2): 39～42
金双峰,窦智,杜帅. 高强度螺柱断裂原因[J]. 理化检验－物理分册, 2023, 59(2): 39～42
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】张友君,刘杰,丁志敏,等.风电装备特种紧固螺栓成型研究[J].湖南有色金属,2021,37(3):46-51.
相关信息