推力滚针轴承推力垫圈断裂原因
Fracture reason of thrust washer of needle roller thrust bearing
摘 要
某推力滚针轴承的推力垫圈发生断裂,采用宏观观察、化学成分分析、扫描电镜分析、硬度测试、金相检验等方法对其断裂原因进行研究。结果表明:推力垫圈与保持架发生滑动磨损,在较高的旋转轴向应力作用下,推力垫圈发生断裂。
推力垫圈
脆性断裂
滑动磨损
needle roller thrust bearing
thrust washer
brittle fracture
sliding wear
Abstract
The thrust washer of a needle roller thrust bearing fractured. The fracture reason was studied by means of macroscopic observation, chemical composition analysis, scanning electron microscope analysis, hardness test and metallographic examination. The results show that sliding wear occured between the thrust washer and the cage, and the thrust washer broke under the action of high rotational axial stress.
中图分类号 TB31 TG115.2 DOI 10.11973/lhjy-wl202306017
所属栏目 质量控制与失效分析
基金项目
收稿日期 2022/8/4
修改稿日期
网络出版日期
作者单位点击查看
备注于娜红(1980-),女,硕士,高级工程师,主要从事燃油喷射系统关键零部件的热处理技术、材料技术、失效分析等方面的研究工作,corepeople@163.com
引用该论文: YU Nahong,ZHANG Ronghua. Fracture reason of thrust washer of needle roller thrust bearing[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2023, 59(6): 63～65
于娜红,张荣华. 推力滚针轴承推力垫圈断裂原因[J]. 理化检验－物理分册, 2023, 59(6): 63～65
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】雷建中,梅亚莉,赖维明,等.摩托车轴承保持架表面处理后组织与性能[J].轴承,2002(8):33-35.
【2】李浩东.推力滚针轴承失效分析及试验研究[D].广州:华南理工大学,2013.
【3】杨晓刚,王旭永,扈文庄.推力滚针轴承垫圈厚度误差对接触应力的影响[J].轴承,2015(12):11-13.
【4】梁华,张延芳,梁林霞.轴承保持架断裂原因分析[J].金属热处理,2005,30(3):80-82.
【2】李浩东.推力滚针轴承失效分析及试验研究[D].广州:华南理工大学,2013.
【3】杨晓刚,王旭永,扈文庄.推力滚针轴承垫圈厚度误差对接触应力的影响[J].轴承,2015(12):11-13.
【4】梁华,张延芳,梁林霞.轴承保持架断裂原因分析[J].金属热处理,2005,30(3):80-82.
相关信息