Preparation and Properties of Environment Friendly Epoxy Coatings with High Solid Content and Low Surface Treatment Tolerance
摘 要
为了满足钢结构设备表面的维修需要,制备了高固含低表面处理容忍性环氧涂层,并分别讨论了树脂含量、固化剂种类以及复配颜填料对于所制备涂层性能的影响。结果表明:采用最优配方(A组分中环氧树脂质量分数为25%,改性曼尼希碱为固化剂,磷酸锌、氧化锌、三聚磷酸铝、钼酸锌、复合铁钛粉复配体系为颜填料)制备的涂料具有较好的流动性和润湿性,在低表面处理基材上即可使用,成膜后涂层的防腐蚀性能优异。
Abstract
Epoxy coatings with high solid content and low surface treatment tolerance were prepared, and the effects of resin content, curing agent type, compound of pigment and filler on the properties of the prepared coatings were discussed respectively, in order to meet the maintenance requirements of steel structure equipment surface. The results showed that the coating prepared with the optimum formula had good flow property and wettability, in which the mass fraction of epoxy resin in component A was 25%, modified Mannich base was curing agent, the compound of zinc phosphate, zinc oxide, aluminum tripolyphosphate, zinc molybdate, and composite iron-titanium powders was pigment and filler. So it was able to be used on the substrate after low surface treatment, and the corrosion resistance of the film coating was excellent.
中图分类号 TQ630.7+9 DOI 10.11973/fsyfh-202302012
所属栏目 试验研究
基金项目
收稿日期 2020/12/16
修改稿日期
网络出版日期
作者单位点击查看
引用该论文: SHI Meihui,LIU Hongyu,WU Jinglong,HAN Yue,KANG Xin,ZHOU Naiyu. Preparation and Properties of Environment Friendly Epoxy Coatings with High Solid Content and Low Surface Treatment Tolerance[J]. Corrosion & Protection, 2023, 44(2): 70
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】PARHIZKAR N, RAMEZANZADEH B, SHAHRABI T. Corrosion protection and adhesion properties of the epoxy coating applied on the steel substrate pre-treated by a Sol-gel based silane coating filled with amino and isocyanate silane functionalized graphene oxide nanosheets[J]. Applied Surface Science, 2018, 439:45-59.
【2】吴贤官. 带锈涂料及其应用[J]. 涂装与电镀, 2003(1):34-36.
【3】殷宪霞. 港口机械设备钢结构的防护涂装[J]. 涂料技术与文摘, 2014, 35(6):41-43.
【4】练兆华, 张强, 霍晟. 低表面处理涂料性能测试[J]. 船海工程, 2019, 48(2):135-137, 141.
【5】徐科, 方健君, 廉兵杰. 高性能低表面处理环氧涂料的制备和性能研究[J]. 涂料工业, 2019, 49(4):27-33.
【6】杨万国, 贾思洋, 张波, 等. 低表面处理涂料的研究现状与发展前景[J]. 现代涂料与涂装, 2011, 14(2):24-27.
【7】黄强, 张霁, 王健, 等. 团体标准《低VOCs含量高固体分、超高固体分和无溶剂环氧涂料定义》的解读[J]. 中国涂料, 2018, 33(9):21-24.
【8】BAGHDADI Y N, YOUSSEF L, BOUHADIR K, et al. The effects of modified zinc oxide nanoparticles on the mechanical/thermal properties of epoxy resin[J]. Journal of Applied Polymer Science, 2020, 137(43):49330.
【9】王德中. 环氧树脂生产与应用[M]. 2版. 北京:化学工业出版社, 2001.
【10】袁涛. 环氧树脂E51改性增韧研究[J]. 山东工业技术, 2017(5):183.
【11】宋道理. 浅谈曼尼希碱环氧固化剂[C]//第十五次全国环氧树脂应用技术学术交流会论文集.[出版地不详]:[出版者不详], 2011.
【12】赵明, 孙明明, 张雪, 等. 曼尼希改性胺固化剂及在环氧胶中的应用研究[J]. 化学与黏合, 2014, 36(6):411-413, 429.
【13】刘守贵, 甘国华, 王家贵. 环氧树脂胺系固化剂改性综述[J]. 热固性树脂, 1996, 11(4):46-52.
【14】姬振行, 袁振, 代凤鸣, 等. 水性带锈防锈涂料的制备[J]. 中国涂料, 2019, 34(10):29-32.
【15】袁爱群. 磷酸锌防锈颜料合成工艺的改进及其防锈性能研究[D]. 南宁:广西大学, 2003.
【16】刘有法, 刘丽亚. 三聚磷酸铝的应用及合成[J]. 磷肥与复肥, 2002, 17(4):77-78.
【17】李家权. 复合铁钛粉及其系列防锈漆[J]. 涂料工业, 2003, 33(7):51-53.
【2】吴贤官. 带锈涂料及其应用[J]. 涂装与电镀, 2003(1):34-36.
【3】殷宪霞. 港口机械设备钢结构的防护涂装[J]. 涂料技术与文摘, 2014, 35(6):41-43.
【4】练兆华, 张强, 霍晟. 低表面处理涂料性能测试[J]. 船海工程, 2019, 48(2):135-137, 141.
【5】徐科, 方健君, 廉兵杰. 高性能低表面处理环氧涂料的制备和性能研究[J]. 涂料工业, 2019, 49(4):27-33.
【6】杨万国, 贾思洋, 张波, 等. 低表面处理涂料的研究现状与发展前景[J]. 现代涂料与涂装, 2011, 14(2):24-27.
【7】黄强, 张霁, 王健, 等. 团体标准《低VOCs含量高固体分、超高固体分和无溶剂环氧涂料定义》的解读[J]. 中国涂料, 2018, 33(9):21-24.
【8】BAGHDADI Y N, YOUSSEF L, BOUHADIR K, et al. The effects of modified zinc oxide nanoparticles on the mechanical/thermal properties of epoxy resin[J]. Journal of Applied Polymer Science, 2020, 137(43):49330.
【9】王德中. 环氧树脂生产与应用[M]. 2版. 北京:化学工业出版社, 2001.
【10】袁涛. 环氧树脂E51改性增韧研究[J]. 山东工业技术, 2017(5):183.
【11】宋道理. 浅谈曼尼希碱环氧固化剂[C]//第十五次全国环氧树脂应用技术学术交流会论文集.[出版地不详]:[出版者不详], 2011.
【12】赵明, 孙明明, 张雪, 等. 曼尼希改性胺固化剂及在环氧胶中的应用研究[J]. 化学与黏合, 2014, 36(6):411-413, 429.
【13】刘守贵, 甘国华, 王家贵. 环氧树脂胺系固化剂改性综述[J]. 热固性树脂, 1996, 11(4):46-52.
【14】姬振行, 袁振, 代凤鸣, 等. 水性带锈防锈涂料的制备[J]. 中国涂料, 2019, 34(10):29-32.
【15】袁爱群. 磷酸锌防锈颜料合成工艺的改进及其防锈性能研究[D]. 南宁:广西大学, 2003.
【16】刘有法, 刘丽亚. 三聚磷酸铝的应用及合成[J]. 磷肥与复肥, 2002, 17(4):77-78.
【17】李家权. 复合铁钛粉及其系列防锈漆[J]. 涂料工业, 2003, 33(7):51-53.
相关信息