高温水中硫酸根阴离子对Inconel 600合金应力腐蚀开裂的影响
Effect of Sulphate Anions in High Temperature Water on Stress Corrosion Cracking of Inconel 600 Alloy
摘 要
采用慢应变速率试验(SSRT)研究了硫酸根阴离子浓度对Inconel 600镍基合金在模拟压水堆(PWR)一回路水中应力腐蚀开裂(SCC)敏感性的影响。结果表明:硫酸根离子促进Inconel 600镍基合金在高温水中的应力腐蚀开裂;随着硫酸根离子浓度升高,合金SCC敏感性增大;当高温水中硫酸根离子含量超过300 μg/kg时,断口边缘出现局部腐蚀和局部穿晶裂纹。
Inconel 600合金
应力腐蚀开裂
高温水
硫酸根阴离子
pressurized water reactor primary water
Inconel 600 alloy
stress corrosion cracking
high temperature water
sulphate anion
Abstract
The effect of sulphate anion concentration on stress corrosion cracking (SCC) sensitivity of Inconel 600 alloy in simulated pressurized water reactor (PWR) primary water was studied by slow strain rate test (SSRT) method. The results showed that sulphate promoted the SCC of Inconel 600 alloy in high temperature water. The SCC sensitivity of the alloy increased with the increase of sulphate concentration. When the sulphate concentration exceeded 300 μg/kg, localized corrosion and localized transgranular cracks appeared on the edge of the fracture surface.
中图分类号 TG172 DOI 10.11973/fsyfh-202304002
所属栏目 试验研究
基金项目 尖峰计划项目(R-2020SZSO53TF);国家自然科学基金(51771107)
收稿日期 2023/3/20
修改稿日期
网络出版日期
作者单位点击查看
引用该论文: WU Yibing,ZHANG Yu,CHEN Hongyu,CUI Tongming,XU Xinhe,PAN Deng,Lü Zhanpeng. Effect of Sulphate Anions in High Temperature Water on Stress Corrosion Cracking of Inconel 600 Alloy[J]. Corrosion & Protection, 2023, 44(4): 9
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】LU Z P,SHOJI T,YAMAZAKI S,et al. Characterization of microstructure,local deformation and microchemistry in Alloy 600 heat-affected zone and stress corrosion cracking in high temperature water[J]. Corrosion Science,2012,58:211-228.
【2】DIERCKS D R,MUSCARA J,SHACK W J. Steam generator tube integrity program[J]. Nuclear Engineering and Design,1996,165:143-149.
【3】ZINKLE S J,WAS G S. Materials challenges in nuclear energy[J]. Acta Materialia,2013,61(3):735-758.
【4】FYFITCH S. Corrosion and stress corrosion cracking of Ni-base alloys[M]//Comprehensive Nuclear Materials. Amsterdam:Elsevier,2012:69-92.
【5】吴思博. 压水堆核电站蒸汽发生器传热管硫致腐蚀失效机理[D]. 天津:天津大学,2018.
【6】袁曹龙,李新民,邓佳杰,等. 阴离子对600镍基合金腐蚀行为影响的研究[J]. 全面腐蚀控制,2011,25(6):45-48.
【7】IAEA Nuclear Energy Series No. NP-T-S. Stress corrosion cracking in light water reactors:good practices and lessons learned[R]. [S.l.]:[s.n.],2011.
【8】PARK J H,CHOPRA O K,NATESAN K,et al. Boric acid corrosion of light water reactor pressure vessel materials[R]. NUREG/CR-6875,ANL-04/08,2005.
【9】孙海涛,凌礼恭,吕云鹤,等. 国内压水堆核电站设备材料应力腐蚀问题及安全管理[J]. 腐蚀科学与防护技术,2016,28(3):283-287.
【10】夏大海,宋诗哲,王俭秋,等. 690和800合金在高温高压水中硫致腐蚀失效研究进展[J]. 金属学报,2017,53(12):1541-1554.
【11】华惠中,黄春波,吕战鹏,等. 800、600和690合金的铅致应力腐蚀破裂[J]. 腐蚀与防护,2001,22(11):483-488.
【12】王光辉,彭君,袁义帆,等. 硫酸根离子和电极电位对异材焊接件A508/52M在高温水中应力腐蚀破裂的影响[J]. 理化检验(物理分册),2013,49(6):357-361,366.
【13】张平柱,胡石林,张伟国. 酸性硫酸根离子介质中奥氏体不锈钢的应力腐蚀行为研究[J]. 原子能科学技术,2003,37:145-148.
【14】夏大海,杨丽霞. 不同浓度比的硫酸根和氯离子溶液中钝化膜的半导体特性转变机制研究[J]. 物理化学学报,2014,30(8):1465-1473.
【15】张锐峰,陈圆,余菲. 690镍基合金在SO42-,S2O32-,Cl-溶液中的电化学行为研究[J]. 清洗世界,2016,32(6):14-16,33.
【16】张丽,韩恩厚,柯伟. S2O32-对Ni基合金671在NaCl水溶液中的点蚀行为的影响[J]. 腐蚀科学与防护技术,2004,16(4):229-232.
【17】陈俊劼,肖茜,吕战鹏,等. 硫酸根离子对铁在弱碱性溶液中阳极溶解和钝化行为的影响[J]. 物理化学学报,2015,31(6):1093-1104.
【18】王钢,袁曹龙,梅其政,等. 硫酸盐对600镍基合金腐蚀行为影响的研究[J]. 清洗世界,2012,28(2):15-19.
【19】夏大海,宋扬,宋诗哲,等. 酸性氯离子溶液中硫代硫酸根对800合金腐蚀机理[J]. 天津大学学报(自然科学与工程技术版),2018,51(6):591-597.
【20】XIA D H,SONG S Z,WANG J Q,et al. Research progress on sulfur-induced corrosion of Alloys 690 and 800 in high temperature and high pressure water[J]. Acta Metallurgica Sinica,2017,53(12):1541-1554.
【21】张伟国,林芳良,高风琴,等. 316NG不锈钢和合金800在含有硫酸盐及氯化物的高温水中应力腐蚀破裂:CNIC-00598[R]. 北京:原子能出版社,1989.
【2】DIERCKS D R,MUSCARA J,SHACK W J. Steam generator tube integrity program[J]. Nuclear Engineering and Design,1996,165:143-149.
【3】ZINKLE S J,WAS G S. Materials challenges in nuclear energy[J]. Acta Materialia,2013,61(3):735-758.
【4】FYFITCH S. Corrosion and stress corrosion cracking of Ni-base alloys[M]//Comprehensive Nuclear Materials. Amsterdam:Elsevier,2012:69-92.
【5】吴思博. 压水堆核电站蒸汽发生器传热管硫致腐蚀失效机理[D]. 天津:天津大学,2018.
【6】袁曹龙,李新民,邓佳杰,等. 阴离子对600镍基合金腐蚀行为影响的研究[J]. 全面腐蚀控制,2011,25(6):45-48.
【7】IAEA Nuclear Energy Series No. NP-T-S. Stress corrosion cracking in light water reactors:good practices and lessons learned[R]. [S.l.]:[s.n.],2011.
【8】PARK J H,CHOPRA O K,NATESAN K,et al. Boric acid corrosion of light water reactor pressure vessel materials[R]. NUREG/CR-6875,ANL-04/08,2005.
【9】孙海涛,凌礼恭,吕云鹤,等. 国内压水堆核电站设备材料应力腐蚀问题及安全管理[J]. 腐蚀科学与防护技术,2016,28(3):283-287.
【10】夏大海,宋诗哲,王俭秋,等. 690和800合金在高温高压水中硫致腐蚀失效研究进展[J]. 金属学报,2017,53(12):1541-1554.
【11】华惠中,黄春波,吕战鹏,等. 800、600和690合金的铅致应力腐蚀破裂[J]. 腐蚀与防护,2001,22(11):483-488.
【12】王光辉,彭君,袁义帆,等. 硫酸根离子和电极电位对异材焊接件A508/52M在高温水中应力腐蚀破裂的影响[J]. 理化检验(物理分册),2013,49(6):357-361,366.
【13】张平柱,胡石林,张伟国. 酸性硫酸根离子介质中奥氏体不锈钢的应力腐蚀行为研究[J]. 原子能科学技术,2003,37:145-148.
【14】夏大海,杨丽霞. 不同浓度比的硫酸根和氯离子溶液中钝化膜的半导体特性转变机制研究[J]. 物理化学学报,2014,30(8):1465-1473.
【15】张锐峰,陈圆,余菲. 690镍基合金在SO42-,S2O32-,Cl-溶液中的电化学行为研究[J]. 清洗世界,2016,32(6):14-16,33.
【16】张丽,韩恩厚,柯伟. S2O32-对Ni基合金671在NaCl水溶液中的点蚀行为的影响[J]. 腐蚀科学与防护技术,2004,16(4):229-232.
【17】陈俊劼,肖茜,吕战鹏,等. 硫酸根离子对铁在弱碱性溶液中阳极溶解和钝化行为的影响[J]. 物理化学学报,2015,31(6):1093-1104.
【18】王钢,袁曹龙,梅其政,等. 硫酸盐对600镍基合金腐蚀行为影响的研究[J]. 清洗世界,2012,28(2):15-19.
【19】夏大海,宋扬,宋诗哲,等. 酸性氯离子溶液中硫代硫酸根对800合金腐蚀机理[J]. 天津大学学报(自然科学与工程技术版),2018,51(6):591-597.
【20】XIA D H,SONG S Z,WANG J Q,et al. Research progress on sulfur-induced corrosion of Alloys 690 and 800 in high temperature and high pressure water[J]. Acta Metallurgica Sinica,2017,53(12):1541-1554.
【21】张伟国,林芳良,高风琴,等. 316NG不锈钢和合金800在含有硫酸盐及氯化物的高温水中应力腐蚀破裂:CNIC-00598[R]. 北京:原子能出版社,1989.
相关信息