单晶硅拉晶炉富氩尾气回收管道腐蚀原因
Corrosion Reasons of Argon-Rich Tail Gas Recovery Pipeline for Single Crystal Silicon Pulling Furnace
摘 要
通过设备运行情况分析、化学成分分析,研究了单晶硅拉晶炉富氩尾气回收管道的腐蚀原因。结果表明:引起管道腐蚀的原因是真空泵的润滑油在高温下分解产生了氟化氢、硫化氢及氯化氢等多种腐蚀性物质,这些腐蚀性物质溶于冷凝水中,并随着时间的延长逐渐累积,从而造成管道的腐蚀。通过吸附剂吸附、去离子水吸收以及优化管道的材质和壁厚解决了管道腐蚀问题。
富氩尾气
管道腐蚀
润滑油
single crystal silicon pulling furnace
argon-rich tail gas
pipeline corrosion
lubricating oil
Abstract
The corrosion causes of argon-rich tail gas recovery pipeline from single crystal silicon pulling furnace were studied by means of equipment operation analysis and chemical composition analysis. The results showed that the cause of pipeline corrosion was that the lubricating oil of the vacuum pump decomposes at high temperature to produce a variety of corrosive substances such as hydrogen fluoride, hydrogen sulfide and hydrogen chloride. These corrosive substances were dissolved in condensed water and gradually accumulated with the extension of time, thus aggravating the corrosion of the pipeline. The pipeline corrosion problem was solved by adsorbent adsorption, deionized water absorption and optimization of pipeline material and wall thickness.
中图分类号 TG174 DOI 10.11973/fsyfh-202303016
所属栏目 失效分析
基金项目 水电机械设备设计与维护湖北省重点实验室开放基金(2019KJK03);石墨增材制造技术与装备湖北省工程研究中心开放基金(HRCGAM202105)
收稿日期 2021/9/26
修改稿日期
网络出版日期
作者单位点击查看
引用该论文: DU Dayan,YUAN Youlu,JIAO Wenyi,HUANG Mengyuan,LI Yunyang. Corrosion Reasons of Argon-Rich Tail Gas Recovery Pipeline for Single Crystal Silicon Pulling Furnace[J]. Corrosion & Protection, 2023, 44(3): 107
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】黄新平,黄春梅. 循环冷却水中氯离子对板换材料选择的影响[J]. 石油化工设计,2006,23(2):44-46,10.
【2】贾逸群,刘人铜,李施放,等. 油气管道二氧化碳腐蚀研究[J]. 云南化工,2019,46(2):177-178.
【3】文宇,刘安峥,宫政,等. 浅谈二氧化碳的腐蚀机理与防护[J]. 科技信息,2012(1):161,111.
【4】王秀文,陈文艺,邹恺. 润滑油基础油结构组成与性能关系研究进展[J]. 应用化工,2014,43(3):539-542.
【5】张峥,翁惠新,张鸣,等. 不同加工工艺基础油的结构特征对其性能的影响(Ⅰ)——饱和烃结构对其性能的影响[J]. 润滑与密封,2002,27(6):35-37,40.
【6】田新衍,王建鑫. 化学气相沉积法多晶硅生产工艺的研究[J]. 广州化工,2014,42(13):183-184,192.
【7】张学元. 二氧化碳腐蚀与控制[M]. 北京:化学工业出版社,2001.
【8】李立峰,马文礼,张伟,等. 润滑油储罐的腐蚀与防护[J]. 石油化工腐蚀与防护,2020,37(5):30-32.
【9】ZHENG Y G,BROWN B,NEČIAĆ S. Electrochemical study and modeling of H2S corrosion of mild steel[J]. Corrosion,2014,70(4):351-365.
【10】JIANG X,NEČIAĆ S,KINSELLA B,et al. Electrochemical investigation of the role of Cl- on localized carbon dioxide corrosion behavior of mild steel[J]. Corrosion,2013,69(1):15-24.
【2】贾逸群,刘人铜,李施放,等. 油气管道二氧化碳腐蚀研究[J]. 云南化工,2019,46(2):177-178.
【3】文宇,刘安峥,宫政,等. 浅谈二氧化碳的腐蚀机理与防护[J]. 科技信息,2012(1):161,111.
【4】王秀文,陈文艺,邹恺. 润滑油基础油结构组成与性能关系研究进展[J]. 应用化工,2014,43(3):539-542.
【5】张峥,翁惠新,张鸣,等. 不同加工工艺基础油的结构特征对其性能的影响(Ⅰ)——饱和烃结构对其性能的影响[J]. 润滑与密封,2002,27(6):35-37,40.
【6】田新衍,王建鑫. 化学气相沉积法多晶硅生产工艺的研究[J]. 广州化工,2014,42(13):183-184,192.
【7】张学元. 二氧化碳腐蚀与控制[M]. 北京:化学工业出版社,2001.
【8】李立峰,马文礼,张伟,等. 润滑油储罐的腐蚀与防护[J]. 石油化工腐蚀与防护,2020,37(5):30-32.
【9】ZHENG Y G,BROWN B,NEČIAĆ S. Electrochemical study and modeling of H2S corrosion of mild steel[J]. Corrosion,2014,70(4):351-365.
【10】JIANG X,NEČIAĆ S,KINSELLA B,et al. Electrochemical investigation of the role of Cl- on localized carbon dioxide corrosion behavior of mild steel[J]. Corrosion,2013,69(1):15-24.
相关信息