高含CO2-H2S-Cl-环境中井深温度对管线钢腐蚀的影响
Effect of Well Depth Temperature on Corrosion of X60 Pipeline Steel in Environment with High CO2-H2S-Cl- Content
摘 要
利用高温高压反应釜模拟高含CO2-H2S-Cl-的腐蚀环境，对X60管线钢进行恒定井深温度和阶变井深温度下的腐蚀模拟试验。通过失重法评价了X60管线钢的均匀腐蚀速率，并利用激光共聚焦显微镜、扫描电子显微镜（SEM）、能谱仪（EDS）和X射线衍射仪（XRD）等测试分析手段，研究了井深温度对X60管线钢腐蚀行为的影响。结果表明：在高含CO2-H2S-Cl-环境中，恒定井深温度下，X60管线钢表面均发生了点蚀，腐蚀速率随着温度升高而下降；X60管线钢在阶变井深温度下的均匀腐蚀速率低于恒定井深温度下的，其局部腐蚀风险随温降的增大而增大。
H2S-CO2腐蚀
局部腐蚀
X60管线钢
well depth temperature
H2S-CO2 corrosion
localized corrosion
X60 pipeline steel
Abstract
A high temperature and high pressure reactor was used to simulate the corrosion environment with high CO2-H2S-Cl- content, and corrosion simulation tests were carried out on X60 pipeline steel at constant well depth temperatures and step-changing well depth temperatures. The uniform corrosion rate of X60 pipeline steel was evaluated by weight loss method. And the effect of well depth temperature on the corrosion behavior of X60 pipeline steel were studied by means of laser confocal microscopy, scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS) and X-ray diffraction (XRD). The results showed that in the environment with high CO2-H2S-Cl- content, pitting corrosion occurred on the surface of X60 pipeline steel at constant well depth temperatures. The corrosion rates of X60 pipeline steel decreased with the increase of temperatures. The corrosion rates of X60 pipeline steel at step-changing well depth temperatures were lower than those at constant well depth temperatures, but the risk of localized corrosion rose with the increase of temperature drop.
中图分类号 TG174 DOI 10.11973/fsyfh-202302003
所属栏目 试验研究
基金项目 国家自然科学基金（52004312，52101071）；中国石油重大科技专项（2021ZZ01-08）
收稿日期 2022/4/6
修改稿日期
网络出版日期
作者单位点击查看
引用该论文: ZHANG Yunan,FAN Xuehua,HU Jiahui,ZHU Jinyang,JIANG Zitao,CHEN Peipei,ZHANG Lei. Effect of Well Depth Temperature on Corrosion of X60 Pipeline Steel in Environment with High CO2-H2S-Cl- Content[J]. Corrosion & Protection, 2023, 44(2): 13
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】张旭. 浅议石油管线钢在H2S/CO2环境下腐蚀行为[J]. 科技信息, 2011(1):445.
【2】樊学华, 于勇, 陈丽娟, 等. 高温高Cl-含量环境中H2S/CO2分压对超级双相不锈钢UNS S32750点蚀行为的影响[J]. 腐蚀与防护, 2021, 42(2):32-36.
【3】尹依娜, 汪沈阳, 王清岭, 等. 含CO2/H2S高温高压油井腐蚀控制技术[J]. 全面腐蚀控制, 2016, 30(3):55-57.
【4】杨建炜, 章军, 曹建平, 等. 温度对管线钢H2S/CO2腐蚀行为的影响[J]. 材料工程, 2011, 39(1):87-91.
【5】刘烈炜, 张振飞, 徐东林. 抗硫碳钢在高温高压CO2/H2S条件下腐蚀速率的研究[J]. 材料保护, 2008, 41(1):15-16, 50, 84.
【6】朱世东, 刘会, 白真权, 等. 模拟油田CO2/H2S环境中P110钢的动态腐蚀行为[J]. 石油与天然气化工, 2009, 38(1):65-68, 97.
【7】田伟, 谢发勤, 严密林, 等. 温度对80SS油管钢腐蚀行为的影响[J]. 电镀与环保, 2008, 28(1):34-37.
【8】MICHEL B, MAGDY G, KEVIN G, et al. Weight loss corrosion with H2S:using past operations for designing future facilities[C]//Corrosion 2006. Houston:NACE International, 2006:06122.
【9】BIJAN K, KHLEFA E. Materials design strategy:effects of H2S/CO2 corrosion on materials selection[C]//Corrosion 2006. Houston:NACE International, 2006:06152.
【10】GREGG M, THILL D, SLOFSTRA J, et al. Corrosion experiences and inhibition practices for managing wet sour salty gas pipeline environments contaminated with elemental sulfur deposits[C]//Corrosion 2003. Houston:NACE International, 2003:03174.
【11】曾勇. L245NCS碳钢和316L不锈钢在CO2/H2S环境中腐蚀行为的研究[D]. 武汉:华中科技大学, 2012.
【12】白真权, 李鹤林, 刘道新, 等. 模拟油田H2S/CO2环境中N80钢的腐蚀及影响因素研究[J]. 材料保护, 2003, 36(4):32-34.
【13】王成达, 严密林, 赵新伟, 等. 油气田开发中H2S/CO2腐蚀研究进展[J]. 西安石油大学学报(自然科学版), 2005, 20(5):66-70.
【14】姜放. 高酸性气田金属材料的实验室评价方法研究[J]. 天然气工业, 2004, 24(10):105-107, 16.
【2】樊学华, 于勇, 陈丽娟, 等. 高温高Cl-含量环境中H2S/CO2分压对超级双相不锈钢UNS S32750点蚀行为的影响[J]. 腐蚀与防护, 2021, 42(2):32-36.
【3】尹依娜, 汪沈阳, 王清岭, 等. 含CO2/H2S高温高压油井腐蚀控制技术[J]. 全面腐蚀控制, 2016, 30(3):55-57.
【4】杨建炜, 章军, 曹建平, 等. 温度对管线钢H2S/CO2腐蚀行为的影响[J]. 材料工程, 2011, 39(1):87-91.
【5】刘烈炜, 张振飞, 徐东林. 抗硫碳钢在高温高压CO2/H2S条件下腐蚀速率的研究[J]. 材料保护, 2008, 41(1):15-16, 50, 84.
【6】朱世东, 刘会, 白真权, 等. 模拟油田CO2/H2S环境中P110钢的动态腐蚀行为[J]. 石油与天然气化工, 2009, 38(1):65-68, 97.
【7】田伟, 谢发勤, 严密林, 等. 温度对80SS油管钢腐蚀行为的影响[J]. 电镀与环保, 2008, 28(1):34-37.
【8】MICHEL B, MAGDY G, KEVIN G, et al. Weight loss corrosion with H2S:using past operations for designing future facilities[C]//Corrosion 2006. Houston:NACE International, 2006:06122.
【9】BIJAN K, KHLEFA E. Materials design strategy:effects of H2S/CO2 corrosion on materials selection[C]//Corrosion 2006. Houston:NACE International, 2006:06152.
【10】GREGG M, THILL D, SLOFSTRA J, et al. Corrosion experiences and inhibition practices for managing wet sour salty gas pipeline environments contaminated with elemental sulfur deposits[C]//Corrosion 2003. Houston:NACE International, 2003:03174.
【11】曾勇. L245NCS碳钢和316L不锈钢在CO2/H2S环境中腐蚀行为的研究[D]. 武汉:华中科技大学, 2012.
【12】白真权, 李鹤林, 刘道新, 等. 模拟油田H2S/CO2环境中N80钢的腐蚀及影响因素研究[J]. 材料保护, 2003, 36(4):32-34.
【13】王成达, 严密林, 赵新伟, 等. 油气田开发中H2S/CO2腐蚀研究进展[J]. 西安石油大学学报(自然科学版), 2005, 20(5):66-70.
【14】姜放. 高酸性气田金属材料的实验室评价方法研究[J]. 天然气工业, 2004, 24(10):105-107, 16.
相关信息